title: The effect of loading on microTBS of four all-in-one adhesives on bonding to dentin.
abstract: This in vitro study analyzed the effect of mechanical loading on microtensile bond strength (microTBS) to dentin of four all-in-one adhesives and compared with a total-etch adhesive system. The tested adhesives were Danville Experimental (an unfilled single-component adhesive containing a proprietary organophosphate and hydrophobic monomers; Danville Materials), G Bond (GC), Clearfil S(3) Bond (Kuraray), AdheSE One (Vivadent), and Prelude Total-Etch (Danville Materials). Dentin surfaces were exposed and composite resin (AP-X, Kuraray) build-ups were created. The samples were divided into two subgroups and the first subgroups were subjected to mechanical fatigue loading (5 x 10(4); 50 Nat 0.2 Hz). Testing was performed after 1 week using a "nontrimming" microTBS test at a cross head speed of 1 mm/min. The data was calculated as MPa and statistically analyzed using Multivariate Analysis of Variance. Multiple comparisons were done using t-test. Mechanical loading significantly decreased microTBS of the tested materials (p = 0.000). Prelude Total-etch showed the highest bond strength values when compared to the tested all-in-one adhesives (p < 0.01). G Bond and Clearfil S(3) Bond showed significantly higher bond strength values than Danville Experimental and AdheSE One (p < 0.01).
authors.affiliation: Department of Endodontics, Faculty of Dentistry, Selçuk University Campus, Konya, Turkey.
authors.forename: Sema
authors.initials: S
authors.lastname: Belli
authors.affiliation: Department of Restorative Dentistry and Endodontics, Faculty of Dentistry, Yüzüncüyıl University, Van, Turkey.
authors.forename: Betül
authors.initials: B
authors.lastname: Özçopur
authors.affiliation: Department of Operative Dentistry, Faculty of Dentistry, Karadeniz Technical University Campus, Trabzon, Turkey.
authors.forename: Cemal
authors.initials: C
authors.lastname: Yeşilyurt
authors.affiliation: Department of Endodontics, Faculty of Dentistry, Karadeniz Technical University, Trabzon, Turkey.
authors.forename: Güneş
authors.initials: G
authors.lastname: Bulut
authors.affiliation: Danville Materials Inc., San Ramon, California.
authors.forename: Xingzhe
authors.initials: X
authors.lastname: Ding
authors.affiliation: Danville Materials Inc., San Ramon, California.
authors.forename: Greg
authors.initials: G
authors.lastname: Dorsman
mesh_terms: D000134:Acid Etching, Dental; D000268:Adhesiveness; D003804:Dentin / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D008964:Molar, Third / Q000648:ultrastructure; D013314:Stress, Mechanical; D013499:Surface Properties; D013718:Tensile Strength; D014014:Tissue Adhesives / Q000737:chemistry*
chemical_list: D014014:Tissue Adhesives