title: [Preparation and characterization of MgxZn(1-x)O powders].
abstract: MgxZn(1-x)O has been subjects of intense attention as a novel photo-electronic functional material in recent years. In the present paper, MgxZn(1-x)O powders were prepared by sol-gel method. Effects of Mg contents on MgxZn(1-x)O structure and luminescence properties were studied. The authors observed that MgxZn(1-x)O exhibited two kinds of structures, hexagonal wurtzite and face center cubic while x was in the range of 0 and 1. The MgxZn(1-x)O powders were hexagonal wurtzite structure with x < 0.2, face center cubic structure with x > 0. 2 and their blend structure with x between 0.2 and 0.8. Luminescence spectrum analysis indicated that all MgxZn(1-x)O samples with various composition showed luminescence of ultra-violet and visible light. The ultraviolet emission peak was from 370 nm to 384 nm and the visible emission peak was around at 468 nm. The average size of MgxZn(1-x)O powders was about 100 nm.
authors.affiliation: School of Material Science and Engineering, Changchun University of Science and Technology, Changchun 130022, China. manlqs@yahoo.com.cn
authors.forename: Quan-sheng
authors.initials: QS
authors.lastname: Liu
authors.forename: Xi-yan
authors.initials: XY
authors.lastname: Zhang
authors.forename: Zhao-hui
authors.initials: ZH
authors.lastname: Bai
authors.forename: Xiao-chun
authors.initials: XC
authors.lastname: Wang
authors.forename: Xiao-yun
authors.initials: XY
authors.lastname: Mi
authors.forename: Li-ping
authors.initials: LP
authors.lastname: Lu
authors.forename: Ying
authors.initials: Y
authors.lastname: Zhou