Early bone response to sandblasted, dual acid-etched and H2O2/HCl treated titanium implants: an experimental study in the rabbit.
The aim of this study was to evaluate the influence of a roughened H(2)O(2)/HCl heat-treated titanium surface on peri-implant bone formation at an early stage in vivo. 24 Ti(6)Al(4)V alloy implants were used; half were treated by sandblasted and dual acid-etched treatments (control group), while the others were treated by sandblasted, dual acid-etched and H(2)O(2)/HCl heat treatments (test group). The morphology and roughness were analyzed by field emission SEM and atomic force microscopy. The implants were inserted into the femora of 12 adult white rabbits. After 2 and 4 weeks, femora block specimens were prepared for histological and histomorphometric analysis. SEM micrographs showed that multilevel and different sized pits were formed on both surfaces. New bone formation was observed on both implant surfaces. Test implants demonstrated a greater mean percentage of bone-implant contact as compared with controls at 2 (46.84 vs. 41.81, p=0.000) and 4 weeks (49.43 vs. 44.87, p=0.006) of healing. It is concluded that the H(2)O(2)/HCl heat-treated rough titanium surface promoted enhanced bone apposition during the early stages of new bone formation around the implant.
He
F M
FM
Department of Implantology, The Affiliated Stomatologic Hospital, College of Medical Sciences, Zhejiang University, Hangzhou, China.
Yang
G L
GL
Li
Y N
YN
Wang
X X
XX
Zhao
S F
SF
D000134:Acid Etching, Dental; D000497:Alloys; D000818:Animals; D015519:Bone Density; D003722:Dental Alloys; D015921:Dental Implants; D017267:Dental Prosthesis Design; D005269:Femur / Q000601:surgery; D006358:Hot Temperature; D006861:Hydrogen Peroxide / Q000494:pharmacology; D020007:Implants, Experimental; D008855:Microscopy, Electron, Scanning; D016348:Osseointegration / Q000187:drug effects; D011817:Rabbits; D013499:Surface Properties; D014025:Titanium
D000497:Alloys; D003722:Dental Alloys; D015921:Dental Implants; C031462:titanium alloy (TiAl6V4); D006861:Hydrogen Peroxide; D014025:Titanium