Strain measurement of pure titanium covered with soft tissue using X-ray diffraction.
Measurement of the stress and strain applied to implants and bone tissue in the human body are important for fracture prediction and evaluations of implant adaptation. The strain of titanium (Ti) materials can be measuring by X-ray diffraction techniques. This study applied X-ray diffraction to the skin tissue-covered Ti. Characteristic X-rays of Mo Kalpha were used and the X-rays diffracted from the Ti were detected through the covering skin tissue. The X-ray absorption by skin tissue is large under the diffracted X-rays detected in low angles because the length of penetration depends on the angle of inclination, equal to the Bragg angle. The effects of skin tissue to detect the diffracted X-rays were investigated in the experiments. And the strain measurements were conducted under bending loads applied to the Ti specimen. The effect of skin tissue was absorption of X-rays as well as the X-rays scattered from the physiological saline contained in the tissue. The X-rays scattered by the physiological saline creates a specific background pattern near the peaks from the (002) and (011) lattice planes of Ti in the X-ray diffraction profile. Diffracted X-rays from the Ti were detected after being transmitted through 1 mm thick skin tissue by Mo Kalpha. Individual peaks such as (010), (002), (011), and (110) were clearly established by using a parallel beam arrangement. The strains of (110) lattice planes were measured with or without the tissue cover were very similar. The strain of the (110) lattice planes of Ti could be measured by Mo Kalpha when the Ti specimen was located under the skin tissue.
Fujisaki
Kazuhiro
K
Division of Human Mechanical Systems and Design, Graduate School of Engineering, Hokkaido University, N-13, W-8, Kita-ku, Sapporo 060-8628, Japan. fujiwax@eng.hokudai.ac.jp
Tadano
Shigeru
S
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry*; D003238:Connective Tissue / Q000502:physiology* / Q000601:surgery; D055119:Elastic Modulus; D019544:Equipment Failure Analysis; D008422:Materials Testing; D019736:Prostheses and Implants; D011817:Rabbits; D013314:Stress, Mechanical; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction / Q000379:methods
D001672:Biocompatible Materials; D014025:Titanium