Corrosion behaviour and surface analysis of a Co-Cr and two Ni-Cr dental alloys before and after simulated porcelain firing.
This study evaluated the corrosion behaviour and surface properties of a commercial cobalt-chromium (Co-Cr) alloy and two nickel-chromium (Ni-Cr) alloys [beryllium (Be)-free and Be-containing] before and after a simulated porcelain-firing process. Before porcelain firing, the microstructure, surface composition and hardness, electrochemical corrosion properties, and metal-ion release of as-cast alloy specimens were examined. After firing, similar alloy specimens were examined for the same properties. In both as-cast and fired conditions, the Co-Cr alloy (Wirobond C) showed significantly more resistance to corrosion than the two Ni-Cr alloys. After firing, the corrosion rate of the Be-free Ni-Cr alloy (Stellite N9) increased significantly, which corresponded to a reduction in the levels of Cr, molybdenum (Mo), and Ni in the surface oxides and to a reduction in the thickness of the surface oxide film. The corrosion properties of the Co-Cr alloy and the Be-containing Ni-Cr alloy (ChangPing) were not significantly affected by the firing process. Porcelain firing also changed the microstructure and microhardness values of the alloys, and there were increases in the release of Co and Ni ions, especially for Ni from the Be-free Ni-Cr alloy. Thus, the corrosion rate of the Be-free Ni-Cr alloy increased significantly after porcelain firing, whereas the firing process had little effect on the corrosion susceptibility of the Co-Cr alloy and the Be-containing Ni-Cr alloy.
Department of Prosthodontics, Ninth People's Hospital, School of Medicine, Shanghai JiaoTong University, Shanghai, China.
Jing
J
Qiu
Wei-Qiang
WQ
Yu
Fu-Qiang
FQ
Zhang
Roger J
RJ
Smales
Yi-Lin
YL
Zhang
Chun-Hui
CH
Lu
D001608:Beryllium; D002858:Chromium Alloys / Q000737:chemistry*; D003035:Cobalt; D003343:Corrosion; D003735:Dental Casting Technique; D003776:Dental Porcelain / Q000737:chemistry*; D003799:Dental Stress Analysis; D006244:Hardness; D008422:Materials Testing; D016876:Metal Ceramic Alloys / Q000737:chemistry*; D008982:Molybdenum; D009532:Nickel; D010087:Oxides; D056951:Photoelectron Spectroscopy; D012464:Saliva, Artificial; D013499:Surface Properties
D002858:Chromium Alloys; D016876:Metal Ceramic Alloys; D010087:Oxides; D012464:Saliva, Artificial; C403005:nickel-chromium-beryllium alloy; D003776:Dental Porcelain; D003035:Cobalt; D009532:Nickel; D008982:Molybdenum; D001608:Beryllium