The influence of micropore size on the mechanical properties of bulk hydroxyapatite and hydroxyapatite scaffolds.
While recognized as a promising bone substitute material, hydroxyapatite (HA) has had limited use in clinical settings because of its inherent brittle behavior. It is well established that macropores ( approximately 100 microm) in a HA implant, or scaffold, are required for bone ingrowth, but recent research has shown that ingrowth is enhanced when scaffolds also contain microporosity. HA is sensitive to synthesis and processing parameters and therefore characterization for specific applications is necessary for transition to the clinic. To that end, the mechanical behavior of bulk microporous HA and HA scaffolds with multi-scale porosity (macropores between rods in the range of 250-350 microm and micropores within the rods with average size of either 5.96 microm or 16.2 microm) was investigated in order to determine how strength and reliability were affected by micropore size (5.96 microm versus 16.2 microm). For the bulk microporous HA, strength increased with decreasing micropore size in both bending (19 MPa to 22 MPa) and compression (71 MPa to 110 MPa). To determine strength reliability, the Weibull moduli for the bulk microporous HA were determined. The Weibull moduli for bending increased (became more reliable) with decreasing pore size (7 to 10) while the Weibull moduli for compression decreased (became less reliable) with decreasing pore size (9 to 6). Furthermore, the elastic properties of the bulk microporous HA (elastic modulus of 30 GPa) and the compressive strengths of the HA scaffolds with multi-scale porosity (8 MPa) did not vary with pore size. The mechanisms responsible for the trends observed were discussed.
Cordell
Jacqueline M
JM
Department of Bioengineering, University of Illinois at Urbana-Champaign, United States.
Vogl
Michelle L
ML
Wagoner Johnson
Amy J
AJ
D018786:Bone Substitutes / Q000737:chemistry; D019245:Compressive Strength; D017886:Durapatite / Q000737:chemistry*; D055595:Mechanical Phenomena; D008855:Microscopy, Electron, Scanning; D010316:Particle Size; D016062:Porosity; D013314:Stress, Mechanical; D054457:Tissue Scaffolds / Q000737:chemistry*; D014465:Ultrasonics
D018786:Bone Substitutes; D017886:Durapatite