Transient photoconductivity and femtosecond nonlinear optical properties of a conjugated polymer-graphene oxide composite.
A water soluble conjugated thiophene polymer, sodium salt of poly[2-(3-thienyl)ethoxy-4-butylsulfonate] (TPP), and graphene oxide (GO) composite film (GO-TPP) device was prepared. Transient photoconductivity measurements were carried out on the GO-TPP composite film using 150 ns laser pulses of 527 nm wavelength. Highly efficient photocurrent generation was observed from the GO-TPP film. The relationships of the film photoconductivity, photocurrent decay time and electron decay times with the incident light intensity were investigated. The photoconductive gain of the film was determined to be greater than 40% and to be independent of the light intensity. Furthermore, the femtosecond nonlinear optical properties of the GO-TPP film were measured using 800 nm femtosecond laser pulses and the composite film exhibited high nonlinear absorption and nonlinear refraction coefficients.
Nalla
Venkatram
V
Department of Physics, National University of Singapore, Singapore, Singapore.
Polavarapu
Lakshminarayana
L
Manga
Kiran Kumar
KK
Goh
Bee Min
BM
Loh
Kian Ping
KP
Xu
Qing-Hua
QH
Ji
Wei
W