Effect of annealing temperature on the structural and magnetic properties of Co-doped TiO2 nanoparticles via complex-polymer sol-gel method.
Co-doped TiO2 nanoparticles were synthesized via non hydrous complex-polymer sol-gel method. A series of Co(x):Ti1-x O2 samples with x = 0.01, 0.03, 0.05, 0.08 and 0.10, were prepared and subsequently annealed at 400 degrees, 600 degrees and 800 degrees C. Structural and magnetic properties of Co(x):Ti1-x O2 have been studied by means of X-ray diffraction and DC magnetometry. All samples annealed at 400 degrees C show a paramagnetic behavior with an average grain size of 11 nm. With increasing annealing temperatures a complete crystallization is seen with growth of the cluster size up to 31 nm with clear evidence of a presence of CoTiO3. For all concentrations and annealing conditions no sign of a metallic phase, even at x = 0.10, is seen.
Department of Material physics, Uppsala University, Box 516, SE-75120, Uppsala, Sweden.
Masoud
M
Karimipour
J Magnus
JM
Wikberg
Nasser
N
Shahtahmasebi
Mahmood Rezaee Rokn
MR
Abad
M M
MM
Bagheri-Mohagheghi
Peter
P
Svedlindh