The large-scale synthesis of one-dimensional TiO2 nanostructures using palladium as catalyst at low temperature.
The synthesis of TiO(2) nanostructures including nanowires and nanobelts has been demonstrated experimentally by anodization of Ti foil in an electrolyte, and by treatment in a PdCl(2) ethanol solution together with UV light irradiation and annealing at a temperature below 800 degrees C. The TiO(2) nanotube arrays resulting from the anodization were used as source precursor and transformed into nanowires and nanobelts respectively with high efficiency during the subsequent processes. The resulting TiO(2) nanowires and nanobelts, characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Raman and surface photovoltage (SPV) spectroscopy, are single rutile crystals of high quality. In addition to the synthesis of the nanostructure at low temperature, this method also shows great advantages for the selectable morphology of the final TiO(2) nanostructures via adjustment of the UV light irradiation time and annealing temperature.
Key Laboratory for Micro-Nano Optoelectronic Devices of Ministry of Education, Hunan University, Changsha 410082, People's Republic of China.
Mingxia
M
Xia
Qinglin
Q
Zhang
Hongxing
H
Li
Guozhang
G
Dai
Hongchun
H
Yu
Taihong
T
Wang
Bingsuo
B
Zou
Yanguo
Y
Wang
D002384:Catalysis; D003460:Crystallization / Q000379:methods*; D004563:Electrochemistry / Q000379:methods*; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D008968:Molecular Conformation; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure*; D036103:Nanotechnology / Q000379:methods*; D010165:Palladium / Q000737:chemistry*; D010316:Particle Size; D013499:Surface Properties; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
D046911:Macromolecular Substances; C009495:titanium dioxide; D010165:Palladium; D014025:Titanium