Structures of Pd(CN)2 and Pt(CN)2: intrinsically nanocrystalline materials?
Analysis and modeling of X-ray and neutron Bragg and total diffraction data show that the compounds referred to in the literature as "Pd(CN)(2)" and "Pt(CN)(2)" are nanocrystalline materials containing small sheets of vertex-sharing square-planar M(CN)(4) units, layered in a disordered manner with an intersheet separation of ~3.44 Å at 300 K. The small size of the crystallites means that the sheets' edges form a significant fraction of each material. The Pd(CN)(2) nanocrystallites studied using total neutron diffraction are terminated by water and the Pt(CN)(2) nanocrystallites by ammonia, in place of half of the terminal cyanide groups, thus maintaining charge neutrality. The neutron samples contain sheets of approximate dimensions 30 Å × 30 Å. For sheets of the size we describe, our structural models predict compositions of Pd(CN)(2)·xH(2)O and Pt(CN)(2)·yNH(3) (x ≈ y ≈ 0.29). These values are in good agreement with those obtained from total neutron diffraction and thermal analysis, and are also supported by infrared and Raman spectroscopy measurements. It is also possible to prepare related compounds Pd(CN)(2)·pNH(3) and Pt(CN)(2)·qH(2)O, in which the terminating groups are exchanged. Additional samples showing sheet sizes in the range ~10 Å × 10 Å (y ~ 0.67) to ~80 Å × 80 Å (p = q ~ 0.12), as determined by X-ray diffraction, have been prepared. The related mixed-metal phase, Pd(1/2)Pt(1/2)(CN)(2)·qH(2)O (q ~ 0.50), is also nanocrystalline (sheet size ~15 Å × 15 Å). In all cases, the interiors of the sheets are isostructural with those found in Ni(CN)(2). Removal of the final traces of water or ammonia by heating results in decomposition of the compounds to Pd and Pt metal, or in the case of the mixed-metal cyanide, the alloy, Pd(1/2)Pt(1/2), making it impossible to prepare the simple cyanides, Pd(CN)(2), Pt(CN)(2), or Pd(1/2)Pt(1/2)(CN)(2), by this method.
Department of Chemistry, University of Reading, Whiteknights, Reading RG6 6AD, UK. s.j.hibble@rdg.ac.uk
Simon J
SJ
Hibble
Ann M
AM
Chippindale
Edward J
EJ
Bilbé
Elena
E
Marelli
Peter J F
PJ
Harris
Alex C
AC
Hannon