title: Nanocap arrays of granular CoCrPt:SiO2 films on silica particles: tailoring of the magnetic properties by Co+ irradiation.
abstract: An approach for tailoring the magnetic properties by ion irradiation of granular perpendicular CoCrPt:SiO(2) films grown on silica particles with sizes down to 10 nm was investigated. The as-prepared samples reveal an intriguing scaling dependence of the coercive field and remnant magnetization: both parameters are found to decrease with decreasing particle size. However, Co(+) irradiation at a low fluence of 0.5 x 10(14) cm(-2) already results in an opposite scaling behavior. It is assumed that this modification is due to the enhancement of the intergranular magnetic exchange coupling of the granular CoCrPt:SiO(2) film initiated by Co(+) irradiation resulting in a modified reversal behavior. Further increase of the irradiation fluence beyond 1.6 x 10(14) ions cm(-2) leads to a degradation of the magnetic layer properties, lowering the remnant magnetization and the coercive field in the easy-axis direction. Moreover, the local magnetic properties of the samples were analyzed by magnetic force microscopy revealing magnetic multi-domain cap structures.
authors.affiliation: Institute of Physics, Chemnitz University of Technology, Chemnitz, Germany. philipp.krone@physik.tu-chemnitz.de
authors.forename: P
authors.initials: P
authors.lastname: Krone
authors.forename: C
authors.initials: C
authors.lastname: Brombacher
authors.forename: D
authors.initials: D
authors.lastname: Makarov
authors.forename: K
authors.initials: K
authors.lastname: Lenz
authors.forename: D
authors.initials: D
authors.lastname: Ball
authors.forename: F
authors.initials: F
authors.lastname: Springer
authors.forename: H
authors.initials: H
authors.lastname: Rohrmann
authors.forename: J
authors.initials: J
authors.lastname: Fassbender
authors.forename: M
authors.initials: M
authors.lastname: Albrecht