Solution synthesis and characterization of indium-zinc formate precursors for transparent conducting oxides.
A series of In-Zn formate mixtures were investigated as potential precursors to amorphous In-Zn-oxide (IZO) for transparent conducting oxide (TCO) applications. These mixtures were prepared by neutralization from formic acid and characterized by elemental analysis, IR spectroscopy, powder X-ray diffraction, and thermogravimetry-differential scanning calorimetry (TG-DSC) measurements. Thermal analysis revealed that a mixture of In and Zn formates reduced the overall decomposition temperature compared to the individual constituents and that OH-substitution enhanced the effect. In terms of precursor feasibility, it was demonstrated that the decomposition products of In-Zn formate could be directed toward oxidation or reduction by controlling the decomposition atmosphere or with solution acid additives. For TCO applications, amorphous IZO films were prepared by ultrasonic spray deposition from In-Zn formate solutions with annealing at 300-400 degrees C.
Pasquarelli
Robert M
RM
Colorado School of Mines, Metallurgical and Materials Engineering, 1500 Illinois Street, Golden, Colorado 80401, USA. robert.pasquarelli@nrel.gov
Curtis
Calvin J
CJ
Miedaner
Alexander
A
van Hest
Maikel F A M
MF
O'Hayre
Ryan P
RP
Ginley
David S
DS
D004553:Electric Conductivity; D005561:Formates / Q000737:chemistry*; D007204:Indium / Q000737:chemistry*; D009942:Organometallic Compounds / Q000138:chemical synthesis* / Q000737:chemistry*; D010087:Oxides / Q000737:chemistry*; D012996:Solutions; D015032:Zinc / Q000737:chemistry*
D005561:Formates; D009942:Organometallic Compounds; D010087:Oxides; D012996:Solutions; D007204:Indium; C030544:formic acid; D015032:Zinc