Shearforce-based constant-distance scanning electrochemical microscopy as fabrication tool for needle-type carbon-fiber nanoelectrodes.
Carbon fiber nanoelectrodes with nanometer radii tip curvatures were fabricated using a shearforce-based constant-distance scanning electrochemical microscope and electrochemically induced polymer deposition. A simple DC etching procedure in alkaline solution provided conically sharpened single carbon fibers with well-formed nanocones at their bottom. Coating the stems but not the end of the tips of the tapered structures with anodic electrodeposition paint was the strategy for limiting the bare carbon to the foremost end and restricting a feasible voltammetry current response to exactly this section. The electrodeposition of the polymer was prevented at the foremost end of the tip using a shearforce-based tip-to-sample distance control that allowed approaching the etched tips carefully in just touching distance to a film of a silicone elastomer. Analysis of the steady-state cyclic voltammograms in presence of a reversible redox compound revealed effective radii for the obtained needle-type carbon-fiber nanoelectrodes down to as small as 46 nm. The method offers an alternative pathway toward the fabrication of highly miniaturized carbon electrodes.
Analytische Chemie - Elektroanalytik & Sensorik, Ruhr-University Bochum, D-44780 Bochum, Germany.
Emad Mohamed
EM
Hussien
Wolfgang
W
Schuhmann
Albert
A
Schulte
D002244:Carbon / Q000737:chemistry*; D000077482:Carbon Fiber; D055664:Electrochemical Techniques / Q000295:instrumentation* / Q000379:methods; D006863:Hydrogen-Ion Concentration; D008839:Microelectrodes; D008855:Microscopy, Electron, Scanning; D008904:Miniaturization; D049329:Nanostructures / Q000737:chemistry*; D010084:Oxidation-Reduction
D000077482:Carbon Fiber; D002244:Carbon