Surface modification of PCL-TCP scaffolds in rabbit calvaria defects: Evaluation of scaffold degradation profile, biomechanical properties and bone healing patterns.
Traditionally, polycaprolactone (PCL) based scaffolds tend to degrade at a slow rate. Pretreatment of polycaprolactone-20% tricalcium phosphate (PCL-TCP) scaffolds under alkaline conditions can be utilized to increase the degradation rate and improve mechanical properties. Three groups of PCL-TCP scaffolds with varying pretreatment exposures with sodium hydroxide (NaOH) were studied in a rabbit calvaria defect model and analyzed at 2, 4, 8, 12, and 24 weeks. (Group A: Untreated, Group B: 3 M NaOH/ 48 h and Group C: 3 M NaOH/96 h). Micro-CT analysis demonstrated that scaffolds with increased surface roughness (Groups B and C) showed a greater impact on the overall volume loss during the early healing period between 2 and 8 weeks as compared to the untreated group. In addition, greater bone formation was detected in NaOH treated scaffolds as compared to the untreated group throughout the experiment. Scaffolds with increased surface roughness generally reported higher push out test and compressive strength values from 4 to 8 weeks of early healing. Interestingly, the mechanical properties displayed a decline in values from 12 weeks onwards in the modified groups suggesting a favorable breakdown or weakening of PCL-TCP scaffolds tailored for replacement by new bone formation.
Yeo
Alvin
A
Department of Restorative Dentistry, National Dental Centre, SingHealth, Singapore.
Wong
Wah Jie
WJ
Teoh
Swee-Hin
SH
D000818:Animals; D001672:Biocompatible Materials; D001696:Biomechanical Phenomena; D001842:Bone and Bones / Q000473:pathology*; D002130:Calcium Phosphates / Q000737:chemistry*; D008297:Male; D010012:Osteogenesis; D011091:Polyesters / Q000737:chemistry*; D011817:Rabbits; D012886:Skull / Q000378:metabolism*; D012972:Sodium Hydroxide / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors; D055114:X-Ray Microtomography / Q000379:methods
D001672:Biocompatible Materials; D002130:Calcium Phosphates; D011091:Polyesters; C016240:polycaprolactone; D012972:Sodium Hydroxide; C018392:tricalcium phosphate