Phase transformation and crystal structure of La(2)Ni(7)H(x) studied by in situ X-ray diffraction.
The phase transformation of La(2)Ni(7) during hydrogenation was investigated by in situ X-ray diffraction. We found two hydride phases, La(2)Ni(7)H(7.1) (phase I) and La(2)Ni(7)H(10.8) (phase II), during the first absorption cycle. The metal sublattice of phase I was orthorhombic (space group Pbcn) with lattice parameters a = 0.50128(6) nm, b = 0.8702(1) nm, and c = 3.0377(1) nm. The sublattice for phase II was monoclinic (space group C2/c) with lattice parameters a = 0.51641(9) nm, b = 0.8960(1) nm, c = 3.1289(1) nm, and β = 90.17(1)°. The lattice parameter c increased with the hydrogen content, while a and b decreased in the formation of phase I from the alloy. Phase transformation from phase I to phase II was accompanied by isotropic expansion. The La(2)Ni(4) and LaNi(5) subunit expanded by 48.9% and 6.0% in volume, respectively, during hydrogenation to phase I. They expanded an additional 14% and 5.8%, respectively, in the formation of phase II. The obtained volume expansion suggested different hydrogen distribution in the La(2)Ni(4) and LaNi(5) subunit during hydrogenation.
Iwase
Kenji
K
National Institute of Advanced Industrial Science and Technology (AIST), AIST Central-5, 1-1-1 Higashi, Tsukuba, Ibaraki 305-8565, Japan. fbiwase@mx.ibaraki.ac.jp
Sakaki
Kouji
K
Nakamura
Yumiko
Y
Akiba
Etsuo
E