Development of a biodegradable tissue adhesive based on functionalized 1,2-ethylene glycol bis(dilactic acid). I.
Tissue adhesives are a valuable alternative for mechanical tissue fixation by sutures or staples. Adhesives are desirable in body regions where damage and bleeding must be avoided. Tissue adhesives provide easy and fast handling. This study reports the development of a tissue adhesive based on 1,2-ethylene glycol bis(dilactic acid) (ELA) functionalized with hexamethylene diisocyanate (HDI) to produce isocyanate terminated ELA-NCO which was characterized by NMR and FTIR spectroscopy. ELA-NCO together with chain elongation agents forms an adhesive system suitable for tissue fixation. Several biodegradable polymers, such as hyaluronic acid, gelatin, chitosan acetate, and chitosan chloride were tested as chain elongation agents to obtain an adhesive system and studied on bovine muscle tissue to evaluate their adhesive strength and compared to fibrin glue. Tensile strength of glued joints was determined by a Zwick universal testing machine at ambient temperature. Mixtures of ELA-NCO and chitosan acetate or chloride, showed significantly higher adhesive strength than fibrin glue. Reaction between ELA-NCO and chitosan chloride produced polyurethane was traced by FTIR spectroscopy. NMR, FTIR, and rheological measurements demonstrated that ELA-NCO and chitosan chloride can be sterilized by gamma-rays or superheated water vapor without alterations, respectively. A mixture of ELA-NCO and chitosan chloride can be useful as medical tissue adhesive.
Sternberg
Katrin
K
Institute for Biomedical Engineering, University of Rostock, D-18119 Rostock, Germany.
Rohm
Henning W
HW
Institute for Biomedical Engineering, University of Rostock, D-18119 Rostock, Germany.
Lurtz
Claudia
C
Institute for Biomedical Engineering, University of Rostock, D-18119 Rostock, Germany.
Wegmann
Juergen
J
B.Braun Aesculap AG, D-78532 Tuttlingen, Germany.
Odermatt
Erich K
EK
B.Braun Aesculap AG, D-78532 Tuttlingen, Germany.
Behrend
Detlef
D
Institute for Biomedical Engineering, University of Rostock, D-18119 Rostock, Germany.
Michalik
Dirk
D
Leibniz Institute for Catalysis, University of Rostock, D-18059 Rostock, Germany.
Schmitz
Klaus-Peter
KP
Institute for Biomedical Engineering, University of Rostock, D-18119 Rostock, Germany.
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry / Q000592:standards; D002417:Cattle; D019855:Ethylene Glycol / Q000737:chemistry / Q000627:therapeutic use*; D019344:Lactic Acid / Q000737:chemistry; D008422:Materials Testing; D012212:Rheology; D013057:Spectrum Analysis; D014014:Tissue Adhesives / Q000737:chemistry*
D001672:Biocompatible Materials; D014014:Tissue Adhesives; D019344:Lactic Acid; D019855:Ethylene Glycol