Torsional superelasticity of NiTi archwires.
OBJECTIVE
To reproduce and compare the intraoral torsional behavior of 10 commonly used preformed upper NiTi 0.017 x 0.025 archwires in 0.018-slot brackets at 20 degrees C, 35 degrees C, and 55 degrees C.


METHODS
Ten upper preformed NiTi archwires were compared to a multibraided stainless steel wire. An original testing bench was used to reproduce palatal root torque applied onto an upper central incisor with a maximum value of 1540 g x mm. Ten samples of each wire type were tested at 20 degrees C, 35 degrees C, and 55 degrees C each.


RESULTS
Loading and unloading at 20 degrees C revealed three categories of wires: a group of four NiTi wires of relative stiffness bereft of any superelasticity, a group of six NiTi wires displaying some horizontal plateau, and finally the stainless steel wire of lesser stiffness. Testing at the average oral temperature of 35 degrees C produced the same three categories of wires, with only 2 of 10 NiTi wires displaying a superelastic effect (Copper NiTi 35 degrees C and 40 degrees C). None of the NiTi wires was superelastic at 55 degrees C. Moments increased with temperature as the martensite was replaced by the more rigid austenite.


CONCLUSIONS
This study showed that most NiTi wires did not exhibit in torsion the superelastic effect traditionally described in bending. The combination of straight-wire prescriptions and rectangular superelastic NiTi archwires did not provide optimal constant moments necessary to gain third-order control of tooth movement early in treatment. A braided stainless steel rectangular archwire displayed better torsional behavior at 35 degrees C than most NiTi archwires of the same dimensions.
Bolender
Yves
Y
Department of Orthodontics, Nancy Université, Nancy, France. bolender@wanadoo.fr
Vernière
Anne
A
Rapin
Christophe
C
Filleul
Marie-Pierryle
MP
D003300:Copper; D003722:Dental Alloys; D003799:Dental Stress Analysis; D004548:Elasticity; D008422:Materials Testing; D009532:Nickel; D009969:Orthodontic Wires; D013193:Stainless Steel; D013696:Temperature; D014025:Titanium; D054159:Torsion, Mechanical
C415948:Copper NiTi; D003722:Dental Alloys; C040654:titanium nickelide; C093824:Martensite; C093826:Austenite; D013193:Stainless Steel; D003300:Copper; D009532:Nickel; D014025:Titanium