title: A high-resolution core-level photoemission study of the Au/4H-SiC(0001)-([Formula: see text]) interface.
abstract: We present a systematic study of different reconstructions obtained after deposition of Au on the [Formula: see text]-4H-SiC(0001) surface. For 1-2 monolayers (ML) Au and annealing temperature T(anneal)∼675 °C, a 3 × 3 reconstruction was observed. For 4 ML Au and T(anneal)∼650 °C, a [Formula: see text] reconstruction appeared, while 5 ML Au annealed at 700 °C reconstructed to give a [Formula: see text] pattern. From the Si 2p and Au 4f core-level components, we propose interface models, depending on the amount of Au on the surface and the annealing temperature. For 1-4 ML Au annealed at 650-675 °C, gold diffuses under the topmost Si into the SiC and forms a silicide. An additional Si component in our Si 2p spectra is related to the interface between the silicide and SiC. For 5 ML Au annealed at 700 °C, silicide is also formed at the surface, covering unreacted Au on top of the SiC substrate. The interface Si component is also observed in the Si 2p spectra of this surface. The key role in [Formula: see text]-4H-SiC(0001) interface formation is played by diffusion and the silicon-richness of the surface.
authors.affiliation: Materialfysik, MAP, KTH-Electrum, SE-16440 Kista, Sweden.
authors.forename: D
authors.initials: D
authors.lastname: Stoltz
authors.forename: S E
authors.initials: SE
authors.lastname: Stoltz
authors.forename: L S O
authors.initials: LS
authors.lastname: Johansson