Effect of Er:YAG laser irradiations on shear bond strength of three self-adhesive resin cements to dentin.
OBJECTIVE
The purpose of this study was to evaluate the influence of Er:YAG laser irradiation on shear-bond strength of self-adhesive resin cements to dentin.


BACKGROUND
Different laser-irradiation settings are used for dentin-surface pretreatment, which may affect the bond strength of resins.


METHODS
Fourty-five extracted third molars were selected, sectioned in a mesiodistal direction, and 90 tooth slabs were obtained. The teeth were ground to expose the dentinal hard tissue with 320- and 600-grit silicon carbide disks. The specimens were randomly assigned to nine groups (n = 10). Surfaces for each group were laser irradiated with 30 Hz/70 mJ (2.1 W), 30 Hz/160 mJ (4.8 W), or non-irradiated (control) for each resin cement (SmartCem2, RelyX Unicem, Multilink Automix). All specimens were stored in distilled water at 37°C for 24 h after luting. Shear-bond testing was carried out by using a Universal testing machine with a crosshead speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and post hoc Tukey HSD tests (p < 0.05).


RESULTS
The highest bond-strength value was obtained with SmartCem2, which was irradiated with Er:YAG laser (30 Hz/160 mJ). The lowest values were exhibited in the control group of SmartCem2, RelyX Unicem and Multilink Automix, respectively (4.92 ± 1.68, 7.17 ± 2.88, and 7.93 ± 3.05).


CONCLUSIONS
The 2.1-W and 4.8-W laser ablation did not show any statistically difference for RelyX Unicem and Multilink Automix materials. However, in the SmartCem2 group, laser irradiated with 30 Hz/160 mJ application increased the bond-strength values, and the highest bond-strength results were obtained in this group.
Capa
Nuray
N
Department of Prosthodontics, Faculty of Dentistry, Yeditepe University, Istanbul, Turkey.
Aykor
Arzu
A
Ozel
Emre
E
Calikkocaoglu
Senih
S
Soyman
Mubin
M
D001840:Dental Bonding; D003799:Dental Stress Analysis; D003804:Dentin / Q000528:radiation effects*; D006801:Humans; D053844:Lasers, Solid-State; D008422:Materials Testing; D019279:Resin Cements / Q000737:chemistry*
D019279:Resin Cements