Shear bond strength of brackets rebonded with a fluoride-releasing and -recharging adhesive system.
OBJECTIVE
To ascertain the effects of repeated bonding on the shear bond strength of orthodontic brackets bonded with a fluoride-releasing and -recharging adhesive system with a self-etching primer in comparison with two other types of adhesive system.


METHODS
A total of 48 premolars were collected and divided equally into three groups of 16. Each group was assigned one of three adhesive systems: Transbond XT, Transbond Plus, or a fluoride-releasing and -recharging adhesive system, Beauty Ortho Bond. Shear bond strength was measured 24 hours after bracket bonding, with the bonding/debonding procedures repeated twice after the first debonding. A universal testing machine was used to determine shear bond strengths, and bracket/adhesive failure modes were evaluated with the adhesive remnant index after each debonding.


RESULTS
At every debonding sequence, all of these three adhesive systems had a shear bond strength of 6 MPa, which is a minimum requirement for clinical use. Transbond XT and Transbond Plus had significantly higher mean shear bond strengths than did Beauty Ortho Bond at each debonding. No significant differences in mean bond strength were observed between the three debondings in each adhesive system. Bond failure at the enamel/adhesive interface occurred more frequently in Beauty Ortho Bond than in Transbond XT or Transbond Plus.


CONCLUSIONS
The fluoride-releasing and -recharging adhesive system with the self-etching primer (Beauty Ortho Bond) had clinically sufficient shear bond strength in repeated bracket bonding; this finding can help orthodontists to decrease the risk of damage to enamel at debonding.
Endo
Toshiya
T
Orthodontic Dentistry, The Nippon Dental University Niigata Hospital, 1-8 Hamaura-cho, Chuo-ku, Niigata 951-8580, Japan. endoto@ngt.ndu.ac.jp
Ozoe
Rieko
R
Shinkai
Koichi
K
Aoyagi
Makiko
M
Kurokawa
Hiroomi
H
Katoh
Yoshiroh
Y
Shimooka
Shohachi
S
D000042:Absorption; D000268:Adhesiveness; D002327:Cariostatic Agents / Q000737:chemistry*; D003722:Dental Alloys / Q000737:chemistry; D001840:Dental Bonding; D003743:Dental Enamel / Q000648:ultrastructure; D003799:Dental Stress Analysis / Q000295:instrumentation; D004058:Diffusion; D005459:Fluorides / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D016910:Orthodontic Brackets; D019279:Resin Cements / Q000737:chemistry*; D033081:Shear Strength; D013193:Stainless Steel / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors
C519484:Beauty Ortho Bond; D002327:Cariostatic Agents; D003722:Dental Alloys; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C477790:Transbond XT; D013193:Stainless Steel; D005459:Fluorides