Effect of collector speed and flow rate on morphology of Er doped TiO2 nanofibers.
The 0.5 mol% Er3+ doped TiO2 (Er(3+)-TiO2) nanofibers were synthesized by a sol-gel derived electrospinning and subsequent calcination for 3 h at 500 degrees C in air. The calcined fibers were examined to evaluate the effect of collector speed and flow rate on morphology of the fibers. The dynamic viscosity and surface tension of precursor solution were 34 cP and 22.7 mN/m, respectively. The Er(3+)-TiO2 nanofibers were electrospun horizontally on the drum rotated at 100-500 rpm and flow rate of 0.2-0.5 mL/h under a DC voltage of 10 kV. The grounded collector is a stainless mandrel placed 12 cm away from the tip of the needle. Beads were observed for the nanofibers prepared at flow rates from 0.2 mL/h to 0.5 mL/h when the collector speed was 100 rpm. The nanofibers increased in diameter slightly from 150 nm to 190 nm as the flow rate was raised from 0.2 mLh to 0.5 mL/h. No beads were found at the collector speed of above 300 rpm when the flow rate was 0.2 mL/h. The optimized flow rate and collector speed of the nanofibers were determined to be in the range of 0.2-0.3 mL/h and 300-400 rpm, respectively. Uniform, smooth and continuous fibers with diameters of 150 to 170 nm were detected. Crystallite size determined by the Scherrer formula was about 6 nm. It can be concluded that the collector speed and the flow rate are influential on the morphology of the Er(3+)-TiO2 nanofibers. The Er(3+)-TiO2 nanofibers, prepared at 0.2 mL/h and 300 rpm, had typical absorption peaks located at 490, 523 and 654 nm, corresponding to the transitions from 4I15/2 to 4F7/2, 2H11/2 and 4F9/2, respectively. The Er(3+)-TiO2 nanofibers showed enhanced photoresponses under visible light.
Department of Materials Engineering, Daelim University College, Anyang 431-715, Korea.
Deuk Yong
DY
Lee
Jung-Yeon
JY
Park
Bae-Yeon
BY
Kim
Nam-Ihn
NI
Cho