Temperature rise during intraoral polymerization of self-cured hard denture base liners.
The aim of this in-vivo study was to evaluate the temperature rise during polymerization of five chairside self-cured hard denture base reliners. For the same patient, 30 identical baseplates, exposing a space on their tissue surface to accommodate the lining material, were made of a light-cured denture base material. A hole was drilled in the center of this area to enable the thermocouple wire of the temperature measuring device to have direct access to the palatal surface of the baseplate. Six baseplates were used for each of the five lining materials tested. Temperature recordings were made every 15 seconds. Data were analyzed using single factor analysis of variance (ANOVA) and the Scheffe's post-hoc analysis for multiple comparisons. The mean maximum temperature values ranged from 40.2 degrees C to 45.7 degrees C being statistically different among the materials (P<0.001). The maximum peak temperature was 53 degrees C and the lowest 39 degrees C. Also the difference between the time each material reached the peak of temperature was statistically significant (P<0.0001). A temperature range of 5.5 degrees C was demonstrated among materials, with the highest polymerization temperatures recorded for Flexacryl Hard and the lowest for Rebase and GC Reline hard. Ufi-gel hard showed the fastest polymerization cycle and was the first to reach the maximum temperature. The available chairside hard liners must be chosen with care considering the thermal effect on the oral mucosa and the discomfort of patient.
Yannikakis
Stavros
S
Technological Educational Institution of Athens, Faculty of Health and Caring Professions, Department of Dental Technology, Athens, Greece. yannista@otenet.gr
Polychronakis
Nick
N
Zissis
Alcibiades
A
D000180:Acrylic Resins; D000704:Analysis of Variance; D003819:Denture Bases; D003823:Denture Rebasing; D006358:Hot Temperature; D006801:Humans; D008422:Materials Testing; D009055:Mouth; D055116:Self-Curing of Dental Resins; D018709:Statistics, Nonparametric
D000180:Acrylic Resins