Effect of filler content of flowable composites on resin-cavity interface.
The purpose of this in vitro study was to evaluate marginal integrity and wall adaptation in 1- and 2-mm-deep cavities restored with a high filler-loaded flowable composite in comparison to a flowable composite with lower filler content and a conventional hybrid composite. 1-mm-deep dentin and 2-mm-deep enamel-dentin Class I cavities were prepared and restored with a self-etch adhesive and with one of the composites. Samples were crosscut and evaluated for marginal integrity and gap formation using a digital microscope. Selected samples were also observed using a scanning electron microscope. For 1-mm-deep cavities, no differences in marginal integrity and wall adaptation were observed among the three composites. For 2-mm-deep cavities, those restored with the bulk technique and with the higher filler-loaded flowable composite demonstrated a similar outcome as that of the conventional hybrid composite. On the effect of restorative techniques, cohesive enamel defects were observed in bulk-filled 2-mm-deep cavities. However, when the incremental technique was used in conjunction with the higher filler-loaded flowable composite and the conventional hybrid composite for 2-mm-deep cavities, superior results were obtained.
Ikeda
Ichiro
I
Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, Tokyo 113-8549, Japan. ikeda-ichiro@ikeda-shika.jp
Otsuki
Masayuki
M
Sadr
Alireza
A
Nomura
Tomomasa
T
Kishikawa
Ryuzo
R
Tagami
Junji
J
D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003737:Dental Cavity Preparation / Q000145:classification*; D003743:Dental Enamel / Q000648:ultrastructure*; D018772:Dental Marginal Adaptation; D003764:Dental Materials / Q000737:chemistry*; D003804:Dentin / Q000648:ultrastructure*; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D011109:Polymethacrylic Acids / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D013499:Surface Properties; D013696:Temperature; D013997:Time Factors; D014867:Water / Q000737:chemistry
C112828:Clearfil AP-X; C501417:Clearfil Flow FX; C438313:Clearfil SE Bond; D003188:Composite Resins; D003764:Dental Materials; D008689:Methacrylates; D011109:Polymethacrylic Acids; D019279:Resin Cements; C541508:clearfil majesty; C111840:flowable hybrid composite; D014867:Water