Control of mode of crystal networking during monolayer assembly of microcrystals on water.
A series of hydrocarbon (HC)-coated cubic zeolite microcrystals (1.7 microm) was prepared. The HCs were n-octyl, n-dodecyl, methyl n-undecanoate, n-octadecyl, and n-heptadecafluorodecyl. The measured water contact angles (theta) of the corresponding HC-coated glass plates were 64, 77, 82, 102, and 105 degrees, respectively, indicating that the hydrophobicity of the surface-tethered hydrophobic chain (HC) increased in the above order. The HC-coated zeolite microcrystals readily formed closely packed monolayers at the air-water interface through interdigitation of surface-tethered HCs, and on glass plates after transferring onto glass plates by dip coating. Interestingly, while the mode of networking was face-to-face (FTF) contacting with n-octyl or n-dodecyl (theta < or =77 degrees) as HC, it changed to edge-to-edge (ETE) contacting mode with n-octadecyl or n-heptadecafluorodecyl (theta > or = 102 degrees) as HC. With methyl n-undecanoate (theta = 82 degrees) as HC, both modes appeared in the monolayers, with about equal populations. The resulting monolayers of cubic zeolite microcrystals with their three-fold axes oriented perpendicular to substrates would be useful for application of the zeolite monolayers for advanced materials.
Park
Jin Seon
JS
Center for Microcrystal Assembly, Center for Nanoporous Materials, Department of Chemistry, and Program of Integrated Biotechnology, Sogang University, Seoul 121-742, Korea.
Jeong
Nak Cheon
NC
Lee
Yun-Jo
YJ
Kim
Min Jung
MJ
Yoon
Kyung Byung
KB