Crystallization of cobalt amorphous alloys under field annealing.
Crystallization of Co-rich amorphous ribbons annealed under a 10 Oe external magnetic field at the early 30 minutes from their glassy status to supercooled liquid status is investigated by high-resolution transmission microscope (HR-TEM), Selected Area Fourier Transform (SA-FT), X-ray diffraction (XRD) and differential scanning calorimetry (DSC). Results indicate that the short-rang ordering feature can be refined very well in specimen annealed under temperatures about 87.4 degrees C below their glass transition (Tg), showing refined salt-pepper morphologies with a mean length changing from 1.2 +/- 0.8 nm to 0.8 +/- 0.2 nm and a mean width shifting from 0.5 +/- 0.2 nm to 0.3 +/- 0.1 nm. When the amorphous ribbons are field-annealed at temperature near to Tg (i.e., 450 degrees C), ultra-fine nanocrystalline structures can be formed on the top surface of ribbons with size of 3.5 +/- 0.5 nm and inter-grain spacing of about 0.4 +/- 0.2 nm even though the inner parts of the ribbons are still in amorphous phases. The nanocrystalline areas are featured by the formation of doped hcp cobalt phase orientated along the c-axis, with the inter-plane spacing ranging from 4 A to 6 A. When the annealing temperature is above Tg, the grain sizes are increased dramatically with multi-phased nanocrystals precipitating from the amorphous substrate, and finally reaching almost complete crystallization at 600 degrees C, causing greatly coarsening of the nanocrystal structures.
Key Laboratory for Aerospace Materials and Performance (Education of Ministry), School of Materials Science and Engineering, Beihang University, Beijing 100191, China.
Yujun
Y
Song
Qiangqiang
Q
Sun
Yanwei
Y
Jiang
Jiancheng
J
Fang
Sansheng
S
Wang
Tao
T
Zhang