Application of TiO2 nanoparticles coated multi-wall carbon nanotube to dye-sensitized solar cells.
This study uses the sol-gel method to prepare TiO2 nanoparticle, and further applies TiO2 nanoparticle coating on the surface of the multi-wall carbon nanotube (MWCNT). As a result, TiO2-CNT composite nanoparticles are prepared to serve as photoelectrode material in dye-sensitized solar cell (DSSC). First, after acid treatment of MWCNT is used to remove impurities. Then, the sol-gel method is employed to prepare TiO2-CNT composite nanopowder. X-ray diffraction (XRD) pattern shows that after the TiO2 in TiO2-CNT composite nanopowder has been thermally treated at 450 degrees C, it can be completely changed to anatase phase. Furthermore, as shown from the SEM image, TiO2 has been successfully coated on CNT. The photoelectrode of DSSC is prepared using the electrophoretic deposition method (EPD) to mix the Degassa P25 TiO2 nanoparticles with TiO2-CNT powder for deposition on the indium tin oxide (ITO) conductive glass. After secondary EPD, a thin film of TiO2/CNTs with thickness 17 microm can be acquired. For the prepared TiO2-CNT composite nanoparticles, since MWCNT can increase the short-circuit current density of DSSC, the light-to-electricity conversion efficiency of DSSC can be effectively increased. Experimental results show that the photoelectric conversion efficiency of DSSC using CNT/TiO2 photoelectrode and N719 dye is increased by 41% from the original 3.45% to 4.87%.
Department of Mechanical Engineering, National Taipei University of Technology, Taipei 10608, Taiwan, China.
Ho
H
Chang
Mu-Jung
MJ
Kao
Kuohsiu-David
KD
Huang
Tung-Jung
TJ
Hsieh
Shu-Hua
SH
Chien