Effectiveness factor and diffusion limitations in collagen gel modules containing HepG2 cells.
A major obstacle in tissue engineering is overcoming hypoxia in thick, three-dimensional (3D) engineered tissues, which is caused by the diffusional limitations of oxygen and lack of internal vasculature to facilitate mass transfer. Modular tissue engineering is a bio-mimetic strategy that forms scalable, vascularized and uniform 3D constructs by assembling small (sub-mm), cell-containing modules. It was previously assumed that mass transfer resistance within the individual modules was negligible, due to their small size. In the present study, this assumption was tested using theoretical analysis of oxygen transport within the module (effectiveness factor) and experimental studies. Small (400 µm diameter post-contraction) and large (700 µm diameter post-contraction) HepG2-collagen modules were made for a range of seeding densities (2 × 10(6) -1 × 10(7) cells/ml collagen). Cell density, distribution and morphology within the modules showed that the small modules were capable of sustaining high cell densities (8.0 × 10(7) ± 4.4 × 10(7) cells/cm(3) ) with negligible mass transfer inhibition. Conversely, large modules developed a necrotic core and had significantly (p < 0.05) reduced cell densities (1.5 × 10(7) ± 9.2 × 10(6) cells/cm(3) ). It was also observed that the embedded cells responded quickly to the oxygen availability, by proliferating or dying, to reach a sustainable density of approximately 8000 cells/module. Furthermore, a simple effectiveness factor calculation was successful in estimating the maximum cell density per module. The results gathered in this study confirm the previous assumption that the small-diameter modules avoid the internal mass transfer limitations that are often observed in larger constructs.
Corstorphine
Lindsay
L
Institute of Biomaterials and Biomedical Engineering, University of Toronto, Canada.
Sefton
Michael V
MV
D015687:Cell Hypoxia; D003094:Collagen; D005782:Gels; D056945:Hep G2 Cells; D006801:Humans; D023822:Tissue Engineering / Q000379:methods*; D054457:Tissue Scaffolds
D005782:Gels; D003094:Collagen