Au disk nanoelectrode by electrochemical deposition in a nanopore.
In this technical note, we report a process in scaling down the fabrication of Au disk nanoelectrodes as small as approximately 4 nm in radii. We have developed a bottom-up approach toward the fabrication of individual disk-shape Au nanoelectrodes. This new approach is based upon electrochemical deposition of Au in a silica nanopore electrode and involves the following four steps. First, a laser-assisted pulling process is employed to fabricate a disk-shape Pt nanoelectrode. Second, a Pt nanopore electrode is obtained by electrochemically etching the Pt from the disk nanoelectrode. Third, a Au metal nanowire is electrochemically deposited using the Pt nanopore electrode as a template. In the last step, the Au electrode is slightly polished to expose a disk-shape Au nanoelectrode, whose size is determined by the size of the initial Pt nanoelectrode. Steady-state voltammetry in the presence of ferrocene has been used to characterize these Au nanoelectrodes. The Au nanoelectrodes are also characterized using cyclic voltammetry in a H2SO4 solution. The results show characteristic peaks corresponding to the formation of Au surface oxides and their subsequent reduction. The Au nanoelectrodes are modified with 6-(ferrocenyl)hexanethiol molecules, and cyclic voltammetry is used to characterize the ferrocene molecules attached at the Au. As an application, we have constructed Au single-nanoparticle electrodes (SNPEs) using the Au disk nanoelectrodes fabricated by electrochemical deposition. Our initial results of such SNPEs show excellent electrochemical response from single Au nanoparticles.
Jena
Bikash Kumar
BK
Department of Chemistry, University of Washington, Seattle, Washington 98195-1700, USA.
Percival
Stephen J
SJ
Zhang
Bo
B