title: Temperature- and photo-excitation effects on the electrical properties of Tl(4)Se(3)S crystals.
abstract: The extrinsic energy states and the recombination mechanism in the Tl(4)Se(3)S chain crystals are being investigated by means of electrical and photoelectrical measurements for the first time. The electrical resistivity is observed to decrease exponentially with increasing temperature. The analysis of this dependence revealed three impurity levels located at 280, 68 and 48 meV. The photocurrent is observed to increase as temperature decreases down to a minimum temperature T(m) = 200 K. Below this temperature the photocurrent decreases upon temperature lowering. Two photoconductivity activation energies of 10 and 100 meV were determined for the temperature ranges below and above T(m), respectively. The photocurrent (I(ph)) versus illumination intensity (F) dependence follows the [Formula: see text] law. The value of γ decreases from ∼1.0 at 300 K to ∼0.34 at 160 K. The change in the value of γ with temperature is attributed to the exchange of roles between the monomolecular recombination at the surface near room temperature and trapping centers in the crystal, which become dominant as temperature decreases.
authors.affiliation: Group of Physics, Faculty of Engineering, Atilim University, 06836 Ankara, Turkey. Department of Physics, Arab-American University, Jenin, West Bank, Palestine.
authors.forename: A F
authors.initials: AF
authors.lastname: Qasrawi
authors.forename: N M
authors.initials: NM
authors.lastname: Gasanly