SiO2 nanodot arrays using functionalized block copolymer templates and selective silylation.
Silicon oxide nanodot arrays were fabricated using functionalized block copolymer templates and selective silylation. A polystyrene-b-poly(acrylic acid/acrylic anhydride) (PS-b-PAA/AN) thin film containing spherical nanodomains was used as a template to build nanoscopic silica structures. A PS-b-PAA/AN thin film was prepared by acid-catalyzed thermal deprotection of polystyrene-b-poly(tert-butyl acrylate) on an SU-8 resist film containing a photoacid generator. This resulting film has excellent solvent and thermal resistance due to crosslinked anhydride linkages in carboxyl-functionalized PAA/AN block domains. Silicon was introduced by spin-spraying of hexamethyldisilazane (HMDS) over the entire surface of a self-assembled PS-b-PAA/AN thin film. HMDS was selectively reacted with carboxylic acid groups in spherical domains of a PAA/AN block. SiO(2) nanodot arrays were generated by oxygen reactive ion etching.
Kim
Su Min
SM
Department of Chemistry, Korea Advanced Institute of Science and Technology (KAIST), Yuseong-Gu, Daejeon, Republic of Korea.
Ku
Se Jin
SJ
Kim
Jin-Baek
JB