Formation mechanism of CaTiO3 hollow crystals with different microstructures.
The crystal growth of CaTiO(3) hollow crystals with different microstructures has been investigated. In a water-free poly(ethylene glycol) 200 (PEG-200) solution, CaTiO(3) nanocubes formed first. The nanocubes underwent an oriented self-assembly into spherical particles, enhanced by the surface-adsorbed polymer molecules. Since the growth of nanocubes and their aggregation took place simultaneously, the nanocubes in the outer shells were larger than those in the cores. Disappearance of the small nanocubes in the cores of the spheres during an Ostwald ripening process led to spherical hollow crystals. Addition of a small amount of water (1.25 vol %) in the polymer solution enhanced surface recrystallization of the aggregated spheres, forming a cubic morphology. The orthorhombic distortion of the perovskite CaTiO(3) structure did not have a significant effect on the nanocube aggregation, resulting in a domain structure in the shells. Single-crystalline hollow cubes were produced with a slightly higher water content, e.g., 5 vol %. This process of (1) aggregation of nanocubes and (2) surface crystallization followed by (3) surface-to-core extension of recrystallization gives a good example of the reversed crystal growth route in ceramic materials. The proposed formation mechanism of the hollow CaTiO(3) crystals would enable us to control the microstructures of these materials and to explain the formation of many other hollow crystals.
Yang
Xianfeng
X
State Key Laboratory of Optoelectronic Materials and Technologies, School of Chemistry and Chemical Engineering, and Instrumental Analysis and Research Centre, Sun Yat-Sen (Zhongshan) University, Guangzhou 510275, PR China.
Fu
Junxiang
J
Jin
Chongjun
C
Chen
Jian
J
Liang
Chaolun
C
Wu
Mingmei
M
Zhou
Wuzong
W
D017610:Calcium Compounds / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D046529:Microscopy, Electron, Transmission; D010087:Oxides / Q000737:chemistry*; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction
D017610:Calcium Compounds; D010087:Oxides; C059910:perovskite; D014025:Titanium