Oxygen plasma treatment of polystyrene and Zeonor: substrates for adhesion of patterned cells.
Plastic substrates made of polystyrene (PS) and Zeonor 1060R were treated with oxygen plasma to introduce polar groups (e.g., carbonyl and carboxylic acid) at the surface that render these materials hydrophilic and promote patterned adhesion of HeLa cells. Resultant surfaces were characterized using contact angle goniometry, atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) to monitor changes in wettability, nanoscale topography, and chemical composition. Biocompatibility of the plastic surfaces was verified through fluorescence microscopy using three fluorophores, Alexa Fluor 488 conjugated to Annexin V, Hoechst 33258, and propidium iodide, indicating cells that undergo apoptosis and necrosis, respectively. The best cell growth was observed on PS treated at 5 W/sccm, for which the viability of adhering HeLa cells exceeded 90%. Patterning was accomplished using an elastomeric microcapillary system (microCS) made of poly(dimethylsiloxane) (PDMS) that consisted of a set of parallel channels to align cells in linear fashion. Densely populated bands were obtained on substrates of both plastic materials when the culture medium contained >2 x 10(5) cells/mL.
Beaulieu
Isabelle
I
Chemistry Department, Universite du Quebec a Montreal, 2101 Jeanne-Mance Street, Montreal, QC, H3C 3P8, Canada.
Geissler
Matthias
M
Mauzeroll
Janine
J
D002448:Cell Adhesion; D006367:HeLa Cells; D006801:Humans; D018625:Microscopy, Atomic Force; D010100:Oxygen; D011137:Polystyrenes / Q000737:chemistry*; D013057:Spectrum Analysis / Q000379:methods; D014965:X-Rays
D011137:Polystyrenes; D010100:Oxygen