The insulation performance of reactive parylene films in implantable electronic devices.
Parylene-C (poly-chloro-p-xylylene) is an appropriate material for use in an implantable, microfabricated device. It is hydrophobic, conformally deposited, has a low dielectric constant, and superb biocompatibility. Yet for many bioelectrical applications, its poor wet adhesion may be an impassable shortcoming. This research contrasts parylene-C and poly(p-xylylene) functionalized with reactive group X (PPX-X) layers using long-term electrical soak and adhesion tests. The reactive parylene was made of complementary derivatives having aldehyde and aminomethyl side groups (PPX-CHO and PPX-CH2NH2 respectively). These functional groups have previously been shown to covalently react together after heating. Electrical testing was conducted in saline at 37 degrees C on interdigitated electrodes with either parylene-C or reactive parylene as the metal layer interface. Results showed that reactive parylene devices maintained the highest impedance. Heat-treated PPX-X device impedance was 800% greater at 10kHz and 70% greater at 1Hz relative to heated parylene-C controls after 60 days. Heat treatment proved to be critical for maintaining high impedance of both parylene-C and the reactive parylene. Adhesion measurements showed improved wet metal adhesion for PPX-X, which corresponds well with its excellent high frequency performance.
Seymour
John P
JP
Department of Biomedical Engineering, University of Michigan, Ann Arbor, MI 48109-2099, USA. seymourj@umich.edu
Elkasabi
Yaseen M
YM
Chen
Hsien-Yeh
HY
Lahann
Joerg
J
Kipke
Daryl R
DR
D001672:Biocompatible Materials / Q000737:chemistry*; D004563:Electrochemistry / Q000379:methods*; D008962:Models, Theoretical; D011108:Polymers / Q000737:chemistry*; D014992:Xylenes / Q000737:chemistry*
D001672:Biocompatible Materials; D011108:Polymers; D014992:Xylenes; C513670:poly(p-xylylene); C011055:parylene
Conf Proc IEEE Eng Med Biol Soc. 2005;2006:1028-31
17282362
Anal Chem. 2003 May 1;75(9):2117-22
12720350
Anal Chem. 2008 Jun 1;80(11):4119-24
18457409
Biomaterials. 2007 Sep;28(25):3594-607
17517431
IEEE Trans Neural Syst Rehabil Eng. 2005 Dec;13(4):524-41
16425835
Biomaterials. 1981 Oct;2(4):239-43
7326319
Biomaterials. 2002 Jul;23(13):2737-50
12059024
IEEE Eng Med Biol Mag. 2005 Sep-Oct;24(5):52-7
16248117
Med Biol Eng Comput. 1988 Jan;26(1):96-101
3199908