Influence of femoral stem surface finish on the apparent static shear strength at the stem-cement interface.
The stem-cement interface has long been implicated in failure of cemented total hip replacement. Much research has been performed to study the factors affecting the bond strength between the femoral stem and the bone cement. The present study aims to further investigate the influence of femoral stem surface finish on the apparent static shear strength at the stem-cement interface through a series of pull out tests, where stainless steel rods are employed to represent the femoral stem. The results demonstrated that there was a general tendency for the apparent static shear strength to be increased with the rise of surface roughness. The polished and glass bead-blasted rods illustrated a slip-stick-slip failure whereas the shot-blasted and grit-blasted rods displayed gross interface failure. Following pull out test, cement transfer films were detected on the polished rods, and there was cement debris adhered to the surface of the grit-blasted rods. Micropores, typically 120 mum in diameter, were prevalent in the cement surface interfaced with the polished rods, and the cement surfaces in contact with the shot-blasted and grit-blasted rods were greatly damaged. There was also evidence of metal debris embedding within the cement mantle originating from the tests of the grit-blasted rods, indicating an extremely strong mechanical interlocking at the interface. In summary, this present research demonstrated that the grit-blasted rods with the highest surface roughness were the best in terms of apparent static shear strength. However, it seemed to be most applicable only to the stem designs in which mechanical interlocking of the stem in the initial fixed position was essential.
Zhang
H
H
Centre for Precision Technologies, School of Computing and Engineering, University of Huddersfield, Queensgate, Huddersfield, HD1 3DH, UK. h.zhang@hud.ac.uk
Brown
L T
LT
Blunt
L A
LA
Barrans
S M
SM
D000268:Adhesiveness; D019644:Arthroplasty, Replacement, Hip / Q000295:instrumentation* / Q000379:methods*; D019544:Equipment Failure Analysis; D006622:Hip Prosthesis; D008422:Materials Testing; D019904:Polymethyl Methacrylate / Q000737:chemistry*; D011474:Prosthesis Design; D033081:Shear Strength; D013499:Surface Properties
D019904:Polymethyl Methacrylate