Transformation-mediated ductility in CuZr-based bulk metallic glasses.
Bulk metallic glasses (BMGs) generally fail in a brittle manner under uniaxial, quasistatic loading at room temperature. The lack of plastic strain is a consequence of shear softening, a phenomenon that originates from shear-induced dilation that causes plastic strain to be highly localized in shear bands. So far, significant tensile ductility has been reported only for microscopic samples of around 100 nm (ref. 4) as well as for high strain rates, and so far no mechanisms are known, which could lead to work hardening and ductility in quasistatic tension in macroscopic BMG samples. In the present work we developed CuZr-based BMGs, which polymorphically precipitate nanocrystals during tensile deformation and subsequently these nanocrystals undergo twinning. The formation of such structural heterogeneities hampers shear band generation and results in macroscopically detectable plastic strain and work hardening. The precipitation of nanocrystals and their subsequent twinning can be understood in terms of a deformation-induced softening of the instantaneous shear modulus. This unique deformation mechanism is believed to be not just limited to CuZr-based BMGs but also to promote ductility in other BMGs.
Pauly
S
S
Gorantla
S
S
Wang
G
G
Kühn
U
U
Eckert
J
J
Phys Rev Lett. 2006 Nov 10;97(19):195501
17155640
Science. 1995 Mar 31;267(5206):1935-9
17770102
Science. 2003 May 23;300(5623):1275-7
12714676
Nat Mater. 2007 Oct;6(10):735-9
17704779
Phys Rev Lett. 1993 Feb 22;70(8):1120-1123
10054291
Science. 2009 Jan 30;323(5914):607-10
19179523
Phys Rev Lett. 2005 Nov 4;95(19):195501
16383993
Phys Rev Lett. 2005 Dec 9;95(24):245501
16384392
Science. 2002 Jan 25;295(5555):654-7
11809965
Phys Rev Lett. 2006 Jun 23;96(24):245502
16907252
Science. 2007 Dec 21;318(5858):1895-9
18096800