Colloidal gas-liquid condensation of polystyrene latex particles with intermediate kappa a values (5 to 160, a >> kappa(-1)).
Polystyrene latex particles showed gas-liquid condensation under the conditions of large particle radius (a >> kappa(-1)) and intermediate kappa a, where kappa is the Debye-Hückel parameter and a is the particle radius. The particles were dissolved in deionized water containing ethanol from 0 to 77 vol %, settled to the bottom of the glass plate within 1 h, and then laterally moved toward the center of a cell over a 20 h period in reaching a state of equilibrium condensation. All of the suspensions that were 1 and 3 microm in diameter and 0.01-0.20 vol % in concentration realized similar gas-liquid condensation with clear gas-liquid boundaries. In 50 vol % ethanol solvent, additional ethanol was added to enhance the sedimentation force so as to restrict the particles in a monoparticle layer thickness. The coexistence of gas-liquid-solid (crystalline solid) was microscopically recognized from the periphery to the center of the condensates. A phase diagram of the gas-liquid condensation was created as a function of KCl concentration at a particle diameter of 3 microm, 0.10 vol % concentration, and 50:50 water/ethanol solvent at room temperature. The miscibility gap was observed in the concentration range from 1 to 250 microM. There was an upper limit of salt concentration where the phase separation disappeared, showing nearly critical behavior of macroscopic density fluctuation from 250 microM to 1 mM. These results add new experimental evidence to the existence of colloidal gas-liquid condensation and specify conditions of like-charge attraction between particles.
Department of Innovative and Engineered Materials, Tokyo Institute of Technology, 4259 Midori-ku, Nagatsuta-cho, Yokohama, Kanagawa 226-8502, Japan. ishikawa.m.ae@m.titech.ac.jp
Masamichi
M
Ishikawa
Ryota
R
Kitano
D003102:Colloids / Q000737:chemistry; D000431:Ethanol / Q000737:chemistry*; D005740:Gases / Q000737:chemistry; D010316:Particle Size; D011137:Polystyrenes / Q000737:chemistry*; D013499:Surface Properties
D003102:Colloids; D005740:Gases; D011137:Polystyrenes; D000431:Ethanol