Core-shell polymer nanorods by a two-step template wetting process.
One-dimensional core-shell polymer nanowires offer many advantages and great potential for many different applications. In this paper we introduce a highly versatile two-step template wetting process to fabricate two-component core-shell polymer nanowires with controllable shell thickness. PLLA and PMMA were chosen as model polymers to demonstrate the feasibility of this process. Solution wetting with different concentrations of polymer solutions was used to fabricate the shell layer and melt wetting was used to fill the shell with the core polymer. The shell thickness was analyzed as a function of the polymer solution concentration and viscosity, and the core-shell morphology was observed with TEM. This paper demonstrates the feasibility of fabricating polymer core-shell nanostructures using our two-step template wetting process and opens the arena for optimization and future experiments with polymers that are desirable for specific applications.
Dougherty
S
S
Mechanical Engineering Department, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609, USA.
Liang
J
J
D000537:Aluminum Oxide / Q000737:chemistry; D019344:Lactic Acid / Q000737:chemistry*; D046529:Microscopy, Electron, Transmission; D008956:Models, Chemical; D036103:Nanotechnology / Q000379:methods*; D043942:Nanotubes / Q000737:chemistry*; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D019904:Polymethyl Methacrylate / Q000737:chemistry*; D014783:Viscosity; D017155:Wettability
D011091:Polyesters; D011108:Polymers; D019344:Lactic Acid; C033616:poly(lactide); D019904:Polymethyl Methacrylate; D000537:Aluminum Oxide