Characterisation of InAs/GaAs short period superlattices using column ratio mapping in aberration-corrected scanning transmission electron microscopy.
The image processing technique of column ratio mapping was applied to aberration-corrected high angle annular dark field (HAADF) images of short period MBE (molecular beam epitaxy) grown InAs/GaAs superlattices. This method allowed the Indium distribution to be mapped and a more detailed assessment of interfacial quality to be made. Frozen-phonon multislice simulations were also employed to provide a better understanding of the experimental column ratio values. It was established that ultra-thin InAs/GaAs layers can be grown sufficiently well by MBE. This is despite the fact that the Indium segregated over 3-4 monolayers. Furthermore, the effect of the growth temperature on the quality of the layers was also investigated. It was demonstrated that the higher growth temperature resulted in a better quality superlattice structure.
SUPA School of Physics & Astronomy, University of Glasgow, G12 8QQ, UK. paul robb@live.co.uk
Paul D
PD
Robb
Michael
M
Finnie
Alan J
AJ
Craven