Ferromagnetism driven by oxygen vacancies in SnO2 nanowires.
Room temperature ferromagnetism has been observed in SnO2 nanowires synthesized by a chemical vapor deposition using Au layers as catalyst. The nanowires are homogeneous and single-crystalline grown along the [101] direction, with diameters ranging from 25 to 100 nm and length greater than 20 microm. The special magnetization reaches 0.114 emu/g for the nanowires with diameter of approximately 25 nm and reduces with increasing diameters. Branched SnO2 nanowires were prepared via a two-step vapor-liquid-solid approach, and an enhanced magnetization was obtained. To the contrary, the nanowires annealed at 1300 degrees C in air were completely transformed into the particles and exhibit weakened magnetization. These results demonstrate that the ferromagnetic properties of the samples depend on the surface-to-volume ratio of nanowires. With a combined study of photoluminescence, our results reveal that the oxygen vacancies at the surface of nanowires contribute to the ferromagnetism of SnO2 nanowires. This argument is further confirmed by a sequential annealing in a rich-oxygen atmosphere, then in a low vacuum condition.
Key Laboratory for Magnetism and Magnetic Materials of Ministry of Education, Lanzhou University Lanzhou 730000, China.
Li
L
Zhang
Shihui
S
Ge
Huaxin
H
Zhang
Yalu
Y
Zuo