Immobilization of simulated radionuclide 133Cs+ by fly ash-based geopolymer.
The recent nuclear leak in Japan once again attracted people's attention to nuclear safety problems. Because of their poor thermal stability, those low-cost materials such as cement and asphalt cannot be used for the solidification of the radioactive wastes. In this work, the solidification behavior of 133Cs(+) by fly ash-based geopolymer was investigated. Leaching tests (carried out in deionized water, sulfuric acid and magnesium sulfate solutions) revealed that the geopolymer solidification had lower cumulative fraction leaching concentration (CFLC) of 133Cs(+) than that of cemented form. The thermal stability (high-temperature and freeze-thaw resistance) and acid-resistance of the geopolymer were also both better than that of cement. The geopolymer solidification block can acquire a compressive strength up to 30 MPa after 2h calcination at 1000 °C. The morphology and mineral phases of the geopolymer and the geopolymer solidification block were characterized by SEM and XRD, and EDX analysis indicated that most of Cs associated with the amorphous geopolymer gel. These results gave encouragement for the idea that the fly ash-based geopolymer could be used as a low-cost and high-efficiency material for the immobilization of radioactive wastes.
State Key Laboratory of Pollution Control and Resource Reuse, and School of the Environment, Nanjing University, Nanjing 210046, PR China.
Qin
Q
Li
Zengqing
Z
Sun
Dejing
D
Tao
Yan
Y
Xu
Peiming
P
Li
Hao
H
Cui
Jianping
J
Zhai
D002588:Cesium Radioisotopes / Q000737:chemistry*; D060729:Coal Ash; D006358:Hot Temperature; D008855:Microscopy, Electron, Scanning; D011108:Polymers / Q000737:chemistry*; D013052:Spectrometry, X-Ray Emission; D014961:X-Ray Diffraction
D002588:Cesium Radioisotopes; D060729:Coal Ash; D011108:Polymers
133Cs(+); Fly ash; Geopolymer; Immobilization; Radioactive waste