Fe2(SO4)3 as a binary oxidant and dopant to thin polyaniline nanowires with high conductivity.
This article exposes a facial approach to self-assemble polyaniline (PANI) nanowires with thin diameter (approximately 10 nm) and high room-temperature conductivity (approximately 10(0) S/cm) by using Fe(2)(SO(4))(3) as a binary oxidant and dopant. The new method not only saves hard templates and postprocess of template removal but also simplifies the reagent. Formation yield, diameter, and room-temperature conductivity of the nanowires are affected by the molar ratios of Fe(2)(SO(4))(3) to aniline. The low redox potential of Fe(2)(SO(4))(3) not only results in a thinner diameter and higher room-temperature conductivity (10(0) S/cm) of the nanowires but also shows a much weaker temperature dependence of resistivity and smaller characteristic Mott temperature (T(0) = 2.5 x 10(3) K).
Ding
Hangjun
H
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, P. R. China.
Long
Yunze
Y
Shen
Jiaoyan
J
Wan
Meixiang
M