Praseodymium doped NaYF4 nanocrystals in oxyfluoride glass-ceramics; morphological and spectroscopic studies.
The synthesis, morphology, optical properties and excited state dynamics of the Pr-doped NaYF4 nanocrystals in glass-ceramics are presented. The crystalline cubic NaYF4:Pr were synthesized by the controlled heat-treatment of multicomponent oxyfluoride glass based on silica and YF3. A series of the two-hour heat treatments at 620-660 degrees C were carried out yielding visually transparent materials. Above 660 degrees C an opaque material was obtained. The crystalline phase was characterized by the X-ray powder diffraction (XRD), high-resolution transmission electron microscopy (TEM) and selected area electron diffraction (SAED). The effect of ceramming temperature on the NaYF4:Pr cell parameter (a = 5.470 A for NaYF4 and 5.4899 A, 5.4979 A and 5.5378 A in glass-ceramics) and particle average size (15-40 nm) was observed. Optical characteristics of formed glass-ceramics were favorably affected by the Pr3+ ions in well-defined sites of NaYF4; emission intensities increased and luminescence decay curves become single exponential with the longer corresponding lifetimes.
Dominiak-Dzik
G
G
Institute of Low Temperature and Structure Research, Polish Academy of Sciences, ul. Okólna 2, 50-395 Wrocław, Poland.