Hydrogen storage properties of nanosized MgH2-0.1TiH2 prepared by ultrahigh-energy-high-pressure milling.
Magnesium hydride (MgH(2)) is an attractive candidate for solid-state hydrogen storage applications. To improve the kinetics and thermodynamic properties of MgH(2) during dehydrogenation-rehydrogenation cycles, a nanostructured MgH(2)-0.1TiH(2) material system prepared by ultrahigh-energy-high-pressure mechanical milling was investigated. High-resolution transmission electron microscope (TEM) and scanning TEM analysis showed that the grain size of the milled MgH(2)-0.1TiH(2) powder is approximately 5-10 nm with uniform distributions of TiH(2) among MgH(2) particles. Pressure-composition-temperature (PCT) analysis demonstrated that both the nanosize and the addition of TiH(2) contributed to the significant improvement of the kinetics of dehydrogenation and hydrogenation compared to commercial MgH(2). More importantly, PCT cycle analysis demonstrated that the MgH(2)-0.1TiH(2) material system showed excellent cycle stability. The results also showed that the DeltaH value for the dehydrogenation of nanostructured MgH(2)-0.1TiH(2) is significantly lower than that of commercial MgH(2). However, the DeltaS value of the reaction was also lower, which results in minimum net effects of the nanosize and the addition of TiH(2) on the equilibrium pressure of dehydrogenation reaction of MgH(2).
Lu
Jun
J
Department of Metallurgical Engineering, University of Utah, 135 South 1460 East Room 412, Salt Lake City, Utah 84112-0114, USA.
Choi
Young Joon
YJ
Fang
Zhigang Zak
ZZ
Sohn
Hong Yong
HY
Rönnebro
Ewa
E