Periodic nanotemplating by selective deposition of electroless gold island films on particle-lithographed dimethyldichlorosilane layers.
Uniform hexagonal arrays of diverse nanotemplated metal structures were formed via selective electroless gold plating on particle-lithographed dimethyldichlorosilane layers. Surface-associated water at silica bead interstices was shown to correlate with the formation of silane rings with outer ring diameters ranging from 522.5+/-29.7 to 1116.9+/-52.6 nm and/or spherical gold nanoparticles with diameters from 145.5+/-20.2 to 389.1+/-51.1 nm in the array. Reproducibility and millimeter-size scalability of the array were achieved without the need for expensive and sophisticated lithography or metal deposition equipment. The formation of each structure was explained on the basis of the silanization mechanism and microscopic characterization, as well as dimensional analysis of the nanostructures. This new, facile, and versatile method enables fine fabrication of regular metal nanoparticle array platforms to improve optical and plasmonic features in nanoelectronics and nanophotonic devices.
Ahn
Wonmi
W
Department of Materials Science and Engineering, 304 CME, University of Utah, Salt Lake City, Utah 84112, USA.
Roper
D Keith
DK
D006046:Gold / Q000737:chemistry*; D036103:Nanotechnology / Q000379:methods*; D011327:Printing / Q000379:methods*; D012821:Silanes / Q000737:chemistry*; D012822:Silicon Dioxide / Q000737:chemistry; D013499:Surface Properties
D012821:Silanes; D006046:Gold; D012822:Silicon Dioxide; C040863:dichlorodimethylsilane