The importance of intrinsic damage properties to bone fragility: a finite element study.
As the average age of the population has increased, the incidence of age-related bone fracture has also increased. While some of the increase of fracture incidence with age is related to loss of bone mass, a significant part of the risk is unexplained and may be caused by changes in intrinsic material properties of the hard tissue. This investigation focused on understanding how changes to the intrinsic damage properties affect bone fragility. We hypothesized that the intrinsic (μm) damage properties of bone tissue strongly and nonlinearly affect mechanical behavior at the apparent (whole tissue, cm) level. The importance of intrinsic properties on the apparent level behavior of trabecular bone tissue was investigated using voxel based finite element analysis. Trabecular bone cores from human T12 vertebrae were scanned using microcomputed tomography (μCT) and the images used to build nonlinear finite element models. Isotropic and initially homogenous material properties were used for all elements. The elastic modulus (E(i)) of individual elements was reduced with a secant damage rule relating only principal tensile tissue strain to modulus damage. Apparent level resistance to fracture as a function of changes in the intrinsic damage properties was measured using the mechanical energy to failure per unit volume (apparent toughness modulus, W(a)) and the apparent yield strength (σ(ay), calculated using the 0.2% offset). Intrinsic damage properties had a profound nonlinear effect on the apparent tissue level mechanical response. Intrinsic level failure occurs prior to apparent yield strength (σ(ay)). Apparent yield strength (σ(ay)) and toughness vary strongly (1200% and 400%, respectively) with relatively small changes in the intrinsic damage behavior. The range of apparent maximum stresses predicted by the models was consistent with those measured experimentally for these trabecular bone cores from the experimental axial compressive loading (experimental: σ(max) = 3.0-4.3 MPa; modeling: σ(max) = 2-16 MPa). This finding differs significantly from previous studies based on nondamaging intrinsic material models. Further observations were that this intrinsic damage model reproduced important experimental apparent level behaviors including softening after peak load, microdamage accumulation before apparent yield (0.2% offset), unload softening, and sensitivity of the apparent level mechanical properties to variability of the intrinsic properties.
Lawrence J. Ellison Musculoskeletal Research Center, Department of Orthopaedic Surgery, University of California, Davis, Sacramento, CA 95817, USA.
M R
MR
Hardisty
R
R
Zauel
S M
SM
Stover
D P
DP
Fyhrie
D001696:Biomechanical Phenomena; D001842:Bone and Bones / Q000166:cytology* / Q000293:injuries* / Q000473:pathology; D020342:Finite Element Analysis; D050723:Fractures, Bone / Q000473:pathology; D006801:Humans; D008297:Male; D008422:Materials Testing; D055595:Mechanical Phenomena; D017711:Nonlinear Dynamics; D012306:Risk; D013131:Spine / Q000166:cytology / Q000473:pathology