Controlling cellular activity by manipulating silicone surface roughness.
Silicone elastomers exhibit a broad range of beneficial properties that are exploited in biomaterials. In some cases, however, problems can arise at silicone elastomer interfaces. With breast implants, for example, the fibrous capsule that forms at the silicone interface can undergo contracture, which can lead to the need for revision surgery. The relationship between surface topography and wound healing--which could impact on the degree of contracture--has not been examined in detail. To address this, we prepared silicone elastomer samples with rms surface roughnesses varying from 88 to 650 nm and examined the growth of 3T3 fibroblasts on these surfaces. The PicoGreen assay demonstrated that fibroblast growth decreased with increases in surface roughness. Relatively smooth (approximately 88 nm) PDMS samples had ca. twice as much fibroblast DNA per unit area than the 'bumpy' (approximately 378 nm) and very rough (approximately 604 and approximately 650 nm) PDMS samples. While the PDMS sample with roughness of approximately 650 nm had significantly fewer fibroblasts at 24h than the TCP control, fibroblasts on the smooth silicone surprisingly reached confluence much more rapidly than on TCP, the gold standard for cell culture. Thus, increasing the surface roughness at the sub-micron scale could be a strategy worthy of consideration to help mitigate fibroblast growth and control fibrous capsule formation on silicone elastomer implants.
Prasad
Babu R
BR
National Centre for Biomedical Engineering Science, National University of Ireland, Galway, Ireland.
Brook
Michael A
MA
Smith
Terry
T
Zhao
Shigui
S
Chen
Yang
Y
Sheardown
Heather
H
D'souza
Renita
R
Rochev
Yuri
Y
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry* / Q000378:metabolism; D018427:Breast Implants; D049109:Cell Proliferation; D004129:Dimethylpolysiloxanes / Q000737:chemistry / Q000378:metabolism; D005260:Female; D005347:Fibroblasts / Q000166:cytology* / Q000378:metabolism; D006801:Humans; D051379:Mice; D018625:Microscopy, Atomic Force; D008855:Microscopy, Electron, Scanning; D041681:NIH 3T3 Cells; D012826:Silicone Elastomers / Q000737:chemistry / Q000378:metabolism; D012828:Silicones / Q000737:chemistry* / Q000378:metabolism; D017550:Spectroscopy, Fourier Transform Infrared; D013499:Surface Properties; D013997:Time Factors
D001672:Biocompatible Materials; D004129:Dimethylpolysiloxanes; D012826:Silicone Elastomers; D012828:Silicones; C013830:baysilon