Study of concentration-dependent cobalt ion doping of TiO2 and TiO(2-x)Nx at the nanoscale.
Experiments with a porous sol-gel generated TiO(2) nanocolloid and its corresponding oxynitride TiO(2-x)N(x) are carried out to evaluate those transformations which accompany additional doping with transition metals. In this study, doping with cobalt (Co(ii)) ions is evaluated using a combination of core level and VB-photoelectron and optical spectroscopy, complementing data obtained from Raman spectroscopy. Raman spectroscopy suggests that cobalt doping of porous sol-gel generated anatase TiO(2) and nitridated TiO(2-x)N(x) introduces a spinel-like structure into the TiO(2) and TiO(2-x)N(x) lattices. TEM and XPS data complemented by valence band-photoelectron spectra demonstrate that metallic cobalt clusters are not formed even at high doping levels. As evidenced by Raman spectroscopy, the creation of a spinel-like structure is commensurate with the room temperature conversion of the oxide and its oxynitride from the anatase to the rutile form. The onset of this kinetically driven process correlates with the formation of spinel sites within the TiO(2) and TiO(2-x)N(x) particles. Despite their visible light absorption, the photocatalytic activity of these cobalt seeded systems is diminished relative to the oxynitride TiO(2-x)N(x).
Gole
James L
JL
School of Physics, Georgia Institute of Technology, 837 State Street, NW, Atlanta, GA 30332-0430, USA. jim.gole@physics.gatech.edu
Prokes
Sharka M
SM
Glembocki
O J
OJ
Wang
Junwei
J
Qiu
Xiaofeng
X
Burda
Clemens
C
D002384:Catalysis; D003035:Cobalt / Q000737:chemistry*; D007700:Kinetics; D053768:Metal Nanoparticles / Q000737:chemistry*; D009584:Nitrogen / Q000737:chemistry; D056951:Photoelectron Spectroscopy; D013059:Spectrum Analysis, Raman; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
C009495:titanium dioxide; D003035:Cobalt; D014025:Titanium; D009584:Nitrogen