Optical ridge waveguides preserving the thermo-optic features in LiNbO3 crystals fabricated by combination of proton implantation and selective wet etching.
We report on a new, simple method to fabricate optical ridge waveguides in a z-cut LiNbO3 wafer by using proton implantation and selective wet etching. The measured modal field is well confined in the ridge waveguide region, which is also confirmed by the numerical simulation. With thermal annealing treatment at 400 degrees C, the propagation loss of the ridge waveguides is determined to be as low as approximately 0.9 dB/cm. In addition, the measured thermo-optic coefficients of the waveguides are in good agreement with those of the bulk, suggesting potential applications in integrated photonics.
Tan
Yang
Y
School of Physics, Shandong University, Jinan 250100, China.
Chen
Feng
F
D003460:Crystallization / Q000379:methods*; D004867:Equipment Design; D019544:Equipment Failure Analysis; D008422:Materials Testing; D009556:Niobium; D010087:Oxides / Q000138:chemical synthesis*; D011522:Protons; D012031:Refractometry / Q000295:instrumentation*; D013499:Surface Properties; D013696:Temperature; D017155:Wettability
D010087:Oxides; D011522:Protons; D009556:Niobium; C091692:lithium niobate