Pt-Al2O3 interfacial bonding in implantable hermetic feedthroughs: morphology and orientation.
The present work examines the chemistry, microstructure, and crystallography of a Pt-Al(2)O(3) joint used in implantable hermetic feedthrough designs in neural prostheses. Pt was joined to Al(2)O(3) by passing Pt pins through green Al(2)O(3) disks and then sintering in air. This created a Pt-Al(2)O(3) joint that was prepared for the current investigation by gross sectioning and then polishing and sectioning into slices using focused ion beam milling. The slices were examined by scanning electron microscopy, transmission electron microscopy, and energy dispersive spectroscopy. Two types of interfaces in the sintered material were identified: Vitreous-bonded Pt-glass-Al(2)O(3) and direct-bonded Pt-Al(2)O(3). In the case of the former, glass formation owing to the presence of glass-forming additives (to enhance densification and suppress grain growth) and consequent wetting of both the Pt and Al(2)O(3) facilitated interfacial bonding. In the case of the latter, the interfacial planes were (002)(Pt) // (022)Al(2)O(3) [rhombohedral] or (002)(Pt) // (022 2)Al(2)O(3) [hexagonal]. The lattice mismatch was calculated to be 11% (based on the calculated d spacings) or 15% (based on the literature d spacings). Both of these suggest the establishment of semicoherent interfaces.
Cochlear Limited, Sydney, New South Wales 2109, Australia. lhong@cochlear.com.au
Hong
H
Lu
Martin Joseph
MJ
Svehla
Mike
M
Skalsky
Charlie
C
Kong
Charles Christopher
CC
Sorrell
D000537:Aluminum Oxide / Q000737:chemistry*; D005898:Glass / Q000737:chemistry; D010984:Platinum / Q000737:chemistry*; D019736:Prostheses and Implants / Q000648:ultrastructure*
D010984:Platinum; D000537:Aluminum Oxide