In-situ powder X-ray diffraction investigation of reaction pathways for the BaCO(3)-CeO(2)-In(2)O(3) and CeO(2)-In(2)O(3) systems.
We report the first in-situ powder X-ray diffraction (PXRD) study of the BaCO(3)-CeO(2)-In(2)O(3) and CeO(2)-In(2)O(3) systems in air over a wide range of temperature between 25 and 1200 degrees C. Herein, we are investigating the formation pathway and chemical stability of perovskite-type BaCe(1-x)In(x)O(3-delta) (x = 0.1, 0.2, and 0.3) and corresponding fluorite-type Ce(1-x)In(x)O(2-delta) phases. The potential direct solid state reaction between CeO(2) and In(2)O(3) for the formation of indium-doped fluorite-type phase is not observed even up to 1200 degrees C in air. The formation of the BaCe(1-x)In(x)O(3-delta) perovskite structures was investigated and rationalized using in-situ PXRD. Furthermore the decomposition of the indium-doped perovskites in CO(2) is followed using high temperature diffraction and provides insights into the reaction pathway as well as the thermal stability of the Ce(1-x)In(x)O(3-delta) system. In CO(2) flow, BaCe(1-x)In(x)O(3-delta) decomposes above T = 600 degrees C into BaCO(3) and Ce(1-x)In(x)O(2-delta). Furthermore, for the first time, the in-situ PXRD confirmed that Ce(1-x)In(x)O(2-delta) decomposes above 800 degrees C and supported the previously claimed metastability. The maximum In-doping level for CeO(2) has been determined using PXRD. The lattice constant of the fluorite-type structure Ce(1-x)In(x)O(2-delta) follows the Shannon ionic radii trend, and crystalline domain sizes were found to be dependent on indium concentration.
Bhella
Surinderjit Singh
SS
Department of Chemistry, University of Calgary, Calgary, AB, T2N 1N4, Canada.
Shafi
Shahid P
SP
Trobec
Francesca
F
Bieringer
Mario
M
Thangadurai
Venkataraman
V