title: Failure mechanism of the all-polyethylene glenoid implant.
abstract: Fixation failure of glenoid components is the main cause of unsuccessful total shoulder arthroplasties. The characteristics of these failures are still not well understood, hence, attempts at improving the implant fixation are somewhat blind and the failure rate remains high. This lack of understanding is largely due to the fundamental problem that direct observations of failure are impossible as the fixation is inherently embedded within the bone. Twenty custom made implants, reflecting various common fixation designs, and a specimen set-up was prepared to enable direct observation of failure when the specimens were exposed to cyclic superior loads during laboratory experiments. Finite element analyses of the laboratory tests were also carried out to explain the observed failure scenarios. All implants, irrespective of the particular fixation design, failed at the implant-cement interface and failure initiated at the inferior part of the component fixation. Finite element analyses indicated that this failure scenario was caused by a weak and brittle implant-cement interface and tensile stresses in the inferior region possibly worsened by a stress raiser effect at the inferior rim. The results of this study indicate that glenoid failure can be delayed or prevented by improving the implant/cement interface strength. Also any design features that reduce the geometrical stress raiser and the inferior tensile stresses in general should delay implant loosening.
authors: Department of Mechanical Engineering, Imperial College London, Exhibition Road, London, SW7 2AZ, UK.
authors: Junaid
authors: J
authors: Sarah
authors: Gupta
authors: G
authors: Sanjay
authors: Sanghavi
authors: S
authors: Sanjay
authors: Anglin
authors: A
authors: Carolyn
authors: Roger
authors: R
authors: Emery
authors: Amis
authors: A
authors: Andrew
authors: Hansen
authors: H
authors: Ulrich
mesh_terms: D019544:Equipment Failure Analysis; D006801:Humans; D007593:Joint Instability / Q000209:etiology* / Q000503:physiopathology*; D007595:Joint Prosthesis / Q000009:adverse effects*; D020959:Polyethylene / Q000737:chemistry*; D011475:Prosthesis Failure; D012785:Shoulder Joint / Q000503:physiopathology* / Q000601:surgery*
chemical_list: D020959:Polyethylene