(31)P Solid-State NMR study of the chemical setting process of a dual-paste injectable brushite cements.
The composition and evolution of a brushite-type calcium phosphate cement was investigated by Solid-State NMR and X-ray during the setting process. The cement is obtained by mixing beta-tricalcium phosphate [Ca(3)(PO(4))(2), beta-TCP] and monocalcium phosphate monohydrate [Ca(H(2)PO(4))(2).H(2)O, MCPM] in presence of water, with formation of dicalcium phosphate dihydrate or brushite [CaHPO(2).2H(2)O, DCPD]. Analysis of the initial beta-TCP paste has shown the presence of beta-calcium pyrophosphate [Ca(2)P(2)O(7), beta-CPy] and that of the initial MCPM a mixture of MCPM and dicalcium phosphate [CaHPO(4), DCP]. Follow-up of the chemical composition by (31)P Solid-State NMR enables to show that the chemical setting process appeared to reach an end after 20 min. The constant composition observed at the end of the process was similarly determined.
Legrand
A P
AP
Laboratoire de Physique Quantique ESPCI PariTech, F-75005, Paris, France. andre-pierre.legrand@espci.fr
Sfihi
H
H
Lequeux
N
N
Lemaître
J
J
D001672:Biocompatible Materials / Q000737:chemistry*; D001843:Bone Cements / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D055598:Chemical Phenomena; D009682:Magnetic Resonance Spectroscopy / Q000379:methods*; D008422:Materials Testing; D014867:Water / Q000737:chemistry; D014961:X-Ray Diffraction
D001672:Biocompatible Materials; D001843:Bone Cements; D002130:Calcium Phosphates; D014867:Water; C494366:calcium phosphate, dibasic, dihydrate