Microporous Ni-doped TiO2 film photocatalyst by plasma electrolytic oxidation.
Ni-doped TiO2 film catalysts were prepared by a plasma electrolytic oxidation (PEO) method and were mainly characterized by means of SEM, EDS, XRD, XPS, and DRS, respectively. The effects of Ni doping on the structure, composition and optical absorption property of the film catalysts were investigated along with their inherent relationships. The results show that the film catalyst is composed of anatase and rutile TiO2 with microporous structure. Doping Ni changes the phase composition and the lattice parameters (interplanar crystal spacing and cell volume) of the films. The optical absorption range of TiO2 film gradually expands and shifts to the red with increasing dosages. Both direct and indirect transition band gaps of the TiO2 films are deduced consequently. Moreover, the photocatalytic activity of the film catalysts for splitting Na2S+Na2SO3 solution into H2 is enhanced by doping with an appropriate amount of Ni. The as-prepared TiO2 film catalyst doping with 10 g/L of Ni(Ac)2 presents the highest photocatalytic reducing activity.
Yao
Zhongping
Z
School of Chemical Engineering and Technology, Harbin Institute of Technology, No. 92 Xidazhijie Street, Nangang, Harbin 150001, PR China.
Jia
Fangzhou
F
Tian
Shujun
S
Li
ChunXiang
C
Jiang
Zhaohua
Z
Bai
Xuefeng
X
D002384:Catalysis; D003460:Crystallization / Q000379:methods; D005740:Gases / Q000737:chemistry; D006358:Hot Temperature; D008027:Light; D008422:Materials Testing; D008567:Membranes, Artificial; D008904:Miniaturization; D009532:Nickel / Q000737:chemistry* / Q000528:radiation effects; D010084:Oxidation-Reduction; D010777:Photochemistry / Q000379:methods; D016062:Porosity / Q000528:radiation effects; D014025:Titanium / Q000737:chemistry* / Q000528:radiation effects
D005740:Gases; D008567:Membranes, Artificial; C009495:titanium dioxide; D009532:Nickel; D014025:Titanium