Methanol oxidation enhanced by the presence of O(2) at novel Pt-C co-sputtered electrode.
In this paper, we describe a novel electrode that exhibits sensitized methanol electrooxidation in an oxygen atmosphere. A binary Pt-C electrode has been developed for use as the anode catalyst of a direct methanol fuel cell using a co-sputtering technique. Characterizations of the electrodes revealed that the sputtered Pt-C forms nanosize and phase-separated Pt and C domains, in which the Pt particle size decreases and its crystallinity gradually becomes amorphous with increasing C content. The current density of methanol oxidation in deaerated conditions exhibited a maximum value at a C content of 23 at%. The result can be well explained from the viewpoints of the morphology and binding energy of Pt. The methanol oxidation current is sensitized by O(2) when the Pt-C electrode contains >23 at% C, and the extent of sensitization increases monotonically with C content. This phenomenon is not observed at a Pt electrode. The sensitization mechanism was investigated by considering the reduction reaction of O(2); it was clarified that the amount of adsorbed species created by O(2) reduction increases with increasing C content. It was deduced that the Pt-OH produced by O(2) reduction participates in oxidation of Pt-CO, which is believed to be the rate-determining step of the methanol electrooxidation.
Umeda
Minoru
M
Department of Materials Science and Technology, Faculty of Engineering, Nagaoka University of Technology, Kamitomioka 1603-1, Nagaoka, Niigata 940-2188, Japan. mumeda@vos.nagaokaut.ac.jp
Nagai
Kazuhiro
K
Shibamine
Masahiko
M
Inoue
Mitsuhiro
M