Isolation of a thermophilic bacterium capable of low-molecular-weight polyethylene degradation.
A thermophilic bacterium capable of low-molecular-weight polyethylene (LMWPE) degradation was isolated from a compost sample, and was identified as Chelatococcus sp. E1, through sequencing of the 16S rRNA gene. LMWPE was prepared by thermal degradation of commercial PE in a strict nitrogen atmosphere. LMWPE with a weight-average-molecular-weight (Mw) in the range of 1,700-23,700 was noticeably mineralized into CO(2) by the bacterium. The biodegradability of LMWPE decreased as the Mw increased. The low molecular weight fraction of LMWPE decreased significantly as a result of the degradation process, and thereby both the number-average-molecular-weight and Mw increased after biodegradation. The polydispersity of LMWPE was either narrowed or widened, depending on the initial Mw of LMWPE, due to the preferential elimination of the low molecular weight fraction, in comparison to the high molecular weight portion. LMWPE free from an extremely low molecular weight fraction was also mineralized by the strain at a remarkable rate, and FTIR peaks assignable to C-O stretching appeared as a result of microbial action. The FTIR peaks corresponding to alkenes also became more intense, indicating that dehydrogenations occurred concomitantly with microbial induced oxidation.
Department of Life Science, Sangmyung University, Seoul, 110-743, Republic of Korea.
Hyun Jeong
HJ
Jeon
Mal Nam
MN
Kim
D020561:Alphaproteobacteria / Q000235:genetics / Q000302:isolation & purification* / Q000378:metabolism*; D001673:Biodegradation, Environmental; D006358:Hot Temperature; D008970:Molecular Weight; D020959:Polyethylene / Q000737:chemistry / Q000378:metabolism*; D012988:Soil Microbiology
D020959:Polyethylene