Controllable fabrication of nanocrystal-loaded photonic crystals with a polymerizable macromonomer via the CCTP technique.
We report an alternative strategy for fabricating nanocrystal-loaded photonic crystals with a polymerizable macromonomer via catalytic chain-transfer polymerization (CCTP) in which CoBF acted as a chain-transfer agent (CTAs). First, monodisperse, functionalized PS-co-PMAA microspheres with polystyrene (PS) cores and poly(methacrylic acid) (PMAA) shells were controllably prepared using styrene and the as-prepared PMAA macromonomer by surfactant-free emulsion polymerization. Then Cd(0.4)Zn(0.6)S nanocrystals capped with as-prepared PMAA macromonomer were synthesized by an in situ growth method. Finally, Cd(0.4)Zn(0.6)S nanocrystal-loaded PS-co-PMAA microspheres hybrids were obtained through simply mixing an aqueous solution of PS-co-PMAA microspheres with an aqueous solution of Cd(0.4)Zn(0.6)S nanocrystals in the appropriate proportions; the multianchor -COOH groups on the surface of core-shell PS-co-PMAA microspheres favor incorporation with Cd(0.4)Zn(0.6)S nanocrystals. Scanning electron microscopy (SEM) images confirm that PS-co-PMAA microspheres are uniformly surrounded by Cd(0.4)Zn(0.6)S nanocrystals. In addition, discrete electronic and photonic states can be combined both with PS-co-PMAA photonic crystals and fluorescent semiconductor Cd(0.4)Zn(0.6)S nanocrystals.
Yan
Lili
L
State Key Laboratory of Material-Oriented Chemical Engineering, College of Chemistry and Chemical Engineering, Nanjing University of Technology, Nanjing 210009, PR China.
Yu
Ziyi
Z
Chen
Li
L
Wang
Caifeng
C
Chen
Su
S