A double-mode piezoelectric single-crystal ultrasonic micro-actuator.
Ternary Pb(In(1/2)Nb(1/2))O(3)-Pb(Mg(1/3)Nb(2/3))O(3)-PbTiO(3) (PIN-PMN-PT) single crystals with higher coercive field (E(C) ~9 kV/cm) and higher ferroelectric-transition temperature (T(R-T) = 108°C) were grown, and correspondingly, a double-mode piezoelectric ultrasonic micro-actuator made of PIN-PMN-PT crystal brick (5 x 1.5 x 1.32 mm) and operated in the first longitudinal and the second bending modes was developed. The ferroelectric, dielectric, electromechanical, and resonance displacement properties of the micro-actuator were characterized for miniature linear piezo-motor applications. The longitudinal displacement of the actuator is ~0.11 μm (with an applied voltage of 5 V), which is comparable to that of a multilayer piezoelectric-ceramic actuator of the same size. This crystal micro-actuator was successfully used to drive a slider moving linearly.