Electrochemical degradation of chlortetracycline using N-doped Ti/TiO2 photoanode under sunlight irradiations.
The appearance and the persistence of pharmaceutical products in the aquatic environment urgently call for the development of an innovative and practical water treatment technology. This study deals with the development of nanostructured nitrogen-doped TiO2 photoanodes and their subsequent use for chlortetracycline (CTC) photoelectrocatalytic oxidation under visible light. The N-doped TiO2 photoanodes with different nitrogen contents were prepared by means of a radiofrequency magnetron sputtering (RF-MS) process, with the objective to tune shift their optical absorption from the UV towards the visible. The N-doped TiO2 consist of nanostructured anatase phase with average TiO2 nanocrystallite size of 29 nm. The nitrogen doping is clearly shown to produce the desired red shift of the absorption onset of the TiO2 coatings (from ~380 nm to ~550 nm). Likewise, the N-doped TiO2 are found to be highly photo-electroactive not only under the UV light but most interestingly under the visible light as well. Using the optimal N-doped photoanodes, 99.6% of CTC (100 μg/L) was successfully degraded after 180 min of treatment time with a current intensity of 0.6 A. Under these conditions, a relatively high mineralization of CTC (92.5% ± 0.26% of TOC removal and 90.3% ± 1.1% of TN removal) was achieved.
Institut National de la Recherche Scientifique, Centre Eau, Terre et Environnement, 490 rue de la Couronne, Québec, QC G1K 9A9, Canada. Electronic address: rimeh.daghrir@ete.inrs.ca.
Rimeh
R
Daghrir
Patrick
P
Drogui
Nazar
N
Delegan
My Ali
MA
El Khakani
D002384:Catalysis / Q000528:radiation effects; D002751:Chlortetracycline / Q000737:chemistry* / Q000528:radiation effects*; D004560:Electricity; D004563:Electrochemistry / Q000379:methods*; D004566:Electrodes; D009584:Nitrogen / Q000737:chemistry*; D013056:Spectrophotometry, Ultraviolet; D013472:Sunlight; D013997:Time Factors; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction
C009495:titanium dioxide; D014025:Titanium; D009584:Nitrogen; D002751:Chlortetracycline
Chlortetracycline; Magnetron sputtering process; N-doped TiO(2); Photoelectrocatalytic oxidation