Effect of hydrophilicity of polyaniline particles on their electrorheology: steady flow and dynamic behaviour.
Electrorheological properties of suspensions are considerably affected by hydrophilicity of suspension particles. As a model material, polyaniline base powder protonated with sulfamic, tartaric, or perfluorooctanesulfonic acids provided particles of various hydrophilicity. The experiments revealed that, in the absence of electric field, due to a good compatibility of hydrophobic polyaniline particles with silicone-oil medium, their interactions were limited and the viscosity of suspension was low. When the electric field was applied, the rigidity of the polarized chain structure of the particles increased and, consequently, viscosity increased as well. In the contrast, the field-off suspension viscosity of highly interacting hydrophilic particles, which are incompatible with the oil, and where particle aggregation may set in, was high especially at low shear rates, and the material had a pseudoplastic character. Then, a relative increase in viscosity due to the polarization of the particles or their clusters in the electric field was much lower than in the former case. Due to a different primary structure of suspension, depending on the particle compatibility with the oil the field-off storage modulus of suspensions of hydrophobic particles was lower than the loss modulus, while in suspensions of hydrophilic particles the former modulus dominated. In both cases, an increase in elasticity with increasing electric field strength was higher than that in viscosity.
Tomas Bata University in Zlin, Faculty of Technology, TGM Sq. 275, 762 72 Zlin, Czech Republic. stenicka@ft.utb.cz
Martin
M
Stěnička
Vladimír
V
Pavlínek
Petr
P
Sáha
Natalia V
NV
Blinova
Jaroslav
J
Stejskal
Otakar
O
Quadrat
D000814:Aniline Compounds / Q000737:chemistry*; D004563:Electrochemistry; D057927:Hydrophobic and Hydrophilic Interactions; D007700:Kinetics; D010316:Particle Size; D013499:Surface Properties; D013535:Suspensions / Q000737:chemistry; D014783:Viscosity
D000814:Aniline Compounds; D013535:Suspensions; C416807:polyaniline