Organic single-crystalline p-n junction nanoribbons.
This article focuses on the growth and transport properties of organic single-crystalline p-n junction nanoribbons. The development of organic nanoelectronics requires the fabrication of organic nanometer-sized p-n junctions for high-performance devices and integrated circuits. Here we demonstrate the formation of single-crystalline p-n junction nanoribbons of organic semiconductors by selective crystallization of copper hexadecafluorophthalocyanine (F(16)CuPc, n-type) on copper phthalocyanine (CuPc, p-type) single-crystalline nanoribbons. The crystallization of F(16)CuPc onto CuPc requires several parameters, including similar molecular structures, similar lattice constants, and pi-stacking along the nanoribbon axis. Ambipolar transport of the p-n junction nanoribbons was observed in field-effect transistors with balanced carrier mobilities of 0.05 and 0.07 cm(2) V(-1) s(-1) for F(16)CuPc and CuPc, respectively. A basic p-n junction nanoribbon photovoltaic device showed current rectification under AM 1.5 simulated light. The discrete p-n junction nanoribbons may serve as ideal systems for understanding basic charge-transport and photovoltaic behaviors at organic-organic interfaces.
Zhang
Yajie
Y
Beijing National Laboratory for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China.
Dong
Huanli
H
Tang
Qingxin
Q
Ferdous
Sunzida
S
Liu
Feng
F
Mannsfeld
Stefan C B
SC
Hu
Wenping
W
Briseno
Alejandro L
AL