Surface properties and in vitro Streptococcus mutans adhesion to self-etching adhesives.
OBJECTIVE
The aim of this in vitro study was to investigate the surface properties and in vitro adhesion of Streptococcus mutans to dental self-etching two-step adhesives using an artificial mouth system.


METHODS
Carriers of a denture base resin supplemented with hydroxyapatite were manufactured, polished, and surface treated with various two-step self-etching dental adhesives (Clearfil Protect Bond, Silorane System Adhesive, Adper Scotchbond SE) according to the manufacturers' instructions. For each adhesive, 14 samples were inserted in an artificial mouth system and successively rinsed with mucin solutions (2 h) and Streptococcus mutans NCTC 10449 suspension (4 h). Surface free energy of the specimens was determined before and after mucin coating. The amount of adhered bacteria was quantified using a fluorescent dye (Resazurin/Alamar Blue) for viable cell quantification.


RESULTS
Before mucin coating, significant differences in surface free energies were found between the various adhesives, with total surface free energies ranging from 34.26 mJ/m(-2) to 42.30 mJ/m(-2). Mucin coating clearly levelled surface free energy differences. Significantly lower fluorescence intensities, indicating lower adhesion of Streptococcus mutans, were found for Silorane System Adhesive than for Clearfil Protect Bond and Adper Scotchbond SE, regardless of mucin coating.


CONCLUSIONS
The findings of this in vitro study indicate that the initial adhesion of Streptococcus mutans is lower to Silorane System Adhesive than to Clearfil Protect Bond or Adper Scotchbond SE. Our data correlated with the common thermodynamic approaches explaining streptococcal adherence to solid surfaces.
Hahnel
Sebastian
S
Department of Prosthetic Dentistry, Regensburg University Medical Center, Regensburg, Germany. Sebastian.Hahnel@klinik.uni-regensburg.de
Leyer
Andrea
A
Rosentritt
Martin
M
Handel
Gerhard
G
Bürgers
Ralf
R
D000180:Acrylic Resins / Q000737:chemistry; D001422:Bacterial Adhesion / Q000502:physiology*; D020099:Coated Materials, Biocompatible / Q000737:chemistry; D003764:Dental Materials / Q000737:chemistry*; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry; D005456:Fluorescent Dyes; D006801:Humans; D008422:Materials Testing; D009077:Mucins / Q000737:chemistry; D010078:Oxazines; D019279:Resin Cements / Q000737:chemistry; D062047:Silorane Resins; D013295:Streptococcus mutans / Q000502:physiology*; D013499:Surface Properties; D013500:Surface Tension; D017155:Wettability; D014966:Xanthenes
D000180:Acrylic Resins; C503075:Clearfil Protect Bond; D020099:Coated Materials, Biocompatible; D003764:Dental Materials; D017220:Dentin-Bonding Agents; D005456:Fluorescent Dyes; D009077:Mucins; D010078:Oxazines; C507521:Palapress Vario; D019279:Resin Cements; D062047:Silorane Resins; D014966:Xanthenes; C005843:resazurin; C041330:Scotchbond; D017886:Durapatite