Enhanced photoanodic output at an organic p/n bilayer in the water phase by means of the formation of whiskered phthalocyanine.
The photoelectrode characteristics of an organic p/n bilayer in the water phase were studied with respect to film; 3,4,9,10-perylenetetracarboxylic-bisbenzimidazole (PTCBI, an n-type semiconductor) was used in combination with 29H,31H-phthalocyanine (H₂Pc, a p-type semiconductor). When H₂Pc was vapor-deposited on top of the PTCBI layer on a heated substrate (cf. degree of pressure, ca. 5.0 × 10⁻⁴ Pa; temperature at the substrate, 120°C), a transmission electron microscopic image showed an enhanced contact area of the p/n interface in comparison with that prepared at r.t., due to the formation of a whisker H₂Pc. The PTCBI/H₂Pc bilayer can work as a photoanode along with photophysical events in its interior. The rate-limiting charge transfer at the H₂Pc/water interface was kinetically analyzed assuming the Langmuir adsorption equilibrium at that interface. Kinetic analysis demonstrated that the increased contact area can successfully lead to efficient photoinduced carrier generation; particularly, when a thick whisker of H₂Pc was formed, the magnitude of the oxidation kinetics at the H₂Pc/water interface was approximately 2.5 times higher than that without thermal treatment.
Department of Frontier Materials Chemistry, Graduate School of Science and Technology, Hirosaki University, 3 Bunkyo-cho, Hirosaki 036-8561, Japan. tabe@cc.hirosaki-u.ac.jp
Toshiyuki
T
Abe
Yoshinori
Y
Tanno
Toshihiro
T
Ebina
Shouichi
S
Miyakushi
Keiji
K
Nagai