Structure and magnetic ordering of the anomalous layered (2D) ferrimagnet [NEt4]2Mn(II)3(CN)8 and 3D bridged-layered antiferromagnet [NEt4]Mn(II)3(CN)7 Prussian blue analogues.
The reaction of Mn(II) and [NEt(4)]CN leads to the isolation of solvated [NEt(4)]Mn(3)(CN)(7) (1) and [NEt(4)](2) Mn(3)(CN)(8) (2), which have hexagonal unit cells [1: R3m, a = 8.0738(1), c = 29.086(1) Å; 2: P3m1, a = 7.9992(3), c = 14.014(1) Å] rather than the face centered cubic lattice that is typical of Prussian blue structured materials. The formula units of both 1 and 2 are composed of one low- and two high-spin Mn(II) ions. Each low-spin, octahedral [Mn(II)(CN)(6)](4-) bonds to six high-spin tetrahedral Mn(II) ions through the N atoms, and each of the tetrahedral Mn(II) ions are bound to three low-spin octahedral [Mn(II)(CN)(6)](4-) moieties. For 2, the fourth cyanide on the tetrahedral Mn(II) site is C bound and is terminal. In contrast, it is orientationally disordered and bridges two tetrahedral Mn(II) centers for 1 forming an extended 3D network structure. The layers of octahedra are separated by 14.01 Å (c axis) for 2, and 9.70 Å (c/3) for 1. The [NEt(4)](+) cations and solvent are disordered and reside between the layers. Both 1 and 2 possess antiferromagnetic superexchange coupling between each low-spin (S = 1/2) octahedral Mn(II) site and two high-spin (S = 5/2) tetrahedral Mn(II) sites within a layer. Analogue 2 orders as a ferrimagnet at 27(±1) K with a coercive field and remanent magnetization of 1140 Oe and 22,800 emuOe mol(-1), respectively, and the magnetization approaches saturation of 49,800 emuOe mol(-1) at 90,000 Oe. In contrast, the bonding via bridging cyanides between the ferrimagnetic layers leads to antiferromagnetic coupling, and 3D structured 1 has a different magnetic behavior to 2. Thus, 1 is a Prussian blue analogue with an antiferromagnetic ground state [T(c) = 27 K from d(χT)/dT].
Department of Chemistry, 315 S. 1400 E. RM 2124, University of Utah, Salt Lake City, Utah 84112-0850, USA.
Christopher M
CM
Kareis
Jae-Hyuk
JH
Her
Peter W
PW
Stephens
Joshua G
JG
Moore
Joel S
JS
Miller