Kinetic model for hydroxyapatite precipitation on human enamel surface by electrolytic deposition.
The electrolytic deposition (ELD) of hydroxyapatite (HAP) coating on human enamel surface for different loading times at varied temperatures (ranging from 37 degrees C to 85 degrees C) and varied current densities (ranging from 0.05 mA cm(-2) to 10 mA cm(-2)) was investigated in this study. Thin film x-ray diffraction, Fourier transform infrared and micro-Raman spectra analysis, as well as an environmental scanning electron microscope, were used to characterize the coating. The results showed that only the HAP phase occurred on the enamel surface after ELD experiments. The contents of HAP deposits on the enamel surface linearly changed proportional to the square root of the loading time, which was in good agreement with the kinetic model of ELD of HAP coating based on one-dimensional diffusion. The induction periods were observed on all the regression lines, and the rate of the HAP coating formation on enamel showed a linear relationship with the current density. It was implied that the diffusion process was the rate-determining step in the ELD of the HAP coating on human enamel.
Lei
Caixia
C
College of Materials, Xiamen University, Xiamen 361005, People's Republic of China.
Liao
Yingmin
Y
Feng
Zude
Z
D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D003198:Computer Simulation; D003743:Dental Enamel / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry*; D004595:Electroplating / Q000379:methods*; D006801:Humans; D066298:In Vitro Techniques; D007700:Kinetics; D008956:Models, Chemical; D008964:Molar, Third / Q000737:chemistry*; D013499:Surface Properties; D013696:Temperature
D020099:Coated Materials, Biocompatible; D017886:Durapatite