Cervical microleakage in Class II cavities restored with the Sonicsys approx system.
OBJECTIVE
To investigate the cervical microleakage in Class II cavities restored with Sonicsys approx ceramic inserts and four resin-based materials.


METHODS
Forty noncarious and crack-free mandibular third molars were used. These teeth were randomly assigned to four groups each containing 10 teeth. No control group was created. On each tooth, one mesial boxlike cavity was prepared using the active head Sonicsys approx no. 3. The cervical margin of each cavity was in enamel about 1 mm coronal to the cementoenamel junction. According to manufacturer's instructions, the prepared cavities were restored using a Sonicsys approx ceramic inserts no.3 and four resin-based materials as follows: group 1, Tetric Flow; group 2, Admira Flow; group 3, Nexus 2; group 4, X-Flow. After finishing and polishing, all specimens were stored in distilled water for 7 days at 37 degrees C, thermocycled 1,000 cycles between 5 degrees and 55 degrees C, and stored for 24 hours in basic fuchsine 2%. All specimens were then embedded in clear acrylic resin and sectioned along a mesial-distal plane through the middle of the cervical margin. The cervical areas of the resulting sections were examined using an optical microscope to assess the dye penetration. The registered scores were analyzed using Kruskal-Wallis and Mann-Whitney U tests.


RESULTS
Microleakage was detected in each experimental group. Kruskal-Wallis test revealed statistically significant differences among groups (P = .009, alpha = .01). The Mann-Whitney U test showed significant differences between Admira Flow group and Tetric Flow (P = .011, alpha = .05), Nexus 2 (P = .001, alpha = .01), and X-Flow (P = .004, alpha = .01), respectively.


CONCLUSIONS
Within the limitations of this study, the extent of microleakage in the cervical area (enamel) of Class II cavities restored with Sonicsys approx ceramic inserts depends on the material used for luting. The highest leakage occurred when Admira flow was used.
Department of Prostheses Technology and Dental Materials, University School of Dentistry, Timisoara, Romania. mrominu@hotmail.com
Mihai
M
Rominu
Zeno
Z
Florita
Sorin
S
Lakatos
Roxana Otilia
RO
Rominu
D004396:Coloring Agents; D003737:Dental Cavity Preparation / Q000145:classification / Q000295:instrumentation* / Q000379:methods; D003743:Dental Enamel; D003763:Dental Leakage / Q000175:diagnosis / Q000209:etiology*; D018772:Dental Marginal Adaptation; D003776:Dental Porcelain; D003793:Dental Restoration, Permanent / Q000379:methods*; D003799:Dental Stress Analysis; D006801:Humans; D008422:Materials Testing; D008964:Molar, Third; D019279:Resin Cements / Q000009:adverse effects*; D019237:Tooth Cervix; D014465:Ultrasonics
D004396:Coloring Agents; D019279:Resin Cements; D003776:Dental Porcelain