Design of low cost gas sensor based on SrTiO3 and BaTiO3 films.
We have prepared SrTiO3/BaTiO3 multilayer film on alumina substrates by a sol-gel technique and investigated their response for sensing ethanol vapor. The surface morphology of the films were characterized by atomic force microscope (AFM) showing that the grain size of the films increase up to 40 nm as the annealing temperature increased to 1000 degrees C. The ethanol sensors based on SrTiO3/BaTiO3 thin films were fabricated by applying interdigitated gold electrodes by sputtering technique. The ethanol sensing characteristics of SrTiO3/BaTiO3 thin films were quantified by the change in resistance of the sensors when they were exposed to ethanol. The optimum operating tempearature of these sensors was found to be 350 degrees C. In addition, the film annealed at 1000 degrees C exhibited p-type gas sensing behavior with the best sensitivity of 30-100 for low ethanol concentration in the range of 100-1000 ppm.
Department of Physics, Faculty of Science, Chulalongkorn University, Bangkok, 10330, Thailand.
Satreerat K
SK
Hodak
Thidarat
T
Supasai
Anurat
A
Wisitsoraat
Jose H
JH
Hodak