Influence of the activating agent and the inert gas (type and flow) used in an activation process for the porosity development of carbon nanofibers.
Carbon nanofibers (CNFs) were activated with different activating agents (KOH, KHCO(3) and K(2)CO(3)). The effects of different activations conditions, including type of protector gas (He, Ar and N(2)) and helium flow rate on the properties of activated carbon nanofibers were studied. The structural changes in activated CNFs were investigated using the following characterization techniques: N(2) adsorption isotherms at 77K, XRD, temperature-programmed desorption of hydrogen, TEM, TPO and elemental composition. The results showed that the surface area increased by a factor of 3.3, 2.0 and 1.8 referred to the parent CNFs after the treatment with KOH, K(2)CO(3) and KHCO(3), respectively. In addition, KOH generated a greater pore volume than the other activating agents; micropores were mainly generated during the process. Finally, different carrier gases were added during the activation in order to study their influence on the pore opening behavior of CNFs. It was found that the activation degree increased in the following order: Ar<N(2)<He. When He was used as the carrier gas, the microporosity was strongly developed.
Jiménez
Vicente
V
Facultad de Ciencias Químicas/Escuela Técnica Agrícola, Departamento de Ingeniería Química, Universidad de Castilla-La Mancha, 13071 Ciudad Real, Spain. vicente.jimenez@uclm.es
Sánchez
Paula
P
Valverde
José Luis
JL
Romero
Amaya
A