The fabrication of ZnO nanowire field-effect transistors by roll-transfer printing.
A method with the potential to fabricate large-area nanowire field-effect transistors (NW-FETs) was demonstrated in this study. Using a high-speed roller (20-80 cm min(-1)), transfer printing was successfully employed to transfer vertically aligned zinc oxide (ZnO) nanowires grown on a donor substrate to a polydimethylsiloxane (PDMS) stamp and then print the ordered ZnO nanowire arrays on the received substrate for the fabrication of NW-FETs. ZnO NW-FETs fabricated by this method exhibit high performances with a threshold voltage of around 0.25 V, a current on/off ratio as high as 10(5), a subthreshold slope of 360 mV/dec, and a field-effect mobility of around 90 cm(2) V(-1) s(-1). The excellent device characteristics suggest that the roll-transfer printing technique, which is compatible with the roll-to-roll (R2R) process and operated in atmosphere, has a good potential for the high-speed fabrication of large-area nanowire transistors for flexible devices and flat panel displays.
Department of Chemical Engineering, National Cheng Kung University, Tainan, Taiwan, Republic of China.
Yi-Kuei
YK
Chang
Franklin Chau-Nan
FC
Hong
D003460:Crystallization / Q000379:methods*; D004867:Equipment Design; D019544:Equipment Failure Analysis; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D008968:Molecular Conformation; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure*; D036103:Nanotechnology / Q000379:methods*; D010316:Particle Size; D011327:Printing / Q000379:methods; D013499:Surface Properties; D014173:Transistors, Electronic; D015034:Zinc Oxide / Q000737:chemistry*
D046911:Macromolecular Substances; D015034:Zinc Oxide