Effect of acid etching duration on tensile bond strength of composite resin bonded to erbium:yttrium-aluminium-garnet laser-prepared dentine. Preliminary study.
The purpose of this study was to compare the tensile bond strength of composite resin bonded to erbium:yttrium-aluminium-garnet (Er:YAG) laser-prepared dentine after different durations of acid etching. The occlusal third of 68 human third molars was removed in order to expose the dentine surface. The teeth were randomly divided into five groups: group B (control group), prepared with bur and total etch system with 15 s acid etching [37% orthophosphoric acid (H(3)PO(4))]; group L15, laser photo-ablated dentine (200 mJ) (laser irradiation conditions: pulse duration 100 micros, air-water spray, fluence 31.45 J/ cm(2), 10 Hz, non-contact hand pieces, beam spot size 0.9 mm, irradiation speed 3 mm/s, and total irradiation time 2 x 40 s); group L30, laser prepared, laser conditioned and 30 s acid etching; group L60, laser prepared, laser conditioned and 60 s acid etching; group L90, laser prepared, laser conditioned and 90 s acid etching. A plot of composite resin was bonded onto each exposed dentine and then tested for tensile bond strength. The values obtained were statistically analysed by analysis of variance (ANOVA) coupled with the Tukey-Kramer test at the 95% level. A 90 s acid etching before bonding showed the best bonding value (P < 0.05) when compared with all the other groups including the control group. There is no significance difference between other groups, nor within each group and the control group. There was a significant increase in tensile bond strength of the samples acid etched for 90 s.
Chousterman
M
M
Department of Dental Sciences, Faculty of Medicine, University of Liege, Quai Godfroid Kurth, 45, 4000, Liege, Belgium.
Heysselaer
D
D
Dridi
S M
SM
Bayet
F
F
Misset
B
B
Lamard
L
L
Peremans
A
A
Nyssen-Behets
C
C
Nammour
S
S
D000134:Acid Etching, Dental / Q000379:methods*; D003188:Composite Resins; D001840:Dental Bonding / Q000379:methods*; D045662:Dental Etching / Q000379:methods; D003799:Dental Stress Analysis; D003804:Dentin / Q000502:physiology / Q000528:radiation effects; D006801:Humans; D066298:In Vitro Techniques; D053844:Lasers, Solid-State / Q000627:therapeutic use*; D028022:Low-Level Light Therapy / Q000379:methods*; D013718:Tensile Strength; D013997:Time Factors
D003188:Composite Resins
J Clin Laser Med Surg. 2004 Feb;22(1):35-41
15117485
Lasers Med Sci. 2009 Jan;24(1):53-7
18034284
J Dent Res. 1996 Jan;75(1):599-605
8655766
J Dent Res. 1998 Jun;77(6):1404-14
9649169
Photomed Laser Surg. 2007 Oct;25(5):373-80
17975950
Photomed Laser Surg. 2008 Oct;26(5):495-500
18800947
Photomed Laser Surg. 2009 Apr;27(2):317-23
18800944
J Dent. 2007 May;35(5):398-402
17222958
Lasers Surg Med. 2004;35(1):51-7
15278928
J Dent Res. 2002 Feb;81(2):119-22
11827256
J Dent. 2004 Jul;32(5):399-405
15193789
Dent Mater. 1997 Jul;13(4):246-51
11696904
Dent Mater. 2005 Jul;21(7):616-24
15978270
Lasers Surg Med. 1989;9(4):345-51
2503667
Photomed Laser Surg. 2007 Oct;25(5):393-401
17975952
Am J Dent. 2004 Oct;17(5):331-6
15575443
Lasers Med Sci. 2009 Jul;24(4):507-13
18351430
Photomed Laser Surg. 2007 Aug;25(4):239-44
17803378
Dent Mater. 2001 Jul;17(4):340-6
11356211
Lasers Med Sci. 2008 Apr;23(2):117-24
17479311
Lasers Surg Med. 1989;9(4):338-44
2761329