Effects of endodontic post surface treatment, dentin conditioning, and artificial aging on the retention of glass fiber-reinforced composite resin posts.
BACKGROUND
Several post surface treatments with or without the application of a bonding agent have been recommended to improve the bond strength of resin cements to posts. A regimen that produces the maximum bond strength of glass fiber-reinforced composite resin posts has not been verified.


OBJECTIVE
The purpose of this study was to evaluate the influence of post surface conditioning methods and artificial aging on the retention and microleakage of adhesively luted glass fiber-reinforced composite resin posts.


METHODS
Seventy-two endodontically treated single-rooted teeth were prepared for glass fiber-reinforced composite resin posts. The posts were submitted to 3 different surface treatments (n=24), including no treatment, etching with phosphoric acid, and airborne-particle abrasion. Subgroups of the posts (n=8) were then allocated for 3 different experimental conditions: no artificial aging, no bonding agent; no artificial aging, bonding agent; or artificial aging, bonding agent. The posts were luted with resin cement (Calibra). Post retention was measured in tension at a crosshead speed of 2 mm/min. The posts assigned for microleakage investigation were placed in fuchsin dye for 72 hours. The dislodged posts and the post spaces were examined microscopically to evaluate the mode of failure and explore the microleakage. Data were analyzed by 2-way ANOVA followed by Tukey HSD test (alpha=.05).


RESULTS
The mean (SD) retention values for test groups ranged from 269 (63.8) to 349 (52.2) N. The retention values of the airborne-particle-abrasion group were significantly higher than those of the acidic-treatment and no-treatment groups. The application of bonding agent on the post surface produced no significant influence on retention. The mean retention values after artificial aging were significantly higher than without artificial aging. Microscopic evaluation demonstrated that the failure mode was primarily mixed.


CONCLUSIONS
Treating the surface of the posts with phosphoric acid for 15 seconds before cementation produced no significant improvement in post retention. Airborne-particle abrasion of the surface of the post significantly improved post retention.
Albashaireh
Zakereyya S
ZS
Jordan University of Science and Technology, Irbid 22110, Jordan. albashai@just.edu.jo
Ghazal
Muhamad
M
Kern
Matthias
M
D000134:Acid Etching, Dental / Q000379:methods; D003188:Composite Resins / Q000737:chemistry; D003738:Dental Cements / Q000737:chemistry*; D003763:Dental Leakage / Q000517:prevention & control; D017267:Dental Prosthesis Design; D017268:Dental Prosthesis Retention / Q000379:methods*; D003804:Dentin / Q000187:drug effects; D017220:Dentin-Bonding Agents / Q000737:chemistry / Q000494:pharmacology*; D005898:Glass; D006801:Humans; D011176:Post and Core Technique / Q000295:instrumentation*; D018915:Root Canal Preparation / Q000379:methods*; D013499:Surface Properties; D014016:Tissue Conditioning, Dental / Q000379:methods*
D003188:Composite Resins; D003738:Dental Cements; D017220:Dentin-Bonding Agents; C009753:fiberglass