The crystal polymorphism of calcium carbonate is determined by the matrix structure in quail eggs.
Two calcified structures, the eggshell and sperm-associated body (SB), are present in the eggs of the Japanese quail, Coturnix japonica. X-ray diffractometry showed that calcium carbonates take the form of calcite in the eggshell and aragonite in the SB. The aim of the present study was to identify the factors that determine the morphology of calcium carbonate crystals. The matrix of EDTA-treated eggshell was a meshwork of vesicles, 200 to 500 nm in diameter, connected by fine fibers or fibrous sheets. The matrix of SB cortex was a radiation of rod-shaped projections approximately 130 nm in width. In vitro crystal formation was achieved by adding dissociated matrix substances to test solutions. When eggshell matrix material was added, formation of calcite crystals, which had many vesicular holes on their surface, was observed. When SB matrix material dissociated by sonication was added, rhombohedral calcite crystals formed at protein concentrations of 100 microg/mL or lower, and elongated and bundled crystals formed at concentrations of 150 microg/mL or higher. When SB matrix material dissociated by pipetting was added, aragonite crystals formed. These observations indicate that the matrix structure is the principal factor in determining the crystal polymorphism of calcium carbonate.
Iwasawa
A
A
Department of Animal Resource Production, Gifu University, Gifu 501-1193, Japan.
Uzawa
M
M
Rahman
M A
MA
Ohya
Y
Y
Yoshizaki
N
N
D000818:Animals; D002119:Calcium Carbonate / Q000032:analysis*; D004528:Egg Shell / Q000737:chemistry* / Q000648:ultrastructure; D010063:Ovum / Q000737:chemistry*; D014961:X-Ray Diffraction
D002119:Calcium Carbonate