Photoassisted reduction of metal ions and organic dye by titanium dioxide nanoparticles in aqueous solution under anoxic conditions.
The photoassisted reduction of metal ions and organic dye by metal-deposited Degussa P25 TiO(2) nanoparticles was investigated. Copper and silver ions were selected as the target metal ions to modify the surface properties of TiO(2) and to enhance the photocatalytic activity of TiO(2) towards methylene blue (MB) degradation. X-ray powder diffraction (XRPD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM) were used to characterize the crystallinity, chemical species and morphology of metal-deposited TiO(2), respectively. Results showed that the particle size of metal-deposited TiO(2) was larger than that of Degussa P25 TiO(2). Based on XRPD patterns and XPS spectra, it was observed that the addition of formate promoted the photoreduction of metal ion by lowering its oxidation number, and subsequently enhancing the photodegradation efficiency and rate of MB. The pseudo-first-order rate constant (k(obs)) for MB photodegradation by Degussa P25 TiO(2) was 3.94 x 10(-2) min(-1) and increased by 1.4-1.7 times in k(obs) with metal-deposited TiO(2) for MB photodegradation compared to simple Degussa P25 TiO(2). The increase in mass loading of metal ions significantly enhanced the photodegradation efficiency of MB; the k(obs) for MB degradation increased from 3.94 x 10(-2) min(-1) in the absence of metal ion to 4.64-7.28 x 10(-2) min(-1) for Ag/TiO(2) and to 5.14-7.61 x 10(-2) min(-1) for Cu/TiO(2). In addition, the electrons generated from TiO(2) can effectively reduce metal ions and MB simultaneously under anoxic conditions. However, metal ions and organic dye would compete for electrons from the illuminated TiO(2).
Doong
Ruey-An
RA
Department of Biomedical Engineering and Environmental Sciences, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu, 30013, Taiwan. radoong@mx.nthu.edu.tw
Hsieh
Tien-Chin
TC
Huang
Chin-Pao
CP
D002384:Catalysis; D004396:Coloring Agents / Q000737:chemistry*; D053768:Metal Nanoparticles; D008670:Metals / Q000737:chemistry*; D046529:Microscopy, Electron, Transmission; D010084:Oxidation-Reduction; D010777:Photochemistry; D012996:Solutions; D014025:Titanium / Q000737:chemistry*; D014867:Water; D014961:X-Ray Diffraction
D004396:Coloring Agents; D008670:Metals; D012996:Solutions; D014867:Water; C009495:titanium dioxide; D014025:Titanium