Optical properties of electrochemically deposited ZnO thin films on colloidal crystal film of SiO2 microspheres.
The optical properties of electrochemically deposited ZnO thin films on colloidal crystal film of SiO2 microspheres structures were studied. Colloidal crystal film of SiO2 microspheres were self-assembled by evaporation using SiO2 in solution at a constant 0.1 wt%. ZnO in thin films was then electrochemically deposited on to colloidal crystal film of SiO2 microspheres. During electrochemical deposition, the content of Zn(NO3)2 x 6H2O in solution was 5 wt%, and the process's conditions were varied between of 2-4 V and 30-120 s at room temperature, with subsequent heat-treatment between 200 and 400 degrees C. A smooth surface and uniform thickness of 1.8 microm were obtained at 3 V for 90 s. The highest PL peak intensity was obtained in the ZnO thin film heat-treated at 400 degrees C. The double layered ZnO/SiO2 colloidal crystals showed clearly better emission properties than the SiO2/ZnO and ZnO structures.
Department of Advanced Materials Engineering, Chosun University, Gwangju, 501-759, Korea.
Yong Taeg
YT
Oh
Bum Ho
BH
Choi
Dong Chan
DC
Shin