Temperature-dependent phonon conduction and nanotube engagement in metalized single wall carbon nanotube films.
Interfaces dominate the thermal resistances in aligned carbon nanotube arrays. This work uses nanosecond thermoreflectance thermometry to separate interface and volume resistances for 10 microm thick aligned SWNT films coated with Al, Ti, Pd, Pt, and Ni. We interpret the data by defining the nanotube-metal engagement factor, which governs the interface resistance and is extracted using the measured film heat capacity. The metal-SWNT and SWNT-substrate resistances range between 3.8 and 9.2 mm(2)K/W and 33-46 mm(2)K/W, respectively. The temperature dependency of the heat capacity data, measured between 125 and 300 K, is in good agreement with theoretical predictions. The temperature dependence demonstrated by the metal-SWNT interface resistance data suggests inelastic phonon transmission.
Panzer
Matthew A
MA
Department of Mechanical Engineering, Stanford University, Stanford, California 94305, USA.
Duong
Hai M
HM
Okawa
Jun
J
Shiomi
Junichiro
J
Wardle
Brian L
BL
Maruyama
Shigeo
S
Goodson
Kenneth E
KE