Formation of AgPt alloy nanoislands via chemical etching with tunable optical and catalytic properties.
An effective way is developed to fabricate AgPt alloy nanoislands on gold nanorods based on the galvanic replacement between Ag and PtCl(4)(2-) in the presence of cetyltrimethylammonium bromide (CTAB). The optical and catalytic properties benefit from the porous structure composed of AgPt nanoislands. A large red shift (265 nm) after etching is observed for longitudinal surface plasmon resonance (SPR) in comparison with Au@Pt0.1@Ag. Alloy compositions in bulk miscibility gap can be obtained and finely tuned from Ag(0.56)Pt(0.44) to Ag(0.38)Pt(0.62). A unique composition dependence is found for both electrocatalytic oxidation of methanol and catalytic oxidation of o-phenylenediamine (OPD) by hydrogen peroxide. In both systems, the highest catalytic activity is achieved at the alloy composition of Pt(0.62)Ag(0.38). Proper alloying with Ag not only improves the CO poisoning of Pt catalyst but also enhances the catalytic activity greatly.
He
Weiwei
W
National Center for Nanoscience and Technology, Beijing 100190, PR China.
Wu
Xiaochun
X
Liu
Jianbo
J
Zhang
Ke
K
Chu
Weiguo
W
Feng
Lili
L
Hu
Xiaona
X
Zhou
Weiya
W
Xie
Sishen
S
D000497:Alloys; D002384:Catalysis; D008855:Microscopy, Electron, Scanning; D046529:Microscopy, Electron, Transmission; D049329:Nanostructures; D010084:Oxidation-Reduction; D010984:Platinum; D012834:Silver; D013056:Spectrophotometry, Ultraviolet; D019265:Spectroscopy, Near-Infrared; D020349:Surface Plasmon Resonance
D000497:Alloys; D012834:Silver; D010984:Platinum