Structural modulation in the high capacity battery cathode material LiFeBO3.
The crystal structure of the promising Li-ion battery cathode material LiFeBO(3) has been redetermined based on the results of single crystal X-ray diffraction data. A commensurate modulation that doubles the periodicity of the lattice in the a-axis direction is observed. When the structure of LiFeBO(3) is refined in the 4-dimensional superspace group C2/c(α0γ)00, with α = 1/2 and γ = 0 and with lattice parameters of a = 5.1681 Å, b = 8.8687 Å, c = 10.1656 Å, and β = 91.514°, all of the disorder present in the prior C2/c structural model is eliminated and a long-range ordering of 1D chains of corner-shared LiO(4) is revealed to occur as a result of cooperative displacements of Li and O atoms in the c-axis direction. Solid-state hybrid density functional theory calculations find that the modulation stabilizes the LiFeBO(3) structure by 1.2 kJ/mol (12 meV/f.u.), and that the modulation disappears after delithiation to form a structurally related FeBO(3) phase. The band gaps of LiFeBO(3) and FeBO(3) are calculated to be 3.5 and 3.3 eV, respectively. Bond valence sum maps have been used to identify and characterize the important Li conduction pathways, and suggest that the activation energies for Li diffusion will be higher in the modulated structure of LiFeBO(3) than in its unmodulated analogue.
Department of Chemistry, SUNY Stony Brook, Stony Brook, New York 11794, United States.
Yuri
Y
Janssen
Derek S
DS
Middlemiss
Shou-Hang
SH
Bo
Clare P
CP
Grey
Peter G
PG
Khalifah