Nanoparticles and 3D sponge-like porous networks of manganese oxides and their microwave absorption properties.
Hydrohausmannite nanoparticles (approximately 10 nm) were prepared by the hydrothermal method at 100 degrees C for 72 h. Subsequent annealing was done in air at 400 degrees C and 800 degrees C for 10 h, Mn(3)O(4) nanoparticles (approximately 25 nm) and 3D Mn(2)O(3) porous networks were obtained, respectively. The products were characterized by XRD, TEM, SAED and FESEM. Time-dependent experiments were carried out to exhibit the formation process of the Mn(2)O(3) networks. Their microwave absorption properties were investigated by mixing the product and paraffin wax with 50 vol%. The Mn(3)O(4) nanoparticles possess excellent microwave absorbing properties with the minimum reflection loss of -27.1 dB at 3.1 GHz. In contrast, the Mn(2)O(3) networks show the weakest absorption of all samples. The absorption becomes weaker with the annealing time increasing at 800 degrees C. The attenuation of microwave can be attributed to dielectric loss and their absorption mechanism was discussed in detail.
Yan
D
D
School of Physical Science and Technology, Lanzhou University, Lanzhou 730000, People's Republic of China.
Cheng
S
S
Zhuo
R F
RF
Chen
J T
JT
Feng
J J
JJ
Feng
H T
HT
Li
H J
HJ
Wu
Z G
ZG
Wang
J
J
Yan
P X
PX
D000042:Absorption; D003460:Crystallization / Q000379:methods*; D046911:Macromolecular Substances / Q000737:chemistry; D017895:Manganese Compounds / Q000737:chemistry* / Q000528:radiation effects; D008422:Materials Testing; D008872:Microwaves; D008968:Molecular Conformation; D049329:Nanostructures / Q000737:chemistry* / Q000528:radiation effects / Q000648:ultrastructure*; D036103:Nanotechnology / Q000379:methods*; D010087:Oxides / Q000737:chemistry* / Q000528:radiation effects; D010316:Particle Size; D016062:Porosity; D012542:Scattering, Radiation; D013499:Surface Properties
D046911:Macromolecular Substances; D017895:Manganese Compounds; D010087:Oxides; C027424:manganese oxide