Resistance to bond degradation between dual-cure resin cements and pre-treated sintered CAD-CAM dental ceramics.
OBJECTIVE
To evaluate the bond stability of resin cements when luted to glass-reinforced alumina and zirconia CAD/CAM dental ceramics.


METHODS
Eighteen glass-infiltrated alumina and eighteen densely sintered zirconia blocks were randomly conditioned as follows: Group 1: No treatment; Group 2: Sandblasting (125 µm Al₂O₃-particles); and Group 3: Silica-coating (50 µm silica-modified Al₂O₃-particles). Composite samples were randomly bonded to the pretreated ceramic surfaces using different resin cements: Subgroup 1: Clearfil Esthetic Cement (CEC); Subgroup 2: RelyX Unicem (RXU); and Subgroup 3: Calibra (CAL). After 24 h, bonded specimens were cut into 1 ± 0.1 mm² sticks. One-half of the beams were tested for microtensile bond strength (MTBS). The remaining one-half was immersed in 10 % NaOCl aqueous solution (NaOClaq) for 5 h before testing. The fracture pattern and morphology of the debonded surfaces were assessed with a field emission gun scanning electron microscope (FEG-SEM). A multiple ANOVA was conducted to analyze the contributions of ceramic composition, surface treatment, resin cement type, and chemical challenging to MTBS. The Tukey test was run for multiple comparisons (p < 0.05).


RESULTS
After 24 h, CEC luted to pre-treated zirconia achieved the highest MTBS. Using RXU, alumina and zirconia registered comparable MTBS. CAL failed prematurely, except when luted to sandblasted zirconia. After NaOClaq storage, CEC significantly lowered MTBS when luted to zirconia or alumina. RXU decreased MTBS only when bonded to silica-coated alumina. CAL recorded 100 % of pre-testing failures. Micromorphological alterations were evident after NaOClaq immersion.


CONCLUSIONS
Resin-ceramic interfacial longevity depended on cement selection rather than on surface pre-treatments. The MDP-containing and the self-adhesive resin cements were both suitable for luting CAD/CAM ceramics. Despite both cements being prone to degradation, RXU luted to zirconia or untreated or sandblasted alumina showed the most stable interfaces. CAL experimented spontaneous debonding in all tested groups.
Department of Dental Materials, School of Dentistry, University of Granada, Granada, Spain.
Raquel
R
Osorio
Raquel
R
Castillo-de Oyagüe
Francesca
F
Monticelli
Estrella
E
Osorio
Manuel
M
Toledano
D000537:Aluminum Oxide; D002516:Ceramics; D017076:Computer-Aided Design; D001840:Dental Bonding; D005898:Glass; D008422:Materials Testing; D019279:Resin Cements; D015040:Zirconium
D019279:Resin Cements; D015040:Zirconium; D000537:Aluminum Oxide; C028541:zirconium oxide