Poly(n-butyl acrylate) based lead (II) selective electrodes.
Poly(n-butyl acrylate) membranes for potentiometric ion-selective electrodes were developed and studied on example of lead-selective sensors. A novel approach resulting in Nernstian responses of tested sensor was proposed. Introduction of 5% (w/w) hydroxyethyl methacrylate into n-butyl acrylate moiety resulted in significant improvement of sensor analytical parameters. For the latter membrane material linear responses were obtained within lead activities range from 10(-2) to 10(-9) mol/dm(3), while for poly(n-butyl acrylate) based membranes pretreated in the same manner super-Nernstian behavior was obtained in a parallel experiment. Electrochemical impedance spectroscopy studies did not reveal significant differences between these two membranes, also similar lead ions diffusion coefficients were determined using inductively coupled plasma mass spectrometry with laser ablation.The difference between two kinds of membranes was found to concern higher Pb(II) ions contents in the surface part of the membrane with hydroxyethyl methacrylate, resulting in balanced Pb ions fluxes from/to the membrane.
Michalska
Agata
A
Department of Chemistry, Warsaw University, Warsaw, Poland. agatam@chem.uw.edu.pl
Wojciechowski
Marcin
M
Bulska
Ewa
E
Mieczkowski
Józef
J
Maksymiuk
Krzysztof
K
D000179:Acrylates; D017097:Electric Impedance; D055664:Electrochemical Techniques; D017736:Ion-Selective Electrodes; D007854:Lead / Q000032:analysis*; D008567:Membranes, Artificial; D008689:Methacrylates; D011108:Polymers; D013057:Spectrum Analysis
D000179:Acrylates; D008567:Membranes, Artificial; D008689:Methacrylates; D011108:Polymers; C498324:poly(n-butyl acrylate); D007854:Lead; C005044:hydroxyethyl methacrylate