The effect of calcium ions and sodium silicate on the adsorption of a model anionic flotation collector on magnetite studied by ATR-FTIR spectroscopy.
Previous studies have shown that agglomeration of the magnetite concentrate after reverse flotation of apatite is negatively affected by the collector species adsorbed on the surface of magnetite. In this work, the effect of ionic strength, calcium ions and sodium silicate on the unwanted adsorption of a model anionic flotation collector on synthetic magnetite was studied in situ using attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR). The amount of collector adsorbed was found to increase with increasing ionic strength at pH 8.5 providing evidence to the contribution of electrostatic forces to the adsorption of the collector. Adding sodium silicate to the system resulted in a threefold decrease in the amount of collector adsorbed compared to when no sodium silicate was added, confirming the depressing activity of sodium silicate on magnetite. Calcium ions were shown to increase the adsorption of both the collector and sodium silicate on magnetite. The depressing effect of sodium silicate on collector adsorption was completely suppressed in the presence of calcium ions under the conditions studied. Furthermore, the amount of collector adsorbed on magnetite from the silicate-collector solution increased 14 times upon addition of calcium ions suggesting that calcium ions in the process water may increase undesired adsorption of the collector on the iron oxide.
Potapova
E
E
Division of Chemical Engineering, Luleå University of Technology, SE-971 87 Luleå, Sweden. elisaveta.potapova@ltu.se
Grahn
M
M
Holmgren
A
A
Hedlund
J
J