Selective adsorption behavior of phosphate onto aluminum hydroxide gel.
The specific surface area and X-ray diffraction patterns for an aluminum hydroxide gel (AHG) calcined at 300-1150 degrees C, the number of surface hydroxyl groups in the AHG, and the adsorption isotherms of phosphate on AHG were measured in order to develop a phosphate recovery agent. AHG was transformed into gamma- and alpha-alumina by the calcinations treatment. The amount of phosphate adsorbed onto AHG increases at calcining temperatures of 300-700 degrees C and decreases above a calcining temperature of 800 degrees C. It was found that AHG selectively adsorbs phosphate ions, but not other anions, and shows the highest adsorption capacity at pH 4-6. Further, the alkali resistance of AHG increased with calcination, and more than 80% of the phosphate adsorbed with an NaOH aqueous solution underwent desorption. The addition of colloidal alumina and colloidal silica resulted in the formation of granules of 500-840 microm size. The amount of phosphate adsorbed onto AHG after granulation was similar to that before granulation. Thus, the phosphate absorption capacity of AHG did not decrease after granulation suggesting that AHG can be used as a phosphate adsorbent.
Kawasaki
Naohito
N
Faculty of Pharmacy, Department of Pharmacy, Kinki University, Higashi-Osaka, Japan. kawasaki@phar.kindai.ac.jp
Ogata
Fumihiko
F
Tominaga
Hisato
H
D000327:Adsorption; D000536:Aluminum Hydroxide / Q000737:chemistry*; D006863:Hydrogen-Ion Concentration; D010316:Particle Size; D010710:Phosphates / Q000302:isolation & purification*; D013696:Temperature; D014961:X-Ray Diffraction
D010710:Phosphates; D000536:Aluminum Hydroxide