Seed-mediated synthesis of single-crystal gold nanospheres with controlled diameters in the range 5-30 nm and their self-assembly upon dilution.
Single-crystal gold nanospheres with controlled diameters in the range 5-30 nm were synthesized by using a facile approach that was based on successive seed-mediated growth. The key to the success of this synthesis was the use of hexadecyltrimethylammonium chloride (CTAC) as a capping agent and a large excess of ascorbic acid as a reductant to ensure fast reduction and, thus, single crystallinity and a spherical shape of the resultant nanoparticles. The diameters of the gold nanospheres could be readily controlled by varying the amount of seeds that were introduced into the reaction system. The gold nanospheres could be produced with uniform diameters of up to 30 nm; thus, their localized surface plasmon resonance properties could be directly compared with the results that were obtained from theoretical calculations. Interestingly, we also found that these gold nanospheres self-assembled into dimers, larger aggregates, and wavy nanowires when they were collected by centrifugation, dispersed in deionized water, and then diluted to different volumes with deionized water.
School of Chemistry and Biochemistry, Georgia Institute of Technology, Atlanta, GA 30332, USA.
Yiqun
Y
Zheng
Yanyun
Y
Ma
Jie
J
Zeng
Xiaolan
X
Zhong
Mingshang
M
Jin
Zhi-Yuan
ZY
Li
Younan
Y
Xia
D001205:Ascorbic Acid / Q000737:chemistry; D003460:Crystallization; D006046:Gold / Q000737:chemistry*; D053768:Metal Nanoparticles / Q000737:chemistry* / Q000648:ultrastructure; D010084:Oxidation-Reduction; D010316:Particle Size; D000644:Quaternary Ammonium Compounds / Q000737:chemistry
D000644:Quaternary Ammonium Compounds; C514921:hexadecyltrimethylammoniumchloride; D006046:Gold; D001205:Ascorbic Acid