Reactive ballistic deposition of alpha-Fe2O3 thin films for photoelectrochemical water oxidation.
We report the preparation of alpha-Fe2O3 electrodes using a technique known as reactive ballistic deposition in which iron metal is evaporatively deposited in an oxygen ambient for photoelectrochemical (PEC) water oxidation. By manipulating synthesis parameters such as deposition angle, film thickness, and annealing temperature, we find that it is possible to optimize the structural and morphological properties of such films in order to improve their PEC efficiency. Incident photon to current conversion efficiencies (IPCE) are used to calculate an AM1.5 photocurrent of 0.55 mA/cm(2) for optimized films with an IPCE reaching 10% at 420 nm in 1 M KOH at +0.5 V versus Ag/AgCl. We also note that the commonly observed low photoactivity of extremely thin hematite films on fluorine-doped tin oxide substrates may be improved by modification of annealing conditions in some cases.
Hahn
Nathan T
NT
Department of Chemical Engineering, Texas Materials Institute, Center for Nano- and Molecular Science, The University of Texas at Austin, 1 University Station C0400, Austin, Texas 78712, USA.
Ye
Heechang
H
Flaherty
David W
DW
Bard
Allen J
AJ
Mullins
C Buddie
CB
D017097:Electric Impedance; D004563:Electrochemistry; D005290:Ferric Compounds / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D010084:Oxidation-Reduction; D055668:Photochemical Processes; D013696:Temperature; D014867:Water / Q000737:chemistry*; D014961:X-Ray Diffraction
D005290:Ferric Compounds; D014867:Water; C000499:ferric oxide