Comparison of the synthesis of Ge nanocrystals in hafnium aluminum oxide and silicon oxide matrices.
Growth of germanium (Ge) nanocrystals in silicon (Si) oxide and hafnium aluminum oxide (HfAlO) is examined. In Si oxide, nanocrystals were able to form at annealing temperatures of 800 degrees C to 1000 degrees C. Nanocrystals formed at 800 degrees C were round and approximately 8 nm in diameter, at 900 degrees C they become facetted and at 1000 degrees C they become spherical again. In HfAlO, at 800 degrees C nanocrystals formed are relatively smaller (approximately 3 nm in diameter) and lower in density. While at 900 degrees C and 1000 degrees C, nanocrystals did not form due to out-diffusion of Ge. Different nanocrystal formation characteristics in the matrices are attributed to differences in their crystallization temperatures.
Chew
H G
HG
Advanced Materials for Micro and Nano-Systems, Singapore-MIT Alliance, 4 Engineering Drive 3, Singapore.
Zheng
F
F
Choi
W K
WK
Chim
W K
WK
Fitzgerald
E A
EA
Foo
Y L
YL