Acoustical evaluation of carbonized and activated cotton nonwovens.
An activated carbon fiber nonwoven (ACF) was manufactured from a cotton nonwoven fabric. For the ACF acoustic application, a nonwoven composite of ACF with cotton nonwoven as a base layer was developed. Also produced were the composites of the cotton nonwoven base layer with a layer of glassfiber nonwoven, and the cotton nonwoven base layer with a layer of cotton fiber nonwoven. Their noise absorption coefficients and sound transmission loss were measured using the Brüel and Kjaer impedance tube instrument. Statistical significance of the differences between the composites was tested using the method of Duncan's grouping. The study concluded that the ACF composite exhibited a greater ability to absorb normal incidence sound waves than the composites with either glassfiber or cotton fiber. The analysis of sound transmission loss revealed that the three composites still obeyed the mass law of transmission loss. The composite with the surface layer of cotton fiber nonwoven possessed a higher fabric density and therefore showed a better sound insulation than the composites with glassfiber and ACF.
Jiang
N
N
School of Human Ecology, Louisiana State University Agricultural Center, Baton Rouge, LA 70803, USA.
Chen
J Y
JY
Parikh
D V
DV
D000042:Absorption; D000162:Acoustics; D002244:Carbon / Q000032:analysis*; D000077482:Carbon Fiber; D032561:Cotton Fiber; D005898:Glass / Q000737:chemistry; D003368:Gossypium / Q000737:chemistry*; D013016:Sound; D013718:Tensile Strength
D000077482:Carbon Fiber; D002244:Carbon