Depletion-induced shape and size selection of gold nanoparticles.
For nanoparticle-based technologies, efficient and rapid approaches that yield particles of high purity with a specific shape and size are critical to optimize the nanostructure-dependent optical, electrical, and magnetic properties, and not bias conclusions due to the existence of impurities. Notwithstanding the continual improvement of chemical methods for shaped nanoparticle synthesis, byproducts are inevitable. Separation of these impurities may be achieved, albeit inefficiently, through repeated centrifugation steps only when the sedimentation coefficient of the species shows sufficient contrast. We demonstrate a robust and efficient procedure of shape and size selection of Au nanoparticles (NPs) through the formation of reversible flocculates by surfactant micelle induced depletion interaction. Au NP flocculates form at a critical surfactant micelle molar concentration, C(m)* where the number of surfactant micelles is sufficient to induce an attractive potential energy between the Au NPs. Since the magnitude of this potential depends on the interparticle contact area of Au NPs, separation is achieved even for the NPs of the same mass with different shape by tuning the surfactant concentration and extracting flocculates from the sediment by centrifugation or gravitational sedimentation. The refined NPs are redispersed by subsequently decreasing the surfactant concentration to reduce the effective attractive potential. These concepts provide a robust method to improve the quality of large scale synthetic approaches of a diverse array of NPs, as well as fine-tune interparticle interactions for directed assembly, both crucial challenges to the continual realization of the broad technological potential of monodispersed NPs.
Park
Kyoungweon
K
Materials and Manufacturing Directorate, Air Force Research Laboratory, Wright-Patterson AFB, Ohio 45433-7702, USA.
Koerner
Hilmar
H
Vaia
Richard A
RA
D006046:Gold / Q000737:chemistry*; D053768:Metal Nanoparticles / Q000737:chemistry*; D008823:Micelles; D036103:Nanotechnology / Q000379:methods; D010316:Particle Size; D013499:Surface Properties; D013501:Surface-Active Agents / Q000737:chemistry
D008823:Micelles; D013501:Surface-Active Agents; D006046:Gold