High-sensitivity Raman scattering substrate based on Au/La(0.7)Sr(0.3)MnO(3) periodic arrays.
We have developed Au/La(0.7)Sr(0.3)MnO(3) (Au/LSMO) periodic arrays with tunable surface plasmon properties that can be used as novel surface-enhanced Raman scattering (SERS) substrates. The periodic arrays are created by electron beam lithography of LSMO resist and metal film deposition. The LSMO electron beam resist is unique in that it exhibits either positive or negative resist behaviors depending on the electron beam dosage. Interestingly, surface plasmon behavior of the arrays can be controlled by just changing the electron beam dosage when presented with a fixed design pattern. Scanning confocal microscopy and spectral microreflectometry have been adapted to directly demonstrate this unique behavior. Furthermore, we show that our novel Au/LSMO array can be used as a high-sensitivity Raman scattering substrate. To illustrate this working principle, the Au/LSMO periodic array is applied to enhance the Raman scattering of a thin film containing 0.1 wt % poly-3-hexylthiophene (P3HT) in poly(methyl methacrylate) (PMMA). By controlling the geometry of the patterned substrate that exhibits gold surface plasmon near the excitation wavelength, we can enhance the intensity of Raman scattering of P3HT at 1350 cm(-1) up to 4 orders of magnitude as compared with previously generated planar Au substrates.
Wu
Ming-Chung
MC
Department of Materials Science and Engineering, National Taiwan University, Taipei 106-17, Taiwan.
Chou
Yi
Y
Chuang
Chih-Min
CM
Hsu
Che-Pu
CP
Lin
Jhih-Fong
JF
Chen
Yang-Fang
YF
Su
Wei-Fang
WF