title: Thermal decomposition of [Co(en)3][Fe(CN)6]∙ 2H2O: Topotactic dehydration process, valence and spin exchange mechanism elucidation.
abstract: BACKGROUND
  The Prussian blue analogues represent well-known and extensively studied group of coordination species which has many remarkable applications due to their ion-exchange, electron transfer or magnetic properties. Among them, Co-Fe Prussian blue analogues have been extensively studied due to the photoinduced magnetization. Surprisingly, their suitability as precursors for solid-state synthesis of magnetic nanoparticles is almost unexplored. In this paper, the mechanism of thermal decomposition of [Co(en)3][Fe(CN)6] ∙∙ 2H2O (1a) is elucidated, including the topotactic dehydration, valence and spins exchange mechanisms suggestion and the formation of a mixture of CoFe2O4-Co3O4 (3:1) as final products of thermal degradation.
  
  
  RESULTS
  The course of thermal decomposition of 1a in air atmosphere up to 600°C was monitored by TG/DSC techniques, (57)Fe Mössbauer and IR spectroscopy. As first, the topotactic dehydration of 1a to the hemihydrate [Co(en)3][Fe(CN)6] ∙∙ 1/2H2O (1b) occurred with preserving the single-crystal character as was confirmed by the X-ray diffraction analysis. The consequent thermal decomposition proceeded in further four stages including intermediates varying in valence and spin states of both transition metal ions in their structures, i.e. [Fe(II)(en)2(μ-NC)Co(III)(CN)4], Fe(III)(NH2CH2CH3)2(μ-NC)2Co(II)(CN)3] and Fe(III)[Co(II)(CN)5], which were suggested mainly from (57)Fe Mössbauer, IR spectral and elemental analyses data. Thermal decomposition was completed at 400°C when superparamagnetic phases of CoFe2O4 and Co3O4 in the molar ratio of 3:1 were formed. During further temperature increase (450 and 600°C), the ongoing crystallization process gave a new ferromagnetic phase attributed to the CoFe2O4-Co3O4 nanocomposite particles. Their formation was confirmed by XRD and TEM analyses. In-field (5 K / 5 T) Mössbauer spectrum revealed canting of Fe(III) spin in almost fully inverse spinel structure of CoFe2O4.
  
  
  CONCLUSIONS
  It has been found that the thermal decomposition of [Co(en)3][Fe(CN)6] ∙∙ 2H2O in air atmosphere is a gradual multiple process accompanied by the formation of intermediates with different composition, stereochemistry, oxidation as well as spin states of both the central transition metals. The decomposition is finished above 400°C and the ongoing heating to 600°C results in the formation of CoFe2O4-Co3O4 nanocomposite particles as the final decomposition product.
authors: Regional Centre of Advanced Technologies and Materials & Department of Inorganic Chemistry, Palacký University, Tř, 17. listopadu 12, Olomouc, CZ-77146, Czech Republic.
authors: Zdeněk
authors: Z
authors: Trávníček
authors: Regional Centre of Advanced Technologies and Materials & Department of Physical Chemistry, Palacký University, Tř, 17. listopadu 12, Olomouc, CZ-77146, Czech Republic.
authors: Radek
authors: R
authors: Zbořil
authors: Regional Centre of Advanced Technologies and Materials & Department of Inorganic Chemistry, Palacký University, Tř, 17. listopadu 12, Olomouc, CZ-77146, Czech Republic.
authors: Miroslava
authors: M
authors: Matiková-Maľarová
authors: Regional Centre of Advanced Technologies and Materials & Department of Inorganic Chemistry, Palacký University, Tř, 17. listopadu 12, Olomouc, CZ-77146, Czech Republic.
authors: Bohuslav
authors: B
authors: Drahoš
authors: Department of Inorganic Chemistry, Institute of Chemistry, Faculty of Sciences, P.J. Šafárik University in Košice, Moyzesova 11, Košice, SK-041 54, Slovakia.
authors: Juraj
authors: J
authors: Cernák
keywords: CoFe2O4; Crystal structure; Hexacyanidoferrate; Mössbauer spectroscopy; Nanocomposite particles; Thermal behavior; Topotactic dehydration
references: Inorg Chem. 2004 Nov 15;43(23):7339-45
references: 15530083
references: J Hazard Mater. 2012 May 30;217-218:85-91
references: 22464752
references: Inorg Chem. 2001 Sep 10;40(19):4876-83
references: 11531434
references: Inorg Chem. 2011 Sep 19;50(18):9153-63
references: 21863788
references: Inorg Chem. 2004 Mar 22;43(6):1969-75
references: 15018518
references: Chem Soc Rev. 2011 Jun;40(6):3356-65
references: 21465059
references: Solid State Nucl Magn Reson. 2003 Sep-Nov;24(2-3):163-83
references: 12943912
references: Inorg Chem. 2006 Jan 9;45(1):74-82
references: 16390042
references: Acc Chem Res. 2003 Sep;36(9):692-700
references: 12974652
references: Biosens Bioelectron. 2005 Sep 15;21(3):389-407
references: 16076428
references: J Am Chem Soc. 2011 Mar 16;133(10):3592-600
references: 21341801
references: Chem Commun (Camb). 2010 Feb 21;46(7):1121-3
references: 20126733
references: Inorg Chem. 1999 Oct 4;38(20):4405-4412
references: 11671150
references: Philos Trans A Math Phys Eng Sci. 2008 Jan 13;366(1862):127-38
references: 17875540
references: Inorg Chem. 2009 Jun 1;48(11):4787-97
references: 19382759
references: Inorg Chem. 2009 Apr 20;48(8):3360-70
references: 19361238
references: J Phys Chem B. 2006 Jan 19;110(2):900-6
references: 16471621
references: Inorg Chem. 2009 Apr 20;48(8):3438-52
references: 19361244
references: Inorg Chem. 2002 Nov 4;41(22):5778-86
references: 12401083
references: Chemistry. 2003 Apr 14;9(8):1677-91
references: 12698426
references: J Am Chem Soc. 2011 Aug 31;133(34):13260-3
references: 21809858
references: Acta Crystallogr A. 2008 Jan;64(Pt 1):112-22
references: 18156677
references: Inorg Chem. 2004 Aug 9;43(16):5034-43
references: 15285680
references: Angew Chem Int Ed Engl. 2007;46(13):2152-87
references: 17348074