Radiopacity of portland cement associated with different radiopacifying agents.
This study evaluated the radiopacity of Portland cement associated with the following radiopacifying agents: bismuth oxide, zinc oxide, lead oxide, bismuth subnitrate, bismuth carbonate, barium sulfate, iodoform, calcium tungstate, and zirconium oxide. A ratio of 20% radiopacifier and 80% white Portland cement by weight was used for analysis. Pure Portland cement and dentin served as controls. Cement/radiopacifier and dentin disc-shaped specimens were fabricated, and radiopacity testing was performed according to the ISO 6876/2001 standard for dental root sealing materials. Using Insight occlusal films, the specimens were radiographed near to a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The radiographs were digitized and radiopacity compared with the aluminum stepwedge using Digora software (Orion Corporation Soredex, Helsinki, Finland). The radiographic density data were converted into mmAl and analyzed statistically by analysis of variance and Tukey-Kramer test (alpha = 0.05). The radiopacity of pure Portland cement was significantly lower (p < 0.05) than that of dentin, whereas all cement/radiopacifier mixtures were significantly more radiopaque than dentin and Portland cement alone (p < 0.05). Portland cement/bismuth oxide and Portland cement/lead oxide presented the highest radiopacity values and differed significantly from the other materials (p < 0.05), whereas Portland cement/zinc oxide presented the lowest radiopacity values of all mixtures (p < 0.05). All tested substances presented higher radiopacity than that of dentin and may potentially be added to the Portland cement as radiopacifying agents. However, the possible interference of the radiopacifiers with the setting chemistry, biocompatibility, and physical properties of the Portland cement should be further investigated before any clinical recommendation can be done.
Húngaro Duarte
Marco Antonio
MA
Department of Dentistry, Sacred Heart University, Bauru, SP, Brazil. mhungaro@travelnet.com.br
de Oliveira El Kadre
Guâniara D'arc
GD
Vivan
Rodrigo Ricci
RR
Guerreiro Tanomaru
Juliane Maria
JM
Tanomaru Filho
Mário
M
de Moraes
Ivaldo Gomes
IG
D015502:Absorptiometry, Photon; D000535:Aluminum / Q000737:chemistry; D001466:Barium Sulfate / Q000737:chemistry; D001672:Biocompatible Materials / Q000737:chemistry; D001729:Bismuth / Q000737:chemistry; D017610:Calcium Compounds / Q000737:chemistry; D002254:Carbonates / Q000737:chemistry; D055598:Chemical Phenomena; D003287:Contrast Media / Q000737:chemistry*; D003738:Dental Cements / Q000737:chemistry*; D003804:Dentin / Q000000981:diagnostic imaging; D006801:Humans; D006847:Hydrocarbons, Iodinated / Q000737:chemistry; D007091:Image Processing, Computer-Assisted; D007854:Lead / Q000737:chemistry; D008422:Materials Testing; D010087:Oxides / Q000737:chemistry; D019252:Radiography, Dental, Digital; D012387:Root Canal Filling Materials / Q000737:chemistry; D017973:Tungsten Compounds / Q000737:chemistry; D015034:Zinc Oxide / Q000737:chemistry; D015040:Zirconium / Q000737:chemistry
D001672:Biocompatible Materials; D017610:Calcium Compounds; D002254:Carbonates; D003287:Contrast Media; D003738:Dental Cements; D006847:Hydrocarbons, Iodinated; D010087:Oxides; D012387:Root Canal Filling Materials; D017973:Tungsten Compounds; C034054:bismuth carbonate; D001466:Barium Sulfate; D007854:Lead; C047365:lead oxide; C018858:calcium tungstate; C033301:bismuth oxide; D015040:Zirconium; D000535:Aluminum; C010804:bismuth subnitrate; C010473:iodoform; C028541:zirconium oxide; D015034:Zinc Oxide; D001729:Bismuth