Oscillatory behaviour in galvanostatic formaldehyde oxidation on nanostructured Pt/glassy carbon model electrodes.
The electrocatalytic oxidation of formaldehyde, which results in CO(2) and HCOOH formation, was investigated under galvanostatic conditions on nanostructured Pt/glassy carbon (GC) electrodes fabricated by employing colloidal lithography (CL). The measurements were performed on structurally well-defined model electrodes of different Pt surface coverages under different applied currents (current densities) and at constant electrolyte transport in a thin-layer flow cell connected to a differential electrochemical mass spectrometry (DEMS) setup to monitor the dynamic response of the reaction selectivity under these conditions. Periodic oscillations of the electrode potential and the CO(2) formation rate appear not only for a continuous Pt film, but also for the nanostructured Pt/GC electrodes when a critical current density is exceeded. The critical current density for achieving regular oscillation patterns increased with decreasing Pt nanodisk density. Lower oscillation frequencies of the electrode potential and lower CO(2) formation rate for nanostructured Pt/GC electrodes compared to continuous Pt film at similar applied current densities suggest that transport processes play an essential role. Moreover, from the simple periodic response of the nanostructured electrodes it follows that all individual Pt disks in the array oscillate in synchrony. This result is discussed in terms of the different modes of spatial coupling present in the system: global coupling, migration coupling and mass transport of the essential chemical species, and the coverage of corresponding adsorbates.
Seidel
Yvonne E
YE
Institute of Surface Chemistry and Catalysis, Ulm University, 89081 Ulm, Germany. yvonne.seidel@uni-ulm.de
Jusys
Zenonas
Z
Lindström
Rakel W
RW
Stenfeldt
Marie
M
Kasemo
Bengt
B
Krischer
Katharina
K
D002244:Carbon / Q000737:chemistry*; D002245:Carbon Dioxide / Q000138:chemical synthesis / Q000737:chemistry; D004058:Diffusion; D004566:Electrodes; D005557:Formaldehyde / Q000737:chemistry*; D005561:Formates / Q000138:chemical synthesis / Q000737:chemistry; D005898:Glass / Q000737:chemistry; D008956:Models, Chemical; D049329:Nanostructures / Q000737:chemistry*; D010084:Oxidation-Reduction; D010984:Platinum / Q000737:chemistry*; D011199:Potentiometry; D013499:Surface Properties
D005561:Formates; D002245:Carbon Dioxide; D005557:Formaldehyde; D010984:Platinum; D002244:Carbon