Tensile strength of laser welded cobalt-chromium alloy with and without an argon atmosphere.
The tensile strength and depth of weld of two cobalt chromium alloys before and after laser welding with and without an argon gas atmosphere were investigated. Using two cobalt chromium alloys, rod shaped specimens (5 cm x 1.5 mm) were cast. Specimens were sand blasted, sectioned and welded with a pulsed Nd: YAG laser welding machine and tested in tension using an Instron universal testing machine. A statistically significant difference in tensile strength was observed between the two alloys. The tensile strength of specimens following laser welding was significantly less than the unwelded controls. Scanning electron microscopy showed that the micro-structure of the cast alloy was altered in the region of the weld. No statistically significant difference was found between specimens welded with or without an argon atmosphere.
Tartari
Anna
A
Clark
Robert K F
RK
Juszczyk
Andrzej S
AS
Radford
David R
DR
D001128:Argon; D002858:Chromium Alloys / Q000737:chemistry*; D003035:Cobalt; D003735:Dental Casting Technique; D012994:Dental Soldering / Q000295:instrumentation*; D003799:Dental Stress Analysis; D003779:Denture Design; D053844:Lasers, Solid-State; D008422:Materials Testing; D013718:Tensile Strength; D014896:Welding / Q000295:instrumentation*
D002858:Chromium Alloys; D003035:Cobalt; D001128:Argon