Effect of surface area enhancement on the adsorption of Bovine Serum Albumin onto titanium dioxide.
The equilibrium and the kinetics of BSA adsorption onto specific surface area changed TiO(2) by heat treatment were studied. The TiO(2) was treated at 100 and 200 degrees C for 24h. The specific surface areas of TiO(2) characterized by BET method were measured as 48.9m(2)/g and 53.0m(2)/g for 100 and 200 degrees C, respectively. The adsorption rate and the equilibrium experiments were carried out at pH 4 for 40 degrees C. The rate kinetics for the adsorption of BSA was best fitted with the pseudo-first-order kinetic model. The equilibrium process was described by the Langmuir and Freundlich isotherm models. The adsorption capacities (Q(0)) calculated from the Langmuir isotherm model were 40.6 and 44.4mg/g for heat-treated TiO(2) at 100 and 200 degrees C, respectively. The adsorption of BSA increased with increasing surface area of TiO(2). The zeta potential values of the 100- and 200 degrees C-treated TiO(2) were found as -2.57mV and 0.39mV, respectively, showing that the interaction between TiO(2) with BSA increased with increasing temperature of heat treatment for TiO(2).
Kopac
Turkan
T
Department of Chemistry, Zonguldak Karaelmas University, Zonguldak, Turkey. turkankopac@yahoo.com
Bozgeyik
Kadriye
K
D000327:Adsorption; D000818:Animals; D002417:Cattle; D006863:Hydrogen-Ion Concentration; D007700:Kinetics; D012710:Serum Albumin, Bovine / Q000737:chemistry*; D013499:Surface Properties; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
C009495:titanium dioxide; D012710:Serum Albumin, Bovine; D014025:Titanium