title: Magnetic properties, phase evolution, and microstructure of melt spun Hf-substituted Sm(Co0.97Hf0.03)(x)Cy (x = 5-9; y = 0-0.1) nanocomposites.
abstract: Magnetic properties, phase evolution, and microstructure of melt spun Hf-substituted Sm(Co0.97Hf0.03)(x)Cy (x = 5-9; y = 0-0.1) ribbons quenched at the wheel speed of 40 m/s are investigated. X-ray diffraction analysis shows that the main phases existed in Sm(Co0.97Hf0.03)(x) ribbons are 1:5 phase for x = 5-5.5; 1:5 and 1:7 phases for x = 6; 1:7 phase for x = 6.5-7.5; 1:7 and 2:17 phases for x = 8; and only 2:17 phase for x = 8.5-9, respectively. For Sm(Co0.97Hf0.03)(x) (x = 5-9) ribbons, the optimum magnetic properties of B(r) = 5.6 kG, (i)H(c)= 15.6 kOe and (BH)(max) = 7.1 MGOe are obtained for Sm(Co0.97Hf0.03)6.5 ribbons. Furthermore, a slight amount of C addition in Sm(Co0.97Hf0.03)(x) ribbons slightly modify phase constitution and effectively refine the grain size from 200-700 nm for C free ribbons to 10-70 nm, strengthening the exchange coupling effect between magnetic grains of the ribbons. As a result, magnetic properties are further improved. The magnetic properties of B(r) = 6.9 kG, (i)H(c) = 9.2 kOe and (BH)(max) = 10.0 MGOe can be achieved for Sm(Co0.97Hf0.03)7.5C0.1 nanocomposites.
authors: Department of Physics, Tunghai University, Taichung 407, Taiwan.
authors: H W
authors: HW
authors: Chang
authors: C S
authors: CS
authors: Guo
authors: C C
authors: CC
authors: Hsieh
authors: W C
authors: WC
authors: Chang
mesh_terms: D003460:Crystallization / Q000379:methods*; D006358:Hot Temperature; D046911:Macromolecular Substances / Q000737:chemistry; D008280:Magnetics; D008422:Materials Testing; D008968:Molecular Conformation; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure*; D010316:Particle Size; D044367:Phase Transition; D012399:Rotation; D012493:Samarium / Q000737:chemistry*; D013499:Surface Properties
chemical_list: D046911:Macromolecular Substances; D012493:Samarium