Development of an alternating magnetic-field-assisted finishing process for microelectromechanical systems micropore x-ray optics.
X-ray astronomy research is often limited by the size, weight, complexity, and cost of functioning x-ray optics. Micropore optics promises an economical alternative to traditional (e.g., glass or foil) x-ray optics; however, many manufacturing difficulties prevent micropore optics from being a viable solution. Ezoe et al. introduced microelectromechanical systems (MEMS) micropore optics having curvilinear micropores in 2008. Made by either deep reactive ion etching or x-ray lithography, electroforming, and molding (LIGA), MEMS micropore optics suffer from high micropore sidewall roughness (10-30nmrms) which, by current standards, cannot be improved. In this research, a new alternating magnetic-field-assisted finishing process was developed using a mixture of ferrofluid and microscale abrasive slurry. A machine was built, and a set of working process parameters including alternating frequency, abrasive size, and polishing time was selected. A polishing experiment on a LIGA-fabricated MEMS micropore optic was performed, and a change in micropore sidewall roughness of 9.3+/-2.5nmrms to 5.7+/-0.7nmrms was measured. An improvement in x-ray reflectance was also seen. This research shows the feasibility and confirms the effects of this new polishing process on MEMS micropore optics.
Riveros
Raul E
RE
Department of Mechanical and Aerospace Engineering, University of Florida,227 MAE-B, Gainesville, Florida 32611, USA. pigup@ufl.edu
Yamaguchi
Hitomi
H
Mitsuishi
Ikuyuki
I
Takagi
Utako
U
Ezoe
Yuichiro
Y
Kato
Fumiki
F
Sugiyama
Susumu
S
Yamasaki
Noriko
N
Mitsuda
Kazuhisa
K