Effect of light-emitting diode (LED) curing modes on resin/dentin bond strength.
OBJECTIVE
This study aimed to compare the effect of three curing modes of a high-powered curing-light source on the shear bond strength and marginal gap of light- and dual-cured adhesive resin cements to dentin.


METHODS
Twelve freshly extracted intact human mandibular molars were selected for this study and stored in the saline solution. Three of the axial surfaces of the teeth were prepared to obtain flat dentinal surfaces. Thirty-six ceramic disks (4-mm diameter, 2- mm thick) were constructed from a pressable glass-ceramic (Vision). The discs were etched with hydrofluoric acid and primed, and then divided into two equal groups, groups I and II (n = 18 each). Two adhesive systems were used following manufacturer's instructions. The discs of group I were bonded to the conditioned dentin surface using adhesive resin (Rely X Veneer), and group II discs were bonded to dentin using Rely X ARC. For each group, the resin was cured using three modes (fast, ramp, pulse). Interfacial gap at the dentin/resin interface was measured at eight predetermined sites for each specimen using a stereomicroscope, and shear bond strength of the bonded specimens was carried out using a universal testing machine.


RESULTS
Ramp-cured specimens recorded significantly higher mean shear bond strengths for both dual- and light-polymerized resins than those with fast and pulse modes. Moreover, fewer interfacial gaps were found at the resin/dentin interface in association with ramp cure modes of both resins. Most failures were adhesive failures at the dentin-resin luting agent (RLA) interface in specimens polymerized using high-powered LED fast or pulse modes, while a cohesive failure pattern within the resin was associated with the ramp-curing mode.


CONCLUSIONS
Within the limitations of this study, the shear bond strength of an RLA to dentin was found to be enhanced with light- or dual-polymerized adhesive resin using an LED light in ramp mode, whereas shear bond strength was significantly lower when polymerized using LED in fast or pulse modes.
Fahmy
Nadia
N
Department of Fixed Prosthodontics, Faculty of Dentistry, October 6 University, Cairo, Egypt. nadiafahmy@hotmail.com
Naguib
Hanan
H
Guindy
Jylan El
JE
D000134:Acid Etching, Dental; D000268:Adhesiveness; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry / Q000528:radiation effects; D002516:Ceramics / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry / Q000528:radiation effects; D055117:Curing Lights, Dental / Q000145:classification*; D001840:Dental Bonding; D018772:Dental Marginal Adaptation; D003764:Dental Materials / Q000737:chemistry; D003776:Dental Porcelain / Q000737:chemistry; D003799:Dental Stress Analysis / Q000295:instrumentation; D003804:Dentin / Q000528:radiation effects* / Q000648:ultrastructure; D005899:Glass Ionomer Cements / Q000737:chemistry / Q000528:radiation effects; D006801:Humans; D006858:Hydrofluoric Acid / Q000737:chemistry; D008422:Materials Testing; D011092:Polyethylene Glycols / Q000737:chemistry / Q000528:radiation effects; D011108:Polymers / Q000737:chemistry / Q000528:radiation effects; D011109:Polymethacrylic Acids / Q000737:chemistry / Q000528:radiation effects; D019279:Resin Cements / Q000737:chemistry / Q000528:radiation effects*; D033081:Shear Strength; D013314:Stress, Mechanical; D013499:Surface Properties
D003188:Composite Resins; D003764:Dental Materials; D005899:Glass Ionomer Cements; D011108:Polymers; D011109:Polymethacrylic Acids; C462240:RelyX ARC; D019279:Resin Cements; C084550:Vitremer; D003776:Dental Porcelain; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate; C023506:Glass ceramics; D006858:Hydrofluoric Acid