title: Synthesis of high thermally-stable mesoporous alumina particles.
abstract: The mesoporous undoped and Si-doped alumina were prepared with an ultrasonic spray process, and found to have well-developed mesopore structures and large surface areas. The mesoporous Si-doped alumina has a high thermal stability up to 1473 K. Its surface area and pore volume were found to slowly decrease with increasing temperature. Mesoporous undoped alumina is transformed to gamma-alumina at 1073 K, whereas the amorphous nature of the pore walls of the Si-doped alumina is maintained up to 1073 K. When heat treatment was carried out at 1473 K for 2 h, the mesopore-networks of the undoped alumina collapsed, and then all the pore walls were converted into the alpha-alumina phase. In contrast, the mesoporosity of the Si-doped alumina persisted during heat treatment, and its pore walls were transformed to gamma-alumina. The decreases in the pore volume of the undoped alumina at 1073 K and 1473 K were found to be 36% and 99% respectively, but for the Si-doped alumina were only 24% and 36% respectively. The surface area of the undoped alumina at 1473 K was found to be 11 m2/g but that of the Si-doped samples at the same temperature is higher than 100 m2/g. Thus this mesoporous Si-doped alumina can be used as a catalytic support in reactions at high temperatures.
authors.affiliation: Department of Chemical and Biomolecular Engineering, KAIST 373-1 Guseong-dong, Yuseong-gu, Daejeon 305-701, Republic of Korea.
authors.forename: Lee-Hwa
authors.initials: LH
authors.lastname: Song
authors.forename: Seung Bin
authors.initials: SB
authors.lastname: Park