Effect of early orthodontic force on shear bond strength of orthodontic brackets bonded with different adhesive systems.
BACKGROUND
This study was conducted to evaluate the effect of applying early orthodontic force on the shear bond strength (SBS) of orthodontic brackets bonded with 4 adhesive systems.


METHODS
Eighty stainless steel brackets were bonded to the enamel surfaces of extracted premolars with 4 adhesive systems. For each adhesive, 10 brackets were bonded without application of force (groups 1, 3, 5, and 7), and another 10 were subjected to a 120-g force with a coil spring (groups 2, 4, 6, and 8). This force was applied 30 minutes after bonding and maintained for 24 hours. Groups 1 and 2 had Rely-a-bond primer and Rely-a-bond adhesive (Reliance Orthodontic Products, Itasca, Ill). Groups 3 and 4 had Transbond XT primer and Transbond XT adhesive (3M Unitek, Monrovia, Calif). Groups 5 and 6 had Transbond Plus Self Etching Primer and Transbond XT adhesive (3M Unitek). Groups 7 and 8 had RelyX Unicem (3M ESPE, Seefeld, Germany). After thermocycling, SBS testing was performed by using a universal testing machine (Type 500, Lloyd Instruments Ltd, Fareham Hants, UK). The results of SBS testing for all adhesives were analyzed by 2-way analysis of variance and the Duncan test. The unpaired Student t test was used to compare the effect of force on the SBS of each adhesive.


RESULTS
Transbond XT primer and its adhesive had the highest values (without force, 11.2 +/- 3.1 MPa; with force, 10.7 +/- 2.7 MPa), and RelyX Unicem had the lowest (without force, 5.8 +/- 1.5MPa; with force, 5.7 +/- 1.6 MPa). Application of force yielded nonsignificant reductions in SBS for all adhesives; this reduction was less pronounced with RelyX Unicem.


CONCLUSIONS
For all studied adhesive systems, orthodontic force up to 120 g can be applied within the first hour after bonding with no deleterious effects on bond strength.
Abdelnaby
Yasser Lotfy
YL
Department of Orthodontics, Faculty of Dentistry, Mansoura University, Mansoura, Egypt. dryasserlotfy@yahoo.com
Al-Wakeel
Essam El Saeid
Eel S
D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D001840:Dental Bonding / Q000379:methods*; D003738:Dental Cements / Q000737:chemistry* / Q000145:classification; D017005:Dental Debonding; D003799:Dental Stress Analysis; D006801:Humans; D016910:Orthodontic Brackets; D019279:Resin Cements / Q000737:chemistry*; D033081:Shear Strength; D013314:Stress, Mechanical
D003738:Dental Cements; C097531:Rely a Bond system; C528569:Rely-X; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C065742:Transbond; D017438:Bisphenol A-Glycidyl Methacrylate