Magnetic properties of iron particles embedded in multiwall carbon nanotubes.
Iron nanoparticles are embedded in multiwall carbon nanotubes by the chemical vapor deposition, where benzene and ferrocene are taken as precursor materials. Varying quantity of iron particles are embedded in these tubes by taking different amount of ferrocene. These particles exhibit a magnetic moment up to 98 emu/g and an enhanced coercivity in the range of 500-2000 Oe. Negative magnetoresistance approximately 10% is observed in the presence of magnetic field up to 11 T applied at various temperatures in the range of 1.3 K-300 K. It is argued that the enhanced coercivity is due to the shape anisotropy. The negative magnetoresistance is believed to be due to the weak localization and spin dependent scattering of electrons by the ferromagnetic particles. In addition we also observe a dependence of the magnetoresistance on the direction of applied field and this is correlated with the shape anisotropy of the Fe particles.
Arya
Ved Prakash
VP
Department of Physics, Indian Institute of Science, Bangalore 560012, India.
Prasad
V
V
Kumar
P S Anil
PS
D016880:Anisotropy; D007501:Iron / Q000737:chemistry; D008280:Magnetics; D037742:Nanotubes, Carbon / Q000737:chemistry; D013696:Temperature
D037742:Nanotubes, Carbon; D007501:Iron