title: The structure and photoluminescence properties of Bi2O3-core/SnO2-shell nanowires.
abstract: Bi2O3-core/SnO2-shell nanowires have been prepared by using a two-step process: thermal evaporation of Bi2O3 powders and sputtering of SnO2. The crystalline nature of the Bi2O3-core/SnO2-shell nanowires has been revealed by high resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED). TEM analysis and X-ray diffraction (XRD) results indicate that the Bi2O3-core/SnO2-shell nanowires consist of pure tetragonal alpha-Bi2O3-phase momocrystalline cores and tetragonal SnO2-phase polycrystalline shells. The photoluminescence (PL) measurements show that Bi2O3 nanowires have a broad emission band centered at around 560 nm in the yellow-green region. On the other hand, the Bi2O3-core/SnO2-shell coaxial nanowires with the sputtering times of 4 and 8 min have a blue emission band centered at around 450 nm. In contrast, those with a sputtering time of 10 min have a broad emission band centered at approximately 550 nm again. The origin of this yellow-green emission from the core/shell nanowires, however, quite differs from that from Bi2O3 nanowires, i.e., it is not from the Bi2O3 cores but from the SnO2 shells.
authors: Department of Materials Science and Engineering, Inha University, Incheon 402-751, Republic of Korea.
authors: Changhyun
authors: C
authors: Jin
authors: Hyunsoo
authors: H
authors: Kim
authors: Chongmu
authors: C
authors: Lee