The induction of dentin bridge-like structures by constructs of subcultured dental pulp-derived cells and porous HA/TCP in porcine teeth.
The purpose of this study was to investigate dentin-bridge formation in teeth following the transplantation of dental pulp-derived cells seeded on hydroxyapatite/tricalcium phosphate (HA/TCP) scaffolds. The dental pulp tissues were removed from the extracted first molar teeth of miniature pigs and single cell populations were subcultured. Second-passage cells that had alkaline phosphatase activity were combined with scaffolds. Cell-scaffold constructs were placed in contact with the exposed pulp tissue. The dimensions of the exposed pulp site were approximately 1-2.5 mm in diameter and 2-3 mm in depth from the tooth surface. After placing the constructs, the tooth was restored with composite resin. Six weeks after transplantation, hard tissue formation was observed on the pulp tissue in histology. Dentinal tubule-like structures were observed in most of the hard tissue generated, and columnar cells, which showed positive immunoreactions with dentin sialoprotein (DSP) and heat shock protein (HSP)-25, were aligned beneath the hard tissues. When only scaffolds were placed on the pulp tissues, particles of hard tissue were formed, however dentinal tubule-like structures and odontoblasts were not observed despite the formation of hard tissue. In conclusion, the implantation of dental pulp constructs into pulp exposed stimulates the formation of calcified dentin-like structures.
Ando
Yusuke
Y
Department of Oral and Maxillofacial Surgery, Nagoya University Graduate School of Medicine, Japan.
Honda
Masaki J
MJ
Ohshima
Hayato
H
Tonomura
Akiko
A
Ohara
Takayuki
T
Itaya
Toshimitsu
T
Kagami
Hideaki
H
Ueda
Minoru
M
D000818:Animals; D002130:Calcium Phosphates; D002478:Cells, Cultured; D003782:Dental Pulp / Q000166:cytology* / Q000637:transplantation*; D003804:Dentin / Q000254:growth & development* / Q000502:physiology; D017886:Durapatite; D009805:Odontogenesis; D013552:Swine; D013556:Swine, Miniature; D023822:Tissue Engineering / Q000379:methods*; D054457:Tissue Scaffolds
D002130:Calcium Phosphates; D017886:Durapatite; C018392:tricalcium phosphate