Integrated microdynamics mechanism of the thermal-induced phase separation behavior of poly(vinyl methyl ether) aqueous solution.
The thermal behavior of a poly(vinyl methyl ether) (PVME) aqueous solution (30 wt %) during a heating-and-cooling cycle is studied using FTIR spectroscopy in combination with 2D correlation analysis. The FTIR spectral data of O-H, CH(3)-O, and C-H stretching vibration regions provide detailed changes of hydrophilic and hydrophobic groups of PVME. Hydrogen bonds between hydrophilic groups and water and hydration interactions between hydrophobic groups and water are confirmed to be completely reversible in the heating-and-cooling cycle. Two-dimensional correlation method helps us to understand the microdynamics mechanism of phase separation behavior of PVME 30 wt % aqueous solution. During the heating process, the initially hydrated CH(3) groups start to dehydrate as the first action of phase separation, and the initially hydrated CH(2) groups follow to start their dehydration; interestingly, water molecules leave CH(2) groups very fast, and the whole dehydration process of CH(2) groups finishes even earlier than that of CH(3). After hydrophobic groups finish their dehydrations, hydrogen bonds between hydrophilic group and water start to dissociate. 1:2 adducts formed between PVME and water dissociate first and transfer to the 1:1 adducts, whereas with further heating, 1:1 adducts eventually dissociate and release free water and free CH(3)-O. PCMW method is used as supplement to determine changing conditions of various chemical structures. During the phase separation, O-H hydrogen bond in 1:2 adduct is found to dissociate between 35.5 and 39 °C in a [Formula: see text] style, whereas the 1:1 adduct (also considered as free water) increases between 35.5 and 39 °C in a [Formula: see text] style. Moreover, dehydration conditions of hydrophobic groups are also found. Both of the dehydrated states CH(3) and CH(2) increase like [Formula: see text].
The Key Laboratory of Molecular Engineering of Polymers, Ministry of Education, Department of Macromolecular Science, and Laboratory of Advanced Materials, Fudan University, Shanghai 200433, People's Republic of China.
Bingjie
B
Sun
Hengjie
H
Lai
Peiyi
P
Wu