Electron-beam-initiated polymerization of poly(ethylene glycol)-based wood impregnants.
The current study demonstrates that methacrylate and acrylate poly(ethylene glycol) (PEG) functional oligomers can be effectively impregnated into wood blocks, and cured efficiently to high conversions without catalyst by e-beam radiation, allowing for less susceptibility to leaching, and favorable properties including higher Brinell hardness values. PEG based monomers were chosen because there is a long history of this water-soluble monomer being able to penetrate the cell wall, thus bulking it and decreasing the uptake of water which further protects the wood from fungal attack. Diacrylate, dimethacrylate, and dihydroxyl functional PEG of M(w) 550-575, of concentrations 0, 30, 60, and 100 wt % in water, were vacuum pressure impregnated into Scots Pine blocks of 15 × 25 × 50 mm in an effort to bulk the cell wall. The samples were then irradiated and compared with nonirradiated samples. It was shown by IR, DSC that the acrylate polymers were fully cured to much higher conversions than can be reached with conventional methods. Leaching studies indicated a much lower amount of oligomer loss from the cured vinyl functional PEG chains in comparison to hydroxyl functional PEG indicating a high degree of fastening of the polymer in the wood. The Brinell hardness indicated a significant increase in hardness to hardwood levels in the modified samples compared to the samples of hydroxyl functional PEG and uncured vinyl PEG samples, which actually became softer than the untreated Scots Pine. By monitoring the dimensions of the sample it was found by weight percent gain calculations (WPG %) that water helps to swell the wood structure and allow better access of the oligomers into the cell wall. Further, the cure shrinkage of the wood samples demonstrated infiltration of the oligomers into the cell wall as this was not observed for methyl methacrylate which is well-documented to remain in the lumen. However, dimensional stability of the vinyl polymer modified blocks when placed in water was not observed to the same extent as PEG.
SP Trätek, SP Technical Research Institute of Sweden, Box 5609, Drottning Kristinas väg 67, SE-114 86, Stockholm, Sweden. Stacy.trey@sp.se
Stacy M
SM
Trey
Julia
J
Netrval
Lars
L
Berglund
Mats
M
Johansson