Effect of hot-water extraction on alkaline pulping of bagasse.
The effect of hot-water extraction on alkaline pulping was investigated. The properties of black liquor and pulp strength of bagasse were analyzed. The extraction was conducted at 160 degrees C for 30min where 13.2% of the mass was dissolved in the extraction liquor. Untreated bagasse and extracted bagasse were digested by soda and soda-AQ processes at 17% and 15.5% (with 0.1% AQ) alkali charge (NaOH). Cooking temperatures were 160 degrees C and 155 degrees C respectively. The pulp from extracted bagasse had a lower Kappa number and a higher viscosity compared to the pulp from the untreated bagasse. The black liquor from pulping extracted bagasse had a lower solid content, a lower viscosity and a lower silica content, but a higher heating value than that from pulping of untreated bagasse. Hot-water extraction resulted in a significant decrease in bleaching chemical consumption and the formation of chlorinated organics. Pulp strength properties such as the tensile index and the burst index were found to be lower, but the tear index, bulk, opacity and pulp freeness were found to be higher when hot-water extraction was applied.
Lei
Yichao
Y
State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China.
Liu
Shijie
S
Li
Jiang
J
Sun
Runcang
R
D000468:Alkalies / Q000737:chemistry*; D001709:Biotechnology / Q000379:methods*; D002482:Cellulose / Q000737:chemistry* / Q000378:metabolism; D006358:Hot Temperature; D006863:Hydrogen-Ion Concentration; D010209:Paper; D012972:Sodium Hydroxide / Q000737:chemistry*; D014867:Water
D000468:Alkalies; D014867:Water; D012972:Sodium Hydroxide; D002482:Cellulose; C027433:bagasse