MnO(x)/TiO(2) composite nanoxides synthesized by deposition-precipitation method as a superior catalyst for NO oxidation.
A series of MnO(x)/TiO(2) composite nanoxides were prepared by deposition-precipitation (DP) method, and the sample with the Mn/Ti ratio of 0.3 showed a superior activity for NO catalytic oxidation to NO(2). The maximum NO conversion over MnO(x)(0.3)/TiO(2)(DP) could reach 89% at 250°C with a GHSV of 25,000h(-1), which was much higher than that over the catalyst prepared by conventional wet-impregnation (WI) method (69% at 330°C). Characterization results including XRD, HRTEM, FTIR, XPS, H(2)-TPR, NO-TPD and Nitrogen adsorption-desorption implied that the higher activity of MnO(x)(0.3)/TiO(2)(DP) could be attributed to the enrichment of well-dispersed MnO(x) on the surface and the abundance of Mn(3+) species. Furthermore, DRIFT investigations and long-time running test indicated that NO(2) came from the decomposition of adsorbed nitrogen-containing species.
Wu
Zhongbiao
Z
Department of Environmental Engineering, Zhejiang University, Hangzhou 310027, China.
Tang
Nian
N
Xiao
Ling
L
Liu
Yue
Y
Wang
Haiqiang
H
D000327:Adsorption; D002384:Catalysis; D017895:Manganese Compounds / Q000737:chemistry*; D049329:Nanostructures / Q000737:chemistry; D009569:Nitric Oxide / Q000737:chemistry*; D009585:Nitrogen Dioxide / Q000138:chemical synthesis* / Q000737:chemistry; D010084:Oxidation-Reduction; D010087:Oxides / Q000138:chemical synthesis* / Q000737:chemistry*; D010316:Particle Size; D013499:Surface Properties; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
D017895:Manganese Compounds; D010087:Oxides; C009495:titanium dioxide; D009569:Nitric Oxide; D014025:Titanium; D009585:Nitrogen Dioxide