Parabolic dependence of material properties and cell behavior on the composition of polymer networks via simultaneously controlling crosslinking density and crystallinity.
A systematic investigation was performed on regulating materials properties and cell behavior using hybrid networks composed of amorphous poly(propylene fumarate) (PPF) and three poly(epsilon-caprolactone) diacrylates (PCLDAs) with variance in crystallinity and melting temperature. Through controlling both crosslinking density and crystallinity in the photo-crosslinked PPF/PCLDA blends, mechanical properties could be tuned efficiently in a wide range. For PCLDA synthesized from a low-molecular weight PCL diol precursor with a low crystallinity and a low melting point, crosslinks could completely suppress crystalline domains over the composition range in the PPF/PCLDA networks. Consequently, tensile, shear, torsional, and compression moduli all increased with the composition of PPF or the crosslinking density continuously for amorphous PPF/PCLDA networks. For PCLDAs synthesized using two PCL diols with higher molecular weights, crystallinity remained for the PCLDA compositions between approximately 80% and 100%. Minimum moduli and tensile stress at break were found at the lowest required composition of PPF for suppressing crystallinity. Surface physicochemical properties and morphology of the crosslinked blend disks have been characterized and their capabilities of adsorbing proteins from cell culture medium have been determined. Using both mouse MC3T3-E1 cells and rat Schwann cell precursor line (SpL201) cells, cell responses to these polymer networks such as cell adhesion, spreading, and proliferation were found to be dramatically distinct on different polymer networks and demonstrated non-monotonic or parabolic dependence on the network composition, coincident with the composition dependence of the mechanical properties.
Cai
Lei
L
Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996, USA.
Wang
Shanfeng
S
D000818:Animals; D001672:Biocompatible Materials / Q000009:adverse effects / Q000138:chemical synthesis / Q000737:chemistry; D002448:Cell Adhesion / Q000187:drug effects; D002460:Cell Line; D049109:Cell Proliferation / Q000187:drug effects; D005650:Fumarates / Q000737:chemistry; D051379:Mice; D008962:Models, Theoretical; D011108:Polymers / Q000009:adverse effects / Q000737:chemistry*; D011126:Polypropylenes / Q000737:chemistry; D051381:Rats; D017550:Spectroscopy, Fourier Transform Infrared; D013696:Temperature
D001672:Biocompatible Materials; D005650:Fumarates; D011108:Polymers; D011126:Polypropylenes; C097850:poly(propylene fumarate)