Water-induced degradation of polymer solar cells studied by H2(18)O labeling.
Water-induced degradation of polymer photovoltaics based on the active materials poly(3-hexylthiophene) (P3HT) or poly[2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenylenevinylene] (MEHPPV) was studied. The solar cell devices comprised a bulk heterojunction formed by the active material and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) in a standard device geometry. The use of H2(18)O in conjunction with time-of-flight secondary ion mass spectrometry enabled mapping of the parts of the device that were induced by water. A comparison was made between the two active materials and between devices that were kept in the dark and devices that had been subjected to illumination under simulated sunlight. Devices that were exposed to ambient humidity were compared to devices exposed to saturated humidity. Finally, a comparison was made between results obtained using H2(18)O and earlier work involving 18O2. Water was found to have behavior similar to but not identical with molecular oxygen.
Norrman
Kion
K
Risø National Laboratory for Sustainable Energy, Technical University of Denmark, Frederiksborgvej 399, DK-4000 Roskilde, Denmark.
Gevorgyan
Suren A
SA
Krebs
Frederik C
FC