Facile synthesis and unique physicochemical properties of three-dimensionally ordered macroporous magnesium oxide, gamma-alumina, and ceria-zirconia solid solutions with crystalline mesoporous walls.
Three-dimensionally (3D) ordered macroporous (3DOM) MgO, gamma-Al(2)O(3), Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) with polycrystalline mesoporous walls have been successfully fabricated with the triblock copolymer EO(106)PO(70)EO(106) (Pluronic F127) and regularly packed monodispersive polymethyl methacrylate (PMMA) microspheres as the template and magnesium, aluminum, cerium and zirconium nitrate(s), or aluminum isopropoxide as the metal source. The as-synthesized metal oxides were characterized by means of techniques such as X-ray diffraction (XRD), thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), Fourier transform infrared (FT-IR), high-resolution scanning electron microscopy (HRSEM), high-resolution transmission electron microscopy/selected area electron diffraction (HRTEM/SAED), BET, carbon dioxide temperature-programmed desorption (CO(2)-TPD), and hydrogen temperature-programmed reduction (H(2)-TPR). It is shown that the as-fabricated MgO, gamma-Al(2)O(3), Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) samples possessed single-phase polycrystalline structures and displayed a 3DOM architecture; the MgO, Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) samples exhibited worm-hole-like mesoporous walls, whereas the gamma-Al(2)O(3) samples exhibited 3D ordered mesoporous walls. The solvent (ethanol or water) nature and concentration, metal precursor, surfactant, and drying condition have an important impact on the pore structure and surface area of the final product. The introduction of surfactant F127 to the synthesis system could significantly enhance the surface areas of the 3DOM metal oxides. With PMMA and F127 in a 40% ethanol solution, one can generate well-arrayed 3DOM MgO with a surface area of 243 m(2)/g and 3DOM Ce(0.6)Zr(0.4)O(2) with a surface area of 100 m(2)/g; with PMMA and F127 in an ethanol-HNO(3) solution, one can obtain 3DOM gamma-Al(2)O(3)with a surface area of 145 m(2)/g. The 3DOM MgO and 3DOM gamma-Al(2)O(3) samples showed excellent CO(2) adsorption behaviors, whereas the 3DOM Ce(0.6)Zr(0.4)O(2) sample exhibited exceptional low-temperature reducibility. The unique physicochemical properties associated with the copresence of 3DOM and mesoporous walls make these porous materials ideal candidates for applications in heterogeneous catalysis and CO(2) adsorption.
Laboratory of Catalysis Chemistry and Nanoscience, Department of Chemistry and Chemical Engineering, College of Environmental and Energy Engineering, Beijing University of Technology, Beijing 100124, China.
Huining
H
Li
Lei
L
Zhang
Hongxing
H
Dai
Hong
H
He