Hierarchical synthesis of silver nanoparticles and wires by copolymer templates and visible light.
Self-assembled silver wires in micro-meter scale were obtained from aqueous silver nitrate solution in the presence of a comb-like copolymer as the sole organic component. The requisite copolymer was easily prepared by the grafting poly(oxyethylene)-monoamine (POE-amine) onto poly(styrene-co-maleic anhydride) (SMA). Upon storage at ambient temperature with exposure to daylight, the aqueous AgNO(3)/SMA-POE solution gradually underwent a color changed from transparent pale-yellow to dark-violet over a period of hours, and after several months a solid precipitate was deposited. The formation process was monitored by ultraviolet-visible spectrometer, particle size analysis, scanning electron microscope, and transmission electron microscope. Silver wires were hierarchically formed by progressive transformation from the initial appearance of silver nanoparticles (ca. 10nm in diameter), followed by the intermediate rectangles (0.6-1.0μm in width and 0.4μm in length) in solution and ultimately the precipitates in micro-scale of silver wires at 1.6-6.4μm in diameter and 100-370μm in length. The progressive formation of the precipitated silver wires was accelerated by the exposure of visible light as a photo-reducing energy source. The micron-scale wires have a silver content over 97.4wt.% and a sheet resistance of 5.5×10(1)Ω/square.
Hsu
Yen-Chi
YC
Institute of Polymer Science and Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan.
Chen
Yu-Min
YM
Lin
Wei-Li
WL
Lan
Yi-Fen
YF
Chan
Ying-Nan
YN
Lin
Jiang-Jen
JJ
D008027:Light; D008298:Maleates / Q000737:chemistry*; D053768:Metal Nanoparticles / Q000737:chemistry*; D053770:Nanowires / Q000737:chemistry*; D009942:Organometallic Compounds / Q000138:chemical synthesis* / Q000737:chemistry; D010316:Particle Size; D011092:Polyethylene Glycols / Q000737:chemistry*; D011137:Polystyrenes / Q000737:chemistry*; D012834:Silver / Q000737:chemistry*; D012835:Silver Nitrate / Q000737:chemistry; D012996:Solutions; D013499:Surface Properties; D013696:Temperature
D008298:Maleates; D009942:Organometallic Compounds; D011137:Polystyrenes; D012996:Solutions; C521900:poly(styrene-co-maleic anhydride); D012834:Silver; D011092:Polyethylene Glycols; D012835:Silver Nitrate