Optical, structural and electrical investigations of TiO2/multi-walled carbon nanotube composites.
Nanocomposites of TiO2 and multi-walled carbon nanotubes (MWNTs) were produced by the addition of different concentrations of MWNTs to a TiO2 sol matrix. Conductive coatings were prepared by spin coating the nanocomposite sols on glass substrates and sintering the samples at 300 degrees C for 15 min. No crystalline phase of TiO2 was formed at this temperature. The sheet resistance of the coatings was decreased from some hundreds of Momega/sq to just a few komega/sq by the addition of MWNTs to the TiO2 matrix. Moreover, sintering of the coatings in a reducing atmosphere has lead to a lower sheet resistance than that presented by coatings sintered in air. The lowest resistivity of 2.0 x 10(-1) omega x cm was obtained by coatings prepared with 5.0 mg/ml MWNTs in the composite sol. The optical, structural and electrical properties of the coatings were correlated and demonstrated.
Castro
M R S
MR
INM-Leibniz Institut für Neue Materialien GmbH, Campus D2 2, D-66123, Saarbrücken, Germany.
Oliveira
P W
PW
Schmidt
H K
HK