Synthesis, characterization and photopolymerization of a new dimethacrylate monomer based on (alpha-methyl-benzylidene)bisphenol used as root canal sealer.
Methacrylate resin-based sealers have attracted wide attention because of their easy handling, superior aesthetic qualities, good mechanical properties and excellent adhesive ability with dentin. 2,2-Bis[4-(2'-hydroxy-3'-methacryloyloxypropoxy)-phenyl]-propane (Bis-GMA) is the main component of the newly developed commercial root canal sealer 'Epiphany', which is one of the methacrylate resin-based sealers. In order to further reduce the polymerization volume shrinkage of Bis-GMA, 4,4'-(alpha-methylbenzylidene)-bis(2'-hydroxy-3'-methacryloyloxy-propoxy)benzene (4,4'-AMBHMB) with higher molecular weight and larger molecular volume was synthesized to replace Bis-GMA as one of the components of the root canal sealer used in this study. The structure of monomer 4,4'-AMBHMB was confirmed by FT-IR, (1)H-NMR, mass spectrum and elemental analysis. The photopolymerization behavior of mixture of 4,4'-AMBHMB and triethylene glycol dimethacrylate (TEGDMA) was investigated by FT-IR. Degree of double bond conversion, volume shrinkage, water sorption and solubility, diffusion coefficient value, flexure strength and glass transition temperature of 4,4'-AMBHMB/TEGDMA system with a mass ratio of 50:50 were measured. A 50:50 Bis-GMA/TEGDMA formulation was used as reference. The results illustrated that 4,4'-AMBHMB/TEGDMA system had the same double bond conversion and water sorption with Bis-GMA/TEGDMA system. Polymerization shrinkage, water solubility and diffusion coefficient of 4,4'-AMBHMB/TEGDMA system were lower than that of the Bis-GMA/TEGDMA system, whereas the flexural strength and glass-transition temperature of 4,4'-AMBHMB/TEGDMA system were higher than that of the Bis-GMA/TEGDMA system.
He
Jingwei
J
College of Materials Science and Engineering, South China University of Technology, Guangzhou 510641, P. R. China.
Luo
Yuanfang
Y
Liu
Fang
F
Jia
Demin
D
D001597:Benzylidene Compounds / Q000737:chemistry*; D003188:Composite Resins / Q000737:chemistry*; D008970:Molecular Weight; D055668:Photochemical Processes; D011092:Polyethylene Glycols / Q000737:chemistry; D011108:Polymers / Q000138:chemical synthesis* / Q000737:chemistry*; D011109:Polymethacrylic Acids / Q000737:chemistry; D012117:Resins, Synthetic / Q000138:chemical synthesis / Q000737:chemistry; D012387:Root Canal Filling Materials / Q000138:chemical synthesis* / Q000737:chemistry*; D013057:Spectrum Analysis
C551882:4,4'-(alpha-methylbenzylidene)-bis(2'-hydroxy-3'-methacryloyloxypropoxy)benzene; D001597:Benzylidene Compounds; D003188:Composite Resins; D011108:Polymers; D011109:Polymethacrylic Acids; D012117:Resins, Synthetic; D012387:Root Canal Filling Materials; C020946:triethylene glycol dimethacrylate; D011092:Polyethylene Glycols