Preparation and capacitance property of MnO2-pillared Ni(2+)-Fe3+ layered double hydroxides nanocomposite.
A novel MnO(2)-pillared Ni(2+)-Fe(3+) layered double hydroxides nanocomposite has been successfully fabricated using an intercalation/reduction reaction followed by heating treatment. The structural evolution of the samples obtained at different stages has been characterized by XRD, TEM, XPS, IR and N(2) adsorption-desorption. The layered structure of MnO(2)-pillared Ni(2+)-Fe(3+) layered double hydroxides nanocomposite can be maintained at 300 °C, and the obtained material has a large surface area of 202 m(2) g(-1). Electrochemical studies indicate that the material obtained by heating at 200 °C exhibits an ideal capacitive behavior and good cycling property in 1 mol L(-1) Na(2)SO(4) aqueous solution, and the specific capacitance value was 190 F g(-1) at a scan rate of 5 mV s(-1).
Li
Hongjuan
H
Key Laboratory of Applied Surface and Colloid Chemistry, Shaanxi Normal University, Ministry of Education, Xi'an 710062, PR China.
Zhu
Gang
G
Yang
Zupei
Z
Wang
Zenglin
Z
Liu
Zong-Huai
ZH