Effect of firing protocols on cohesive failure of all-ceramic crowns.
OBJECTIVE
The mechanical properties of veneering material in all-ceramic restorations are inferior to those of high-strength ceramics. The objective of this study was to assess the effect of three different firing protocols (different cooling times) on cohesive failure of veneered all-ceramic crowns using a newly developed in vitro test design.


METHODS
A prepared anterior maxillary incisor was used to produce geometrically identical crowns (n=68) with a zirconia framework 0.4mm thick veneered with two different ceramics and prepared by use of three different firing protocols. Twenty crowns were loaded until fracture without artificial ageing; the other crowns underwent thermocycling and chewing simulation before ultimate-load testing. Statistical analysis was performed using non-parametric tests.


RESULTS
The results showed that a reduced temperature decrease after firing led to better performance of all-ceramic anterior crowns in the in vitro tests. A significant difference with regard to firing protocol (p=0.006) was observed for one veneering ceramic material only, however.


CONCLUSIONS
It can therefore be concluded that the test design presented enabled sensitive measurement of the effect of firing protocol on cohesive failure of all-ceramic crowns. The modified firing protocol with 6min additional cooling time resulted in greater resistance.
Rues
Stefan
S
Department of Prosthodontics, Dental School, University of Heidelberg, MZK II - Prothetik, Im Neuenheimer Feld 400, D-69120 Heidelberg, Germany.
Kröger
Elke
E
Müller
Denise
D
Schmitter
Marc
M
D003442:Crowns; D003735:Dental Casting Technique; D003776:Dental Porcelain; D019232:Dental Restoration Failure; D003799:Dental Stress Analysis; D003801:Dental Veneers; D018709:Statistics, Nonparametric; D013997:Time Factors
D003776:Dental Porcelain