Hydrothermal synthesis of TiO2 hollow microspheres for the photocatalytic degradation of 4-chloronitrobenzene.
TiO(2) hollow microspheres were synthesized by a simple hydrothermal method followed by calcination at different temperatures ranging from 400 to 800°C. The prepared samples were characterized by XRD, SEM, TEM, SAED, HRTEM, N(2) adsorption, and UV-vis spectroscopy. The photocatalytic activities of the hollow microspheres were evaluated by photocatalytic decomposition of 4-chloronitrobenzene (4-CNB). Results showed that the TiO(2) hollow microspheres, which had an average external diameter of 1.75 μm, were composed of numerous TiO(2) nanoparticles. Photocatalysis experiments indicated that the TiO(2) hollow microspheres calcined at 500°C exhibited the highest photocatalytic activity, which was nearly 2 and 1.5 times higher than that of the uncalcined sample and Degussa P25, respectively. The catalyst crystallinity, catalyst dosage and 4-CNB concentration were found to have a significant impact on the degradation efficiency whereas solution pH has relatively less effect. The removal of total organic carbon (TOC) and formation of chloride, nitrate (V) anions were monitored to follow the mineralization process of 4-CNB. In addition, it was demonstrated that these TiO(2) hollow microspheres could be recycled easily without decreasing their photocatalytic activities.
Ye
Miaomiao
M
State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, PR China; Institute of Municipal Engineering, Zhejiang University, Hangzhou, 310058, PR China.
Chen
Zhonglin
Z
State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, PR China. Electronic address: zhonglinchen@263.net.
Wang
Wenshou
W
School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, PR China.
Shen
Jimin
J
State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, PR China.
Ma
Jun
J
State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, PR China.
D002384:Catalysis; D008854:Microscopy, Electron / Q000379:methods; D008863:Microspheres; D009578:Nitrobenzenes / Q000737:chemistry*; D010777:Photochemistry; D013056:Spectrophotometry, Ultraviolet; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction
D009578:Nitrobenzenes; C009495:titanium dioxide; C010407:4-chloronitrobenzene; D014025:Titanium