Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO(2)/TiO(2) core/shell microspheres as high performance photocatalyst for dye degradation.
The monodisperse hybrid silica particles (h-SiO(2)) were firstly prepared by a modified sol-gel process and the surface was modified in situ with double bonds, then abundant carboxyl moieties were introduced onto the surface of the silica core via thiol-ene click reaction. Afterward, the h-SiO(2)/TiO(2) core/shell microspheres were prepared by hydrolysis of titanium tetrabutoxide (TBOT) via sol-gel process in mixed ethanol/acetonitrile solvent, in which the activity of TBOT could be easily controlled. The carboxyl groups on the surface of silica particles promote the formation of a dense and smooth titania layer under well control, and the layer thickness of titania could be tuned from 12 to 100nm. The well-defined h-SiO(2)/TiO(2) core/shell structures have been confirmed by electron microscopy and X-ray photoelectron spectroscopy studies. After calcination at 500°C for 2h, the amorphous TiO(2) layer turned into anatase titania. These anatase titania-coated silica particles showed good photocatalytic performance in degradation of methyl orange aqueous solution under UV light.
Key Laboratory of Molecular Engineering of Polymers (Minister of Education), Department of Macromolecular Science and Laboratory of Advanced Materials, Fudan University, Shanghai 200433, People's Republic of China.
Zhe-Ying
ZY
Shen
Long-Yu
LY
Li
Yat
Y
Li
Chang-Chun
CC
Wang