Chipping resistance of graded zirconia ceramics for dental crowns.
A serious drawback of veneering porcelains is a pronounced susceptibility to chipping. Glass-infiltrated dense zirconia structures can now be produced with esthetic quality, making them an attractive alternative. In this study, we examined the hypothesis that such infiltrated structures are much more chip-resistant than conventional porcelains, and at least as chip-resistant as non-infiltrated zirconia. A sharp indenter was used to produce chips in flat and anatomically correct glass-infiltrated zirconia crown materials, and critical loads were measured as a function of distance from the specimen edge (flat) or side wall (crown). Control data were obtained on zirconia specimens without infiltration and on crowns veneered with porcelains. The results confirmed that the resistance to chipping in graded zirconia is more than 4 times higher than that of porcelain-veneered zirconia and is at least as high as that of non-veneered zirconia.
New York University College of Dentistry, Department of Biomaterials and Biomimetics, 345 East 24th Street, Room 813C, New York, NY 10010, USA. yz21@nyu.edu
Y
Y
Zhang
H
H
Chai
J J-W
JJ
Lee
B R
BR
Lawn
D003116:Color; D003442:Crowns; D003776:Dental Porcelain; D019232:Dental Restoration Failure; D003799:Dental Stress Analysis; D003801:Dental Veneers; D005898:Glass; D006801:Humans; D008422:Materials Testing; D015040:Zirconium / Q000737:chemistry
D003776:Dental Porcelain; D015040:Zirconium; C028541:zirconium oxide