Tellurium nano-structure based NO gas sensor.
Tellurium nanotubes were grown on bare and silver/gold nanoparticle (nucleation centers) deposited silicon substrates by vacuum deposition technique at a substrate temperature of 100 degrees C under high vacuum conditions. Silver and gold nanoparticles prepared on (111) oriented silicon substrates were found to act as nucleation centers for growth of Tellurium nanostructures. Density of nanotubes was found to increase while their diameter reduced when grown using metallic nanoparticle template. These Te nanostructures were investigated for their gas sensitivity. Tellurium nanotubes on Ag templates showed better response to NO in comparison to H2S and NH3 gases. Selectivity in response to NO was improved in comparison to Te thin film sensors reported earlier. The gas sensing mechanism was investigated using Raman and X-ray photoelectron spectroscopy techniques. The interaction of NO is seen to yield increased adsorption of oxygen that in turn increases hole density and conductivity in the material.
Kumar
Vivek
V
Department of Physics, Barkatullah University, Bhopal 462026, M.R, India.
Sen
Shashwati
S
Sharma
M
M
Muthe
K P
KP
Jagannath
Gaur
N K
NK
Gupta
S K
SK
D005740:Gases; D006046:Gold / Q000737:chemistry; D049329:Nanostructures / Q000737:chemistry; D012834:Silver / Q000737:chemistry; D013691:Tellurium / Q000737:chemistry
D005740:Gases; D012834:Silver; D006046:Gold; D013691:Tellurium