title: CO as an IR probe molecule for characterization of copper ions in a basolite C300 MOF sample.
abstract: The state of the accessible copper ions in a Cu-basolite C300 sample (copper benzene-1,3,5-tricarboxylate) was studied by CO as an IR probe molecule. Low temperature CO adsorption on a sample activated at 473 K results in a series of carbonyl bands. Three intense sharp bands at 2141, 2128 and 2123 cm(-1) are very sensitive to the CO equilibrium pressure and are associated with CO polarized by the aromatic ring. Three bands, at ca. 2192, 2178 and 2148 cm(-1) are assigned to three different kinds of monocarbonyl species. At high CO coverage, the principal carbonyls (2178 cm(-1)) are converted into polycarbonyls. A band at 2125 cm(-1) (resistant to evacuation) is associated with Cu(+) ions on small CuO particles. Experiments on (12)CO-(13)CO adsorption revealed lack of vibrational coupling and also showed that the bands at 2192 and 2148 cm(-1), although changing almost in concert, were due to individual species. Sample activated at 373 K does not contain copper oxide, which indicates that activation at higher temperatures, 473 K, leads to some irreversible changes.
authors.affiliation: Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev str., bl. 11, Sofia 1113, Bulgaria.
authors.forename: Nikola
authors.initials: N
authors.lastname: Drenchev
authors.forename: Elena
authors.initials: E
authors.lastname: Ivanova
authors.forename: Mihail
authors.initials: M
authors.lastname: Mihaylov
authors.forename: Konstantin
authors.initials: K
authors.lastname: Hadjiivanov