Influence of an acrylic polymer blend on the physical stability of film-coated theophylline pellets.
The purpose of this study was to investigate the physical stability of a coating system consisting of a blend of two sustained release acrylic polymers and its influence on the drug release rate of theophylline from coated pellets. The properties of both free films and theophylline pellets coated with the polymer blend were investigated, and the miscibility was determined via differential scanning calorimetry. Eudragit RS 30 D was plasticized by the addition of Eudragit NE 30 D, and the predicted glass transition temperature (T(g)) of the blend was similar to the experimental values. Sprayed films composed of a blend of Eudragit NE 30 D/Eudragit RS 30 D (1:1) showed a water vapor permeability six times greater than films containing only Eudragit NE 30 D. The presence of quaternary ammonium functional groups from the RS 30 D polymer increased the swellability of the films. The films prepared from the blend exhibited stable permeability values when stored for 1 month at both 25 degrees C and 40 degrees C, while the films which were composed of only Eudragit NE 30 D showed a statistically significant decrease in this parameter when stored under the same conditions. Eudragit NE 30 D/Eudragit RS 30 D (1:1)-sprayed films decreased in elongation from 180% to 40% after storage at 40 degrees C for 1 month, while those stored at 25 degrees C showed no change in elongation. In coated pellets, the addition of Eudragit RS 30 D to the Eudragit NE 30 D increased the theophylline release rate, and the pellets were stable when stored at 25 degrees C for a period of up to 3 months due to maintenance of the physico-mechanical properties of the film. Pellets stored at 40 degrees C exhibited a decrease in drug release rate over time as a result of changes in film physico-mechanical properties which were attributed to further coalescence and densification of the polymer. When the storage temperature was above the T(g) of the composite, instabilities in both drug release rate and physical properties were evident. Stabilization in drug release rate from coated pellets could be correlated with the physico-mechanical stability of the film formulation when stored at temperatures below the T(g) of the polymer.
Kucera
Shawn
S
Department of Pharmaceutics, College of Pharmacy, The University of Texas at Austin, Austin, Texas 78712, USA. shawn.kucera@evonik.com
Shah
Navnit H
NH
Malick
A Waseem
AW
Infeld
Martin H
MH
McGinity
James W
JW
D000179:Acrylates; D001993:Bronchodilator Agents / Q000008:administration & dosage / Q000737:chemistry*; D004355:Drug Stability; D004356:Drug Storage; D005079:Excipients; D007700:Kinetics; D010539:Permeability; D011108:Polymers; D011109:Polymethacrylic Acids; D013806:Theophylline / Q000008:administration & dosage / Q000737:chemistry*; D014867:Water / Q000737:chemistry
D000179:Acrylates; D001993:Bronchodilator Agents; D005079:Excipients; D011108:Polymers; D011109:Polymethacrylic Acids; D014867:Water; C038300:methylmethacrylate-methacrylic acid copolymer; D013806:Theophylline