Tailoring the morphology of high molecular weight PLLA scaffolds through bioglass addition.
Thermally induced phase separation (TIPS) has proven to be a suitable method for the preparation of porous structures for tissue engineering applications, and particular attention has been paid to increasing the pore size without the use of possible toxic surfactants. Within this context, an alternative method to control the porosity of polymeric scaffolds via the combination with a bioglass is proposed in this work. The addition of a bioactive glass from the 3CaO x P2O5-MgO-SiO2 system enables the porous structure of high molecular weight poly(l-lactic) acid (PLLA) scaffolds prepared by TIPS to be tailored. Bioglass acts as a nucleating catalyst agent of the PLLA matrix, promoting its crystallization, and the glass solubility controls the pore size. A significant increase in the pore size is observed as the bioglass content increases and scaffolds with large pore size (approximately 150 microm) can be prepared. In addition, the bioactive character of the scaffolds is proved by in vitro tests in synthetic plasma. The importance of this approach resides on the combination of the ability to tailor the porosity of polymeric scaffolds via the tunable solubility of bioglasses, without the use of toxic surfactants, leading to a composite structure with suitable properties for bone tissue engineering applications.
Barroca
N
N
Department of Ceramics and Glass Engineering and Centre for Research in Ceramics and Composite Materials, CICECO, University of Aveiro, 3810-193 Aveiro, Portugal.
Daniel-da-Silva
A L
AL
Vilarinho
P M
PM
Fernandes
M H V
MH
D001672:Biocompatible Materials / Q000737:chemistry; D002152:Calorimetry, Differential Scanning; D002516:Ceramics / Q000737:chemistry*; D019245:Compressive Strength; D003460:Crystallization; D055119:Elastic Modulus; D007477:Ions / Q000032:analysis; D019344:Lactic Acid / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D008970:Molecular Weight; D010316:Particle Size; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D016062:Porosity; D012542:Scattering, Radiation; D017550:Spectroscopy, Fourier Transform Infrared; D013696:Temperature; D013997:Time Factors; D054457:Tissue Scaffolds / Q000737:chemistry*
D001672:Biocompatible Materials; C022107:Bioglass; D007477:Ions; D011091:Polyesters; D011108:Polymers; D019344:Lactic Acid; C033616:poly(lactide)