title: Vulcanization characteristics and dynamic mechanical behavior of natural rubber reinforced with silane modified silica.
abstract: Two silane coupling agents were used for hydrolysis-condensation reaction modification of nanosilica surfaces. The surface characteristics were analyzed using Fourier transform infrared spectroscopy (FTIR). The vulcanization kinetics of natural rubber (NR) + silica composites was studied and compared to behavior of the neat NR using differential scanning calorimetry (DSC) in the dynamic scan mode. Dynamic mechanical analysis (DMA) was performed to evaluate the effects of the surface modification. Activation energy E(a) values for the reaction are obtained. The presence of silica, modified or otherwise, inhibits the vulcanization reaction of NR. The neat silica containing system has the lowest cure rate index and the highest activation energy for the vulcanization reaction. The coupling agent with longer chains causes more swelling and moves the glass transition temperature T(g) downwards. Below the glass transition region, silica causes a lowering of the dynamic storage modulus G', a result of hindering the cure reaction. Above the glass transition, silica-again modified or otherwise-provides the expected reinforcement effect.
authors: Department of Chemistry, Faculty of Science, King Mongkut's University of Technology Thonburi, Bangmod, Toongkru, Bangkok 10140, Thailand.
authors: Wunpen
authors: W
authors: Chonkaew
authors: Withawat
authors: W
authors: Minghvanish
authors: Ulchulee
authors: U
authors: Kungliean
authors: Nutthaya
authors: N
authors: Rochanawipart
authors: Witold
authors: W
authors: Brostow
mesh_terms: D055119:Elastic Modulus; D006244:Hardness; D008422:Materials Testing; D044367:Phase Transition; D012408:Rubber / Q000737:chemistry*; D012821:Silanes / Q000737:chemistry*; D012822:Silicon Dioxide / Q000737:chemistry*; D013499:Surface Properties
chemical_list: D012821:Silanes; D012822:Silicon Dioxide; D012408:Rubber