[In situ diffuse reflectance FTIR spectroscopy study of CO adsorption on Ni2P/mesoporous molecule sieve catalysts].
Abstract The supported nickel phosphate precursors were prepared by incipient wetness impregnation using nickel nitrate as nickel source, diammonium hydrogen phosphate as phosphorus source, and MCM-41, MCM-48, SBA-15 and SBA-16 as supports, respectively. Then, the supported Ni2 P catalysts were prepared by temperature-programmed reduction in flowing Hz from their nickel phosphate precursors. The in situ diffuse reflectance FTIR spectroscopy (DRIFTS) analysis with the probe molecule CO was carried out to characterize the surface properties. The results indicated that there were significant differences in the spectral features of the samples. The upsilon(CO) absorbances observed for adsorbed CO on mesoporous molecule sieve was attributed to weak physical adsorption. There are four different kinds of upsilon(CO) absorbances observed for adsorbed CO on Ni2 P/MCM-41 catalyst with the following assignments: (1) the formation of Ni(CO)4 at 2055 cm(-1). (2) CO terminally bonded to cus Ni(delta+) (0<delta<1) sites at 2091 cm(-1). (3) CO terminally bonded to Ni+ sites at 2127 cm(-1). (4) CO terminally bonded to P and form P==C==O between 2198 and 2202 cm(-1). There are two different kinds of upsilon(CO) absorbances observed for adsorbed CO on Ni2P/MCM-48, Ni2P/ SBA-15 and Ni2P/SBA-16 catalysts. The absorbance observed at 2051-2055 cm(-1) for CO adsorption on Ni2P/MCM-48, Ni2P/SBA-15 and Ni2P/SBA-16 catalysts is due to the formation of Ni(CO)4 species. The other upsilon absorbances observed at 2093-2096 cm(-1) was attributed to CO terminally bonded to cus Ni(delta+) (0<delta<1) sites.
Liu
Qian-qian
QQ
State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China. qianqianliu902@yahoo.cn
Ji
Sheng-fu
SF
Wu
Ping-yi
PY
Hu
Lin-hua
LH
Huang
Xiao-fan
XF
Zhu
Ji-qin
JQ
Li
Cheng-yue
CY