Fabrication of nano-LaCrO3 receptor by polymeric precursor method and its impedancemetric NOx sensing properties.
LaCrO3 was prepared by using the polymeric precursor method for use as a receptor material and its NOx sensing characteristics were investigated. Nano-LaCrO3 powders were synthesized at the optimum compositions of the mole ratio of [La-, Cr-source]:[EG]:[AcAc] = [a, a]:[160 a]:[8 a] with 1 wt% polyvinylpyrrolidone (PVP) using ethylene glycol (EG) as a solvent, acetyl acetone (AcAc) as a chelating agent, and PVP as a polymer additive. The thermal decomposition behavior, crystal structure, morphology, and particle sizes of nano powders were characterized by a thermal analysis (TG-DTA), X-ray diffraction (XRD), a field emission scanning electron microscopy (FE-SEM), and a particle size analyzer, respectively LaCrO3 powders were mainly orthorhombic in structure and the primary particle size was 30 nm according to the XRD results. All solid-state compact impedancemetric-type sensor devices composed of Li1.5Al0.5Ti1.5(PO4)3 (LATP) as a transducer and a perovskite-type LaCrO3 nano powder as a receptor, have been investigated for their ability to detect NOx (NO and NO2) in the range of 1-250 ppm at 400 degrees C. The sensor device showed high gas sensitivities at NO gas, but relatively low gas sensitivities for NO2 gas.
Department of Materials Engineering, Graduate School of PaiChai University, Daejeon 302-735, Korea.
Young-Sung
YS
Lee
Hong-Chan
HC
Cho
S
S
Takase
Y
Y
Shimizu
Jong-Tae
JT
Baek
Jeong-Hwan
JH
Song