Corrosion fatigue behaviors of two biomedical Mg alloys - AZ91D and WE43 - In simulated body fluid.
Magnesium alloys have been recently developed as biodegradable implant materials, yet there has been no study concerning their corrosion fatigue properties under cyclic loading. In this study the die-cast AZ91D (A for aluminum 9%, Z for zinc 1% and D for a fourth phase) and extruded WE43 (W for yttrium 4%, E for rare earth mischmetal 3%) alloys were chosen to evaluate their fatigue and corrosion fatigue behaviors in simulated body fluid (SBF). The die-cast AZ91D alloy indicated a fatigue limit of 50MPa at 10⁷ cycles in air compared to 20MPa at 10⁶ cycles tested in SBF at 37°C. A fatigue limit of 110MPa at 10⁷ cycles in air was observed for extruded WE43 alloy compared to 40MPa at 10⁷ cycles tested in SBF at 37°C. The fatigue cracks initiated from the micropores when tested in air and from corrosion pits when tested in SBF, respectively. The overload zone of the extruded WE43 alloy exhibited a ductile fracture mode with deep dimples, in comparison to a brittle fracture mode for the die-cast AZ91D. The corrosion rate of the two experimental alloys increased under cyclic loading compared to that in the static immersion test.
Gu
X N
XN
State Key Laboratory for Turbulence and Complex System, College of Engineering, Peking University, Beijing 100871, China.
Zhou
W R
WR
Zheng
Y F
YF
Cheng
Y
Y
Wei
S C
SC
Zhong
S P
SP
Xi
T F
TF
Chen
L J
LJ
D000497:Alloys / Q000737:chemistry*; D001672:Biocompatible Materials / Q000737:chemistry*; D001826:Body Fluids / Q000737:chemistry*; D003343:Corrosion; D004573:Electrolytes / Q000737:chemistry; D008274:Magnesium / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D013314:Stress, Mechanical; D013499:Surface Properties; D013696:Temperature; D014961:X-Ray Diffraction
D000497:Alloys; D001672:Biocompatible Materials; D004573:Electrolytes; D008274:Magnesium