Analysis of ultra-thin HfO(2)/SiON/Si(001): comparison of three different techniques.
Composition depth profiling of HfO(2) (2.5 nm)/SiON (1.6 nm)/Si(001) was performed by three diffetent analytical techniques: high-resolution Rutherford backscattering spectroscopy (HRBS), angle-resolved X-ray photoelectron spectroscopy (AR-XPS) and high-resolution elastic recoil detection (HR-ERD). By comparing these results we found the following: (1) HRBS generally provides accurate depth profiles. However, care must be taken in backgroud subtraction for depth profiling of light elements. (2) In the standard AR-XPS analysis, a simple exponential formula is often used to calculate the photoelectron escape probability. This simple formula, however, cannot be used for the precise depth profiling. (2) Although HR-ERD is the most reliable technique for the depth profiling of light elements, it may suffer from multiple scattering, which deteriorates the depth resolution, and also may cause a large background.
Kimura
Kenji
K
Department of Micro Engineering, Kyoto University, Japan. kimura@kues.kyoto-u.ac.jp
Nakajima
Kaoru
K
Conard
Thierry
T
Vandervorst
Wilfried
W
Bergmaier
Andreas
A
Dollinger
Günther
G