Improved performance of membrane free single-chamber air-cathode microbial fuel cells with nitric acid and ethylenediamine surface modified activated carbon fiber felt anodes.
Surface modifications of anode materials are important for enhancing power generation of microbial fuel cell (MFC). Membrane free single-chamber air-cathode MFCs, MFC-A and MFC-N, were constructed using activated carbon fiber felt (ACF) anodes treated by nitric acid and ethylenediamine (EDA), respectively. Experimental results showed that the start-up time to achieve the maximum voltages for the MFC-A and MFC-N was shortened by 45% and 51%, respectively as compared to that for MFC-AT equipped with an unmodified anode. Moreover, the power output of MFCs with modified anodes was significantly improved. In comparison with MFC-AT which had a maximum power density of 1304 mW/m(2), the MFC-N achieved a maximum power density of 1641 mW/m(2). The nitric acid-treated anode in MFC-A increased the power density by 58% reaching 2066 mW/m(2). XPS analysis of the treated and untreated anode materials indicated that the power enhancement was attributable to the changes of surface functional groups.
Zhu
Nengwu
N
College of Environmental Science and Engineering, South China University of Technology, Guangzhou 510006, China. nwzhu@scut.edu.cn
Chen
Xi
X
Zhang
Ting
T
Wu
Pingxiao
P
Li
Ping
P
Wu
Jinhua
J
D000388:Air; D001674:Bioelectric Energy Sources / Q000382:microbiology*; D002241:Carbohydrates / Q000737:chemistry*; D002606:Charcoal / Q000737:chemistry*; D004560:Electricity; D004566:Electrodes; D004867:Equipment Design; D005029:Ethylenediamines / Q000737:chemistry*; D017942:Nitric Acid / Q000737:chemistry*; D056951:Photoelectron Spectroscopy; D013499:Surface Properties
D002241:Carbohydrates; D005029:Ethylenediamines; D002606:Charcoal; D017942:Nitric Acid; C031234:ethylenediamine