Ultrasmall monodisperse NaYF(4):Yb(3+)/Tm(3+) nanocrystals with enhanced near-infrared to near-infrared upconversion photoluminescence.
Photoluminescent NaYF(4):Yb(3+)/Tm(3+) nanocrystals are ideally suited for in vitro and in vivo photoluminescence (PL) bioimaging due to their virtue of near-infrared to near-infrared (NIR-to-NIR) upconversion (UC); they display PL with a peak at approximately 800 nm if excited at approximately 980 nm. Here, we report the synthesis of monodisperse NaYF(4):Yb(3+)/Tm(3+) nanocrystals of ultrasmall size (7-10 nm) with high UC efficiency. The intensity of their NIR UC emission was demonstrated to increase by up to 43 times along with an increase in the relative content of Yb(3+) ions from 20 to 100%, with a corresponding decrease in the Y(3+) content from 80 to 0%. The achieved ultrasmall NaYbF(4):2% Tm(3+) nanocrystals manifest NIR PL emission, which is 3.6 times more intense than that from 25-30 nm sized NaYF(4):20% Yb(3+)/2% Tm(3+) nanocrystals, previously synthesized and used for in vitro and in vivo bioimaging. An optimization of both size and UC PL efficiency of NIR-to-NIR nanocrystals provides us with highly efficient optical imaging probes for bioapplications.
Institute for Lasers, Photonics, and Biophotonics, The State University of New York at Buffalo, Buffalo, New York 14260, USA.
Guanying
G
Chen
Tymish Y
TY
Ohulchanskyy
Rajiv
R
Kumar
Hans
H
Agren
Prasas N
PN
Prasad
D003460:Crystallization / Q000379:methods*; D005459:Fluorides / Q000138:chemical synthesis*; D008163:Luminescent Measurements / Q000379:methods*; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D008968:Molecular Conformation; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure*; D036103:Nanotechnology / Q000379:methods*; D010316:Particle Size; D013055:Spectrophotometry, Infrared / Q000379:methods*; D013499:Surface Properties; D015019:Yttrium
D046911:Macromolecular Substances; C525362:sodium yttriumtetrafluoride; D015019:Yttrium; D005459:Fluorides