Synthesis of single-crystalline alpha-Si(3)N(4) nanobelts by extended vapour-liquid-solid growth.
A simple chemical method for the production of single-crystalline alpha-Si(3)N(4) nanobelts has been developed, consisting of nitridation of a high-Si-content Fe-Si 'catalyst' by ammonia at 1300 degrees C. The as-synthesized product was characterized by means of x-ray diffraction, electron microscopy and energy-dispersive x-ray spectroscopy. The alpha-Si(3)N(4) nanobelts have widths of 60-120 nm, thicknesses of 10-30 nm and lengths up to microns. Four intense green-blue luminescence bands at 398 nm (3.12 eV), 434 nm (2.86 eV), 492 nm (2.52 eV) and 540 nm (2.30 eV) were observed and analysed for the product, which indicates the potential applications in optoelectronics. The growth mechanism has also been speculated upon. The potential technological importance of the product, the simplicity of the preparation procedure, as well as the cheap commercial precursor of Fe-Si alloy particles makes this study both scientifically and technologically interesting.
Huo
Kaifu
K
Key Laboratory of Mesoscopic Chemistry of MOE and Jiangsu Provincial Laboratory for Nanotechnology, Department of Chemistry, Nanjing University, Nanjing 210093, People's Republic of China.
Ma
Yanwen
Y
Hu
Yemin
Y
Fu
Jijiang
J
Lu
Bin
B
Lu
Yinong
Y
Hu
Zheng
Z
Chen
Yi
Y