[Preparation and characterization of MgxZn(1-x)O powders].
MgxZn(1-x)O has been subjects of intense attention as a novel photo-electronic functional material in recent years. In the present paper, MgxZn(1-x)O powders were prepared by sol-gel method. Effects of Mg contents on MgxZn(1-x)O structure and luminescence properties were studied. The authors observed that MgxZn(1-x)O exhibited two kinds of structures, hexagonal wurtzite and face center cubic while x was in the range of 0 and 1. The MgxZn(1-x)O powders were hexagonal wurtzite structure with x < 0.2, face center cubic structure with x > 0. 2 and their blend structure with x between 0.2 and 0.8. Luminescence spectrum analysis indicated that all MgxZn(1-x)O samples with various composition showed luminescence of ultra-violet and visible light. The ultraviolet emission peak was from 370 nm to 384 nm and the visible emission peak was around at 468 nm. The average size of MgxZn(1-x)O powders was about 100 nm.
Liu
Quan-sheng
QS
School of Material Science and Engineering, Changchun University of Science and Technology, Changchun 130022, China. manlqs@yahoo.com.cn
Zhang
Xi-yan
XY
Bai
Zhao-hui
ZH
Wang
Xiao-chun
XC
Mi
Xiao-yun
XY
Lu
Li-ping
LP
Zhou
Ying
Y