Mechanical and ultrastructural evaluation of quartz post-endodontic reconstructions.
Aesthetics is a very important element in dentistry, but requires the support of good mechanical performance. Quartz fiber used in post-endodontic reconstruction is an aesthetic material, although there is little research concerning its mechanical properties. This study evaluated the retentive property of post-endodontic reconstruction, composed of a quartz fiber post. Different thermal stresses were applied in vitro to post-endodontic reconstructions, in order to simulate oral thermal action on post-system dental structure linkage. We chose 30 human extracted teeth, endodontically treated and restored, and then divided them into three groups of 10 teeth. A different treatment was applied to each group before mechanical testing: in the 1st group no treatment was done (controls); in the 2nd group teeth were subjected, in a climatic chamber, to 10 thermo-cycles between 4 degrees C and 58 degrees C; in the 3rd group teeth were stored in a saline solution at 37 degrees C for 48 hr. The teeth then underwent tensile shear stress tests at break point using a computerized electronic dynamometer. After mechanical testing, two teeth from each group were longitudinally half-sectioned, sputter-coated in gold and observed by scanning electron microscopy (SEM). The extracted quartz fiber post of each tooth also underwent SEM observation. Mechanical test results demonstrated that thermal cyclic variations could affect bond stability between dental structures and posts in quartz fiber reconstructions, whereas their bond strength seemed unaffected by humidity increases. Quartz fiber post SEM observation demonstrated a homogeneous structure and a regular fiber disposition. Dental root canal morphology SEM images always showed a different thickness in the cement layer. (Journal of Applied Biomaterials & Biomechanics 2004; 2: 156-61).
Majori
M
M
Department of Technology and Health, Italian National Institute of Health, Roma - Italy.
Bedini
R
R
Altamura
C
C
Filippini
P
P
Caiazza
S
S