Photocatalytic cementitious materials: influence of the microstructure of cement paste on photocatalytic pollution degradation.
Incorporation of nanophotocatalysts into cementitious materials is an important development in the field of photocatalytic pollution mitigation. In this study, the photocatalytic nitrogen oxides (NO(x)) conversion by titanium dioxide (TiO(2)) blended cement pastes was used as a standard process to evaluate the internal factors that may influence the depollution performance. The chemical composition and microstructure of the TiO(2) modified cement pastes were characterized and analyzed. The active photocatalytic sites related to the surface area of TiO(2) are the key factor in determining the photocatalytic activity. Ordinary Portland cement pastes showed lower photocatalytic activity than white cement pastes probably due to the influence of minor metallic components. X-ray diffraction and thermal gravity analysis demonstrated that TiO(2) was chemically stable in the hydrated cement matrix. The NO(x) removal ability decreased with the increase of curing age. This could be attributed to the cement hydration products which filled up capillary pores forming diffusion barriers to both reactants and photons. It was also proved that surface carbonation could reduce the photocatalytic pollution removal efficiency after the hydration of cement.
Chen
Jun
J
Department of Civil and Structural Engineering, Research Center for Environmental Technology and Management, The Hong Kong Polytechnic University, Hung Hom, Hong Kong.
Poon
Chi-Sun
CS
D000397:Air Pollution / Q000032:analysis*; D002244:Carbon / Q000737:chemistry; D002384:Catalysis / Q000528:radiation effects; D003252:Construction Materials / Q000032:analysis*; D008027:Light; D008970:Molecular Weight; D009566:Nitrates / Q000737:chemistry; D009573:Nitrites / Q000737:chemistry; D016062:Porosity; D013997:Time Factors; D014025:Titanium / Q000737:chemistry
D009566:Nitrates; D009573:Nitrites; C009495:titanium dioxide; D002244:Carbon; D014025:Titanium