Nanosecond laser induced damage in RbTiOPO4: the missing influence of crystal quality.
Nanosecond laser induced damage in RbTiOPO(4) (RTP) an isomorphic material to the more widely known KTiOPO(4) (KTP) is studied in crystals with varying properties. The ionic conductivity along the z-axes of the tested crystals ranged from 1.5 10(-9) S/cm to 1.1 10(-12) S/cm. Further, different growth sectors with different absorption in the range of hundreds of ppm/cm and differing zones in inhomogeneous crystals have been investigated. Despite these important differences in crystal quality, no significant difference could be observed in the laser damage resistance at 1064 nm. Thus growth induced defects only play a minor role in nanosecond laser induced damage in RTP. Transient, laser induced defects are discussed in analogy with KTP as possible laser damage precursors.
Hildenbrand
Anne
A
Institut Fresnel, CNRS, Aix-Marseille Université, Ecole Centrale Marseille, Campus de Saint-Jérôme, 13013 Marseille, France.
Wagner
Frank R
FR
Natoli
Jean-Yves
JY
Commandré
Mireille
M
D017076:Computer-Aided Design; D003460:Crystallization / Q000379:methods*; D004867:Equipment Design; D004868:Equipment Failure; D019544:Equipment Failure Analysis; D010710:Phosphates / Q000737:chemistry* / Q000528:radiation effects; D015203:Reproducibility of Results; D012413:Rubidium / Q000737:chemistry* / Q000528:radiation effects; D012680:Sensitivity and Specificity; D014025:Titanium / Q000737:chemistry* / Q000528:radiation effects
D010710:Phosphates; C009495:titanium dioxide; D014025:Titanium; D012413:Rubidium