Carbonated apatites obtained by the hydrolysis of monetite: influence of carbonate content on adhesion and proliferation of MC3T3-E1 osteoblastic cells.
The influence of the carbonate content in apatites on the adhesion and the proliferation of MC3T3-E1 osteoblastic cells was investigated. B-type carbonated apatites (DCAps) were prepared by the hydrolysis of monetite (CaHPO(4), DCP) in solutions with a carbonate concentration ranging from 0.001 to 0.075 mol l(-1). Stoichiometric hydroxyapatite (DCAp0) was synthesized in carbonate-free solution. MC3T3-E1 cells were seeded on the compacted DCAps and cell adhesion and proliferation were analysed after 24h and 7 days, respectively, using a MTS assay and fluorescence microscopy. Cell adhesion tends to increase with increasing carbonate content for carbonate contents between 0 and 6.9 wt.% and levels out to an acceptable value (+ or - 50% compared to the control) for carbonate contents between 6.9 and 16.1 wt.%. Only DCAps with a carbonate content equal to or higher than 11% support high cell proliferation comparable to the control. On the latter DCAps, the cells have a spread morphology and form a near-confluent layer. A decrease in charge density and crystallinity at the apatite surface, as well as the formation of more spheroidal crystals with increasing carbonate content, might attribute to changes in composition and three-dimensional structure of the protein adsorption layer and hence to the observed cell behaviour. Consequently, only DCAps with a high carbonate content, mimicking early in vivo mineralization, are possible candidates for bone regeneration.
Pieters
Ilse Y
IY
Department of Basic Medical Science, Biomaterials Group, Ghent University, De Pintelaan 185 (Building B, 4th Fl), B-9000 Ghent, Belgium. ilse.pieters@ugent.be
Van den Vreken
Natasja M F
NM
Declercq
Heidi A
HA
Cornelissen
Maria J
MJ
Verbeeck
Ronald M H
RM
D001031:Apatites / Q000494:pharmacology*; D002130:Calcium Phosphates / Q000737:chemistry*; D002254:Carbonates / Q000494:pharmacology*; D002448:Cell Adhesion / Q000187:drug effects; D049109:Cell Proliferation / Q000187:drug effects; D048430:Cell Shape / Q000187:drug effects; D002470:Cell Survival / Q000187:drug effects; D006863:Hydrogen-Ion Concentration / Q000187:drug effects; D006868:Hydrolysis / Q000187:drug effects; D008855:Microscopy, Electron, Scanning; D008856:Microscopy, Fluorescence; D010006:Osteoblasts / Q000166:cytology* / Q000187:drug effects*; D013055:Spectrophotometry, Infrared; D014961:X-Ray Diffraction
D001031:Apatites; D002130:Calcium Phosphates; D002254:Carbonates; C030782:carboapatite; C485838:calcium phosphate, monobasic, anhydrous