A copper-deficient tetragonal phase derived from chalcopyrite CuGaS2.
Direct synthesis of CuGaS(2) from elemental ingredients in a two-zone furnace resulted in a macroseparation of Cu-rich and Ga-rich regions over the crystallization volume. In the Cu-rich parts of the ingot, a near-stoichiometric CuGaS(2) chalcopyrite phase (I42d) and copper sulfides were found. In the Ga-rich part, along with a chalcopyrite phase with some Cu deficiency, a new tetragonal phase I4m2 with composition close to Cu(5)Ga(9)S(16) and the crystal lattice parameters a = 3.7777(2) Å, c = 5.2483(4) Å was revealed. It was concluded that this Cu-deficient chalcopyrite-like phase is not an ordered defect compound (ODC). As opposed to the systems Cu-Ga-Se and Cu-Ga-Te, in a system based on sulfur, the ODC phenomenon is unlikely to occur.
Department of Materials and Ceramic Engineering/CICECO, University of Aveiro, 3810-193 Aveiro, Portugal. salak@ua.pt
A N
AN
Salak
A L
AL
Zhaludkevich
B V
BV
Korzun
A D
AD
Lisenkov
M L
ML
Zheludkevich
D003300:Copper / Q000737:chemistry / Q000172:deficiency*; D003460:Crystallization; D005708:Gallium / Q000737:chemistry*; D008958:Models, Molecular; D013440:Sulfides / Q000737:chemistry*
D013440:Sulfides; C012819:chalcopyrite; D003300:Copper; D005708:Gallium