Electroosmotic flow in vapor deposited silicon dioxide and nitride microchannels.
Electroosmotic flow was studied in thin film microchannels with silicon dioxide and silicon nitride sidewalls formed using plasma-enhanced chemical vapor deposition (PECVD). A sacrificial etching process was employed for channel fabrication allowing for cross-sections with heights of 3 mum, ranging from 2 mum to 50 mum in width. Flow rates were measured for single channels and multichannel electroosmotic pump structures for pH levels ranging from 2.6 to 8.3, and zeta potentials were calculated for both silicon dioxide and silicon nitride surfaces. Flow rates as high as 0.086 muLmin were measured for nitride multichannel pumps at applied electric fields of 300 Vmm. The surface characteristics of PECVD nitride were analyzed and compared to more well-known oxide surfaces to determine the density of amine sites compared to silanol sites.
Hamblin
Mark N
MN
Department of Electrical and Computer Engineering, Brigham Young University, Provo, Utah 84602, USA.
Edwards
John M
JM
Lee
Milton L
ML
Woolley
Adam T
AT
Hawkins
Aaron R
AR
Electrophoresis. 2004 Jan;25(2):203-13
14743474
Anal Chem. 1999 Apr 15;71(8):1658-61
10221079
Electrophoresis. 2003 Nov;24(21):3563-76
14613181
Anal Chem. 2002 Dec 15;74(24):6259-68
12510747
Science. 1998 Oct 16;282(5388):484-7
9774277
Anal Chem. 2003 Aug 1;75(15):3758-64
14572041
Opt Express. 2005 Dec 26;13(26):10564-70
19503271
Lab Chip. 2005 May;5(5):501-5
15856085
Electrophoresis. 2006 Dec;27(24):4888-95
17117379
Electrophoresis. 2004 Jan;25(2):187-202
14743473
Opt Lett. 2004 Aug 15;29(16):1894-6
15357351
Biomicrofluidics. 2007 Jan 01;1(1):14101
19693350