Synthesis of soluble poly-yne polymers containing zirconium and silicon and corresponding conversion to nanosized ZrC/SiC composite ceramics.
Soluble organometallic polymers containing zirconium and silicon were synthesized by a salt metathesis reaction. The molecular weight of the polymers was measured by GPC and the corresponding structures were identified by (13)C NMR and FT-IR. After heat treatment of the polymers under argon at 1400 °C for 2 h, ZrC/SiC composites with different molar ratios of crystalline phases were obtained and characterized by XRD, elemental analysis, SEM and Raman spectroscopy. The crystalline size of the composites was approximately 100 nm-200 nm and the elements were well distributed at the different sites in the ceramics. The Raman results indicated that the ceramic residue could be considered as ZrC/SiC/C ternary composites.
Laboratory of Advanced Polymer Materials, Center for Molecular Science, Institute of Chemistry, Chinese Academy of Science, Beijing 100190, People's Republic of China.
Tao
T
Cai
Wen-Feng
WF
Qiu
Dan
D
Liu
Wei-Jian
WJ
Han
Li
L
Ye
Ai-Jun
AJ
Zhao
Tong
T
Zhao