Thermal stability and in vitro bioactivity of Ti-Al-V-O nanostructures fabricated on Ti6Al4V alloy.
This work investigates the thermal stability and in vitro bioactivity of Ti-Al-V-O nanostructures grown on Ti6Al4V alloy through an anodization method. After anodization of the two-phase Ti6Al4V alloy, there were two different kinds of Ti-Al-V-O nanostructure (nanotube arrays grown in the alpha-phase region and irregular nanopores grown in the beta-phase region) that formed on the surface of the alloy. It was found that the Ti-Al-V-O nanotubes can withstand a high temperature of 675 degrees C in air without collapse, whereas the irregular Ti-Al-V-O nanopores presented a lower thermal stability. In vitro simulated body fluid (SBF) testing of heat-treated nanostructures indicated that a quick apatite formation on these nanostructures occurred after only several hours of sample immersion in the SBF.
State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, People's Republic of China.
Yan
Y
Li
Dongyan
D
Ding
Congqin
C
Ning
Shuo
S
Bai
Lin
L
Huang
Ming
M
Li
Dali
D
Mao
D000497:Alloys; D001031:Apatites / Q000378:metabolism; D001826:Body Fluids / Q000378:metabolism; D006358:Hot Temperature; D043942:Nanotubes / Q000737:chemistry*; D014025:Titanium / Q000378:metabolism*
D000497:Alloys; D001031:Apatites; C031462:titanium alloy (TiAl6V4); D014025:Titanium