Novel ferromagnetic materials of SmCo5 nanoparticles in single-nanometer size: chemical syntheses and characterizations.
We first succeeded in preparing ferromagnetic materials of SmCo(5) nanoparticles in sizes of single nanometers by a chemical route using a polyol process. In order to produce ferromagnetic SmCo(5) nanoparticles with a CaCu(5)-type structure, the chemical preparation was conducted under a molar ratio of 1:1.3 of Sm:Co as compositions of metallic precursors when tetraethylene glycol (TEG), and oleic acid and oleylamine were used as a reductant and protectant, respectively. However, XRD profiles of the products showed the presence of oxides and other by-products besides the CaCu(5)-type structured nanoparticles. The best metallic precursors and protective reagent to prevent oxidization under reaction were SmCl(3) and Co(acac)(3), and 1-adamantanecarboxylic acid (ACA) and poly(N-vinyl-2-pyrrolidone) (PVP), respectively when TEG was used as the reducing reagent. We found that oxides and other by-products were not detected and pure SmCo(5) nanoparticles with the CaCu(5)-type structure were prepared under the chemical condition. The SmCo(5) nanoparticles coated by ACA and PVP were 6.2 nm in diameter and showed a coercivity of 1500 Oe at 300 K.
Matsushita
Toru
T
Department of Applied Chemistry, Faculty of Engineering, Tokyo University of Science Yamaguchi, Yamaguchi, Japan.
Iwamoto
Takashi
T
Inokuchi
Makoto
M
Toshima
Naoki
N