Tantalum clusters supported on silica-alumina: influence of support composition and chemistry on cluster structure.
Small cationic tantalum clusters were prepared on the surfaces of SiO2, silica-aluminas, and gamma-Al2O3 supports by treating physisorbed pentabenzyltantalum at 523 K for 24 h in flowing H2. The rate of decomposition and the products formed in the decomposition of pentabenzyltantalum are dependent on the support composition. When the support was SiO2, the evolved products were mainly biphenyl and a small amount of toluene, indicating that the Ta-C bond in pentabenzyltantalum was activated. As the alumina content of the support increased, diphenylmethane, benzene, and ethylene were increasingly formed, and these products show that the activation of the C-C bonds linking the C atoms of methyl groups to the aromatic rings of the benzyl ligands was facilitated. Infrared spectra of the surface species and mass spectra of the effluents formed during the treatment show that the composition of the support had significant influence on the decomposition of pentabenzyltantalum, and the chemistry is inferred to be related to the electron-donor properties of the supports. Extended X-ray absorption fine structure (EXAFS) spectra recorded at the Ta LIII edge indicate the formation of clusters with a Ta-Ta first-shell coordination number of approximately 3, and images obtained by scanning transmission electron microscopy (STEM) confirm the presence of such small clusters. X-ray absorption near edge structure (XANES) data indicate that the formal oxidation state of the tantalum in the clusters decreased from approximately 3.0 to approximately 2.6 as the support was changed from SiO2 to silica-aluminas to gamma-Al2O3. The data suggest that the tantalum clusters were anchored to the supports via bridging O atoms. The EXAFS data show that the support composition had little influence on the cluster structure.
Sun
Junming
J
Department of Chemical Engineering and Materials Science, University of California, Davis, California 95616, USA.
Chi
Miaofang
M
Lobo-Lapidus
Rodrigo J
RJ
Mehraeen
Shareghe
S
Browning
Nigel D
ND
Gates
Bruce C
BC
D000537:Aluminum Oxide / Q000737:chemistry*; D002412:Cations / Q000737:chemistry; D013058:Mass Spectrometry; D017348:Microscopy, Electron, Scanning Transmission; D009942:Organometallic Compounds / Q000737:chemistry*; D010084:Oxidation-Reduction; D012822:Silicon Dioxide / Q000737:chemistry*; D013053:Spectrophotometry; D013635:Tantalum / Q000737:chemistry*
D002412:Cations; D009942:Organometallic Compounds; D013635:Tantalum; D012822:Silicon Dioxide; D000537:Aluminum Oxide