Surface characterization of the chitosan membrane after oxygen plasma treatment and its aging effect.
Chitosan has received considerable attention for biomedical applications in recent years because of its biocompatibility and biodegradability. In this paper, angle-resolved x-ray photoelectron spectroscopy (ARXPS) was carried out to investigate the chemical groups' spatial orientation on the chitosan membrane surface. Oxygen plasma treatment was also employed to improve the surface hydrophilicity of the chitosan membrane. The results of ARXPS revealed the distribution of surface polar groups, such as-OH and O=CNH(2) toward the membrane bulk, which was the origin of the chitosan membrane surface hydrophobicity. The contact angle measurements and XPS results indicated that oxygen plasma treatment can markedly improve the surface hydrophilicity and surface energy of the chitosan membrane by incorporating oxygen-containing polar groups. With the existence of the aging process, the influence of plasma treatment was not permanent, it faded with storage time. The ARXPS result discovered that the reorientation of polar functional groups generated by plasma treatment toward the membrane bulk was primarily responsible for the aging effect.
Wang
Yingjun
Y
College of Materials Science and Engineering, South China University of Technology, Guangzhou, 510640, People's Republic of China.
Yin
Shiheng
S
Ren
Li
L
Zhao
Lianna
L
D001672:Biocompatible Materials / Q000737:chemistry*; D048271:Chitosan / Q000737:chemistry*; D005740:Gases / Q000737:chemistry; D006358:Hot Temperature; D008422:Materials Testing; D008567:Membranes, Artificial; D010100:Oxygen / Q000737:chemistry*; D013499:Surface Properties
D001672:Biocompatible Materials; D005740:Gases; D008567:Membranes, Artificial; D048271:Chitosan; D010100:Oxygen