Thermally triggered reversible transformation between parallel staggered stacking and plywood-like stacking of 1D coordination polymer chains.
An unusual example showing reversible interconversion of chain-like isomers under controlled experimental settings is reported, which illustrates the key role of assembly conditions for the target packing architecture with related properties. The reaction of Mn(II) ions with an organic ligand 2-hydroxypyrimidine-4,6-dicarboxylic acid (H(3)hpdc) at room temperature gives a coordination polymer {[Mn(3)(hpdc)(2)(H(2)O)(6)] x 2 H(2)O}(n) containing parallel staggered stacking, whereas the reaction under hydrothermal conditions at 150 degrees C affords a compound {[Mn(3)(hpdc)(2)(H(2)O)(6)] x H(2)O}(n) possessing plywood-like stacking. Interestingly, two compounds contain similar one-dimensional chain components with different orientations that can be controlled by thermodynamic factors. Thermally triggered reversible interconversion of the two compounds was verified by X-ray powder, IR, and element analysis. The spin-canted antiferromagnetic behaviors are observed in as-synthesized samples, and the influence of chain orientations on magnetic properties has been detected.
Sun
Jian-Ke
JK
State Key Laboratory of Structural Chemistry, Fujian Institute of Research on the Structure of Matter and Graduate School of the Chinese Academy of Sciences, Fuzhou, Fujian 350002 China.
Jin
Xu-Hui
XH
Chen
Chao
C
Zhang
Jie
J