Synthesis, self-assembly, and charge transporting property of contorted tetrabenzocoronenes.
A facile route has been developed for the preparation of a new family of contorted 1.2,3.4,7.8,9.10-tetrabenzocoronenes (TBCs). A two-step cyclization reaction, i.e., oxidative photocyclization followed by FeCl(3)-mediated intramolecular cyclodehydrogenation, was carried out on the olefin precursors to obtain the final TBC compounds. These new TBC molecules have contorted conformation due to steric overcrowding as disclosed by single-crystal crystallographic analysis. Nevertheless, they showed extended π-conjugation compared with coronene and exhibited strong aggregation in solution. The thermal behavior and self-assembly of TBC-C8 in solid were studied by a combination of thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), powder X-ray diffraction (XRD), scanning electron microscope (SEM), and transmission electron microscope (TEM). Compound TBC-C8 showed very good thermal and photostability and exhibited long-range ordered π-stacking in the bulk state. Moreover, uniform nanofibers with tens of micrometer length are formed in the drop-casted thin films. TBC-C8 also possesses a desirable HOMO energy level (-5.10 eV), which allows efficient charge injection from electrodes such as gold electrode. The charge carrier mobilities were determined by using the space-charge limited-current (SCLC) technique and high average hole mobility of 0.61 cm(2) V(-1) s(-1) was obtained for TBC-C8.
Department of Chemistry, National University of Singapore, 3 Science Drive 3, Singapore, 117543.
Xiaojie
X
Zhang
Xiaoxia
X
Jiang
Kai
K
Zhang
Lu
L
Mao
Jing
J
Luo
Chunyan
C
Chi
Hardy Sze On
HS
Chan
Jishan
J
Wu