In vivo restoration of full-thickness cartilage defects by poly(lactide-co-glycolide) sponges filled with fibrin gel, bone marrow mesenchymal stem cells and DNA complexes.
A composite construct comprising of bone marrow mesenchymal stem cells (BMSCs), plasmid DNA encoding transforming growth factor-beta1 (pDNA-TGF-beta1), fibrin gel and poly (lactide-co-glycolide) (PLGA) sponge was designed and employed to repair articular cartilage defects. To improve the gene transfection efficiency, a cationized chitosan derivative N,N,N-trimethyl chitosan chloride (TMC) was employed as the vector. The TMC/DNA complexes had a transfection efficiency of 9% to BMSCs and showed heterogeneous TGF-beta1 expression in a 10-day culture period in vitro. In vivo culture of the composite constructs was performed by implantation into full-thickness cartilage defects of New Zealand white rabbit joints, using the constructs absence of pDNA-TGF-beta1 or BMSCs as controls. Heterogeneous expression of TGF-beta1 in vivo was detected at 4 weeks, but its level was decreased in comparison with that of 2 weeks. After implantation for 12 weeks, the cartilage defects were successfully repaired by the composite constructs of the experimental group, and the neo-cartilage integrated well with its surrounding tissue and subchondral bone. Immunohistochemical and glycosaminoglycans (GAGs) staining confirmed the similar amount and distribution of collagen type II and GAGs in the regenerated cartilage as that of hyaline cartilage. The cartilage special genes expressed in the neo-tissue were closer to those of the normal cartilage. An overall score of 2.83 was obtained according to Wakitani's standard. By contrast, only part of the defects was repaired by the pDNA-TGF-beta1 absence constructs, and no cartilage repair but fibrous tissue was found for the BMSCs absence constructs. Therefore, combination of the PLGA sponge/fibrin gel scaffold with BMSCs and gene therapy is an effective method to restore cartilage defects and may have a great potential for practical applications in the near future.
Wang
Wei
W
MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, China.
Li
Bo
B
Li
Yanglin
Y
Jiang
Yangzi
Y
Ouyang
Hongwei
H
Gao
Changyou
C
D000818:Animals; D001483:Base Sequence; D015153:Blotting, Western; D001854:Bone Marrow Cells / Q000166:cytology*; D002356:Cartilage / Q000473:pathology*; D004247:DNA / Q000008:administration & dosage*; D017931:DNA Primers; D005337:Fibrin / Q000008:administration & dosage*; D019344:Lactic Acid / Q000737:chemistry*; D059630:Mesenchymal Stem Cells / Q000166:cytology*; D011100:Polyglycolic Acid / Q000737:chemistry*; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011817:Rabbits; D020133:Reverse Transcriptase Polymerase Chain Reaction
D017931:DNA Primers; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid; D005337:Fibrin; D004247:DNA