Very high frequency (beyond 100 MHz) PZT kerfless linear arrays.
This paper presents the design, fabrication, and measurements of very high frequency kerfless linear arrays prepared from PZT film and PZT bulk material. A 12-microm PZT thick film fabricated from PZT-5H powder/solution composite and a piece of 15-microm PZT-5H sheet were used to fabricate 32-element kerfless high-frequency linear arrays with photolithography. The PZT thick film was prepared by spin-coating of PZT sol-gel composite solution. The thin PZT-5H sheet sample was prepared by lapping a PZT-5H ceramic with a precision lapping machine. The measured results of the 2 arrays were compared. The PZT film array had a center frequency of 120 MHz, a bandwidth of 60% with a parylene matching layer, and an insertion loss of 41 dB. The PZT ceramic sheet array was found to have a center frequency of 128 MHz with a poorer bandwidth (40% with a parylene matching layer) but a better sensitivity (28 dB insertion loss).
Wu
Da-Wei
DW
NIH Center for Ultrasonic Transducer Technol., Univ. of Southern California, Los Angeles, CA, USA. daweiwu@usc.edu
Zhou
Qifa
Q
Geng
Xuecang
X
Liu
Chang-Geng
CG
Djuth
Frank
F
Shung
K Kirk
KK
D002516:Ceramics / Q000737:chemistry; D002857:Chromium / Q000737:chemistry; D006046:Gold / Q000737:chemistry; D007854:Lead / Q000737:chemistry*; D055617:Micro-Electrical-Mechanical Systems / Q000295:instrumentation*; D008855:Microscopy, Electron, Scanning; D014025:Titanium / Q000737:chemistry*; D014159:Transducers; D014463:Ultrasonography / Q000295:instrumentation*; D015040:Zirconium / Q000737:chemistry*
D002857:Chromium; C065536:lead titanate zirconate; D007854:Lead; D006046:Gold; D015040:Zirconium; D014025:Titanium