The recovery of zinc from hot galvanizing slag in an anion-exchange membrane electrolysis reactor.
This paper reports the optimization of the process parameters for recovery of zinc from hot galvanizing slag in an anion-exchange membrane electrolysis reactor. The experiments were carried out in an ammoniacal ammonium chloride system. The influence of composition of electrolytes, pH, stirring rate, current density and temperature, on cathodic current efficiency, specific power consumption and anodic dissolution of Zn were investigated. The results indicate that the cathode current efficiency increases and the hydrogen evolution decreased with increasing the cathode current density. The partial current for electrodeposition of Zn has liner relationship with omega(1/2) (omega: rotation rate). The highest current efficiency for dissolving zinc was obtained when NH(4)Cl concentration was 53.46 g L(-1) and the anodic dissolution of zinc was determined by mass transfer rate at stirring rate 0-300 r min(-1). Increase in temperature benefits to improve CE and dissolution of Zn, and reduce cell voltage. Initial pH of electrolytes plays an important role in the deposition and anodic dissolution of Zn. The results of single factor experiment show that about 50% energy consumption was saved for electrodeposition of Zn in the anion-exchange membrane electrolysis reactor.
Ren
Xiulian
X
College of Ocean, Harbin Institute of Technology at Weihai, Weihai, PR China.
Wei
Qifeng
Q
Hu
Surong
S
Wei
Sijie
S
D004572:Electrolysis / Q000191:economics / Q000295:instrumentation / Q000379:methods*; D006358:Hot Temperature; D006863:Hydrogen-Ion Concentration; D007474:Ion Exchange; D008567:Membranes, Artificial; D012995:Solubility; D015032:Zinc / Q000302:isolation & purification*
D008567:Membranes, Artificial; D015032:Zinc