Surface characteristics of orthodontic adhesives and effects on streptococcal adhesion.
BACKGROUND
In this study, we analyzed the surface roughness (SR) and surface free energy (SFE) characteristics of various orthodontic adhesives and their effects on the adhesion of mutans streptococci (MS).


METHODS
Three nonfluoride-releasing composites, 1 fluoride-releasing composite, 1 polyacid-modified composite (compomer), and 2 resin-modified glass ionomers (RMGIs) were analyzed with confocal laser scanning microscopy and the sessile drop method. Each material was incubated with whole saliva or phosphate-buffered saline solution. Adhesion assays were then performed by incubating each material with tritium-labeled cariogenic streptococci.


RESULTS
We found that SFE and its components were significantly different among the adhesives, despite relatively uniform SR. RMGIs showed significantly higher SFE-particularly, dispersive, polar, and acidic characteristics-than did the composites. The compomer had intermediate characteristics between the composites and RMGIs. MS adhered to RMGIs significantly more than to the composites and the compomer, but there was no significant difference among the composites. The longer incubation time increased MS adhesion, whereas saliva coating did not significantly influence MS adhesion. There was a correlation between SFE and MS adhesion. SFE and its dispersive, polar, and acid components significantly influenced MS adhesion irrespective of saliva coating.


CONCLUSIONS
This study suggests that initial MS adhesion is significantly influenced by SFE characteristics of adhesives rather than SR or saliva coating.
Ahn
Sug-Joon
SJ
Department of Orthodontics, Dental Research Institute, School of Dentistry, Seoul National University, 28-22 Yungeon-Dong, Jongro-Gu, Seoul, Korea.
Lim
Bum-Soon
BS
Lee
Shin-Jae
SJ
D000180:Acrylic Resins / Q000737:chemistry; D000538:Aluminum Silicates / Q000737:chemistry; D001422:Bacterial Adhesion / Q000502:physiology*; D002021:Buffers; D002327:Cariostatic Agents / Q000737:chemistry; D020770:Compomers / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry; D003738:Dental Cements / Q000737:chemistry*; D005459:Fluorides / Q000737:chemistry; D005899:Glass Ionomer Cements / Q000737:chemistry; D006801:Humans; D008422:Materials Testing; D018613:Microscopy, Confocal; D009967:Orthodontic Appliances; D010710:Phosphates / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D012463:Saliva / Q000737:chemistry; D012965:Sodium Chloride / Q000737:chemistry; D013291:Streptococcus / Q000502:physiology*; D013295:Streptococcus mutans / Q000502:physiology; D016986:Streptococcus sobrinus / Q000502:physiology; D013499:Surface Properties; D014783:Viscosity
D000180:Acrylic Resins; D000538:Aluminum Silicates; D002021:Buffers; D002327:Cariostatic Agents; D020770:Compomers; D003188:Composite Resins; D003738:Dental Cements; C418867:Enlight; C095451:Fuji Ortho LC; D005899:Glass Ionomer Cements; C516145:Multicure cement; D010710:Phosphates; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C477790:Transbond XT; D012965:Sodium Chloride; D005459:Fluorides