Microdomain orientation dependence on thickness in thin films of cylinder-forming PS-b-PMMA.
The self-assembly of block-copolymer thin films in periodic nanostructures has received considerable attention during the last decade due to their potential applications in nanofabrication and nanolithography. We followed the morphologies developed in thin films of a cylinder-forming diblock copolymer polystyrene-b-poly(methylmethacrylate) ((PS-b-PMMA), PS 46.1 kg mol( - 1), PMMA 21.0 kg mol( - 1), lattice spacing L(0) = 36 nm), as a function of the film thickness (t), analyzing the effect of thickness commensurability on domain orientation in respect to the substrate. The study was circumscribed to the unexplored range of thickness below L(0). Two thickness windows with perpendicular orientation of the PMMA domains were identified: a well-known window at t approximately L(0) and a new window at t approximately L(0)/2. A half-parallel cylinder morphology was observed for [Formula: see text] with a progressive change in morphology [Formula: see text] when thickness increases from L(0)/2 to L(0). This experimental evidence provides new insights on the mechanism of block copolymers self-organization and indicates the possibility to tune the thickness of the nanostructured polymeric film below L(0), allowing the fabrication of ultrathin soft masks for advanced lithographic processes.
Zucchi
I A
IA
Laboratorio MDM, INFM-CNR Via Olivetti 2, 20041 Agrate Brianza, Italy. ileanazu@yahoo.com.ar
Poliani
E
E
Perego
M
M