Contribution of spatially and spectrally resolved cathodoluminescence to study crack-tip phenomena in silica glass.
A current controversy over the nature of fracture in silica glass is revisited in the light of additional experimental evidence obtained by cathodoluminescence (CL) spectroscopy in the immediate crack-tip zone of two different types of silica glass. The Letter describes the dual experimental output obtained by monitoring optically active oxygen defects in silica glass, as follows: (i) analysis of local crack-tip stoichiometry (i.e., lattice defect population); and, (ii) spatially resolved stress analysis ahead of the crack tip based on a piezo-spectroscopic (PS) approach. CL experiments provided us with direct access to crack-tip stress fields, thus unfolding some missing detail about the complex mechanochemical interactions occurring at the crack tip in silica glass.
Pezzotti
Giuseppe
G
Ceramic Physics Laboratory & Research Institute for Nanoscience, Kyoto Institute of Technology, Sakyo-ku, Matsugasaki, 606-8585 Kyoto, Japan.
Leto
Andrea
A