Reinforced thermoplastic polyimide with dispersed functionalized single wall carbon nanotubes.
Molecular pi-complexes were formed from pristine HiPCO single- wall carbon nanotubes (SWCNTs) and 1-pyrene- N-(4-N'-(5-norbornene-2,3-dicarboxyimido)phenyl butanamide, 1. Polyimide films were prepared with these complexes as well as uncomplexed SWCNTs and the effects of nanoadditive addition on mechanical, thermal, and electrical properties of these films were evaluated. Although these properties were enhanced by both nanoadditives, larger increases in tensile strength and thermal and electrical conductivities were obtained when the SWCNT/1 complexes were used. At a loading level of 5.5 wt %, the T(g) of the polyimide increased from 169 to 197 degrees C and the storage modulus increased 20-fold (from 142 to 3045 MPa). The addition of 3.5 wt % SWCNT/1 complexes increased the tensile strength of the polyimide from 61.4 to 129 MPa; higher loading levels led to embrittlement and lower tensile strengths. The electrical conductivities (DC surface) of the polyimides increased to 1 x 10(-4) Scm(-1) (SWCNT/1 complexes loading level of 9 wt %). Details of the preparation of these complexes and their effects on polyimide film properties are discussed.
Lebrón-Colón
Marisabel
M
NASA Glenn Research Center, 21000 Brookpark Road, Cleveland, Ohio 44135, USA. Marisabel.lebron-colon-1@nasa.gov
Meador
Michael A
MA
Gaier
James R
JR
Solá
Francisco
F
Scheiman
Daniel A
DA
McCorkle
Linda S
LS