Stacked porous tin phosphate nanodisk anodes.
Stacked porous octahedral tin phosphate Sn(2)P(2)O(7) nanodisks, with a thickness and a width of 20 nm and 200 nm, respectively, were prepared from quenching hydrothermally prepared (SnHPO(4))(2).H(2)O at 600 degrees C. The first discharge capacity was 600 mA h g(-1) while the capacity retention, even after 220 cycles, was 93%.