title: Valence-change of Eu and its effects on the luminescent properties of Sr2MgSi2O7:Eu,Dy.
abstract: Long afterglow phosphors of Sr2MgSi2O7:Eu,Dy were prepared by high temperature solid state reaction in oxidation atmospheres, and then were treated sequentially in reducing atmosphere --> oxidation atmosphere --> reducing atmosphere. The crystal structure of the samples was investigated by using powder X-ray diffraction (XRD). The measurements of the photoluminescence and the thermoluminescence properties suggest the difference in the luminescent properties between Eu2+ and Eu3+. Eu3+ ions occupy two different sites, and their emission spectra consist of four discrete line spectra, due to the 5D0 --> 7F1 (590 nm), 5D0 --> 7F2 (618 nm), 5D0 --> 7F4 (703 nm) and the 5D2 --> 7F3 (510 nm) transitions. But in contrast, the emission spectrum of Eu2+ is characteristic of a broadband spectrum due to the 4f(7) --> 4f(6) 5d(1) transition. The luminescence of Sr2MgSi2O7:Eu2+,Dy3+ displays both higher intensity and longer decay than that of Sr2MgSi2O7:Eu3+,Dy3+. The emissions from Dy3+ are detected in all samples, indicating that Dy3+ ions act not only the trap center but also the luminescence center in the host lattice of Sr2MgSi2O7.
authors.affiliation: School of Physics and Optoelectronic Engineering, Guangdong University of Technology, Guangzhou, 510006, China.
authors.forename: Xuehua
authors.initials: X
authors.lastname: Chen
authors.forename: Yihua
authors.initials: Y
authors.lastname: Hu
authors.forename: Yinhai
authors.initials: Y
authors.lastname: Wang