Controlled growth of heteroepitaxial zinc oxide nanostructures on gallium nitride.
ZnO epitaxial layers were grown on GaN underlying films by metalorganic chemical vapor deposition at various temperatures. An increase in growth temperature led to morphological changes from a smooth film with hexagonal-shaped surface pits to honeycomb-like nanostructures with deep hollow, and additionally resulted in a decrease in dislocation density in the interfacial layers. The reduced dislocation density at the higher growth temperature was attributed to an increase in the size of the critical nucleus and the low nucleation density at the initial stage. The shifts in the peak positions in the X-ray diffraction and photoluminescence were also observed in the samples grown at different temperatures, and were caused by the variation of residual strains after the complete coalescence of the nuclei.
Kong
Bo Hyun
BH
School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746, Korea.
Kim
Dong Chan
DC
Mohanta
Sanjay Kumar
SK
Han
Won Suk
WS
Cho
Hyung Koun
HK
Hong
Chang-Hee
CH
Kim
Hyung Gu
HG