Direct metallization local Al-back surface field for high efficiency screen printed crystalline silicon solar cells.
In this paper, we present a detailed study on the local back contact (LBC) formation of rear-surface-passivated silicon solar cells, where both the LBC opening and metallization are realized by one-step alloying of a dot of fine pattern screen-printed aluminum paste with the silicon substrate. Based on energy dispersive spectrometer (EDS) and scanning electron microscopy (SEM) characterizations, we suggest that the aluminum distribution and the silicon concentration determine the local-back-surface-field (Al-p+) layer thickness, resistivity of the Al-p+ and hence the quality of the Al-p+ formation. The highest penetration of silicon concentration of 78.17% in aluminum resulted in the formation of a 5 microm-deep Al-p+ layer, and the minimum LBC resistivity of 0.92 x 10-6 omega cm2. The degradation of the rear-surface passivation due to high temperature of the LBC formation process can be fully recovered by forming gas annealing (FGA) at temperature and hydrogen content of 450 degrees C and 15%, respectively. The application of the optimized LBC of rear-surface-passivated by a dot of fine pattern screen(-) printed aluminum paste resulted in efficiency of up to 19.98% for the p-type czochralski (CZ) silicon wafers with 10.24 cm2 cell size at 649 mV open circuit voltage. By FGA for rear-surface passivation recovery, efficiencies up to 20.35% with a V(OC) of 662 mV, FF of 82%, and J(SC) of 37.5 mA/cm2 were demonstrated.
Applied Optics and Energy Research Group, Korea Institute of Industrial Technology, Gwangju, 500-480, South Korea.
Jonghwan
J
Lee
Cheolmin
C
Park
Vinh Ai
VA
Dao
Youn-Jung
YJ
Lee
Kyungyul
K
Ryu
Gyuho
G
Choi
Bonggi
B
Kim
Minkyu
M
Ju
Chaehwan
C
Jeong
Junsin
J
Yi
D000535:Aluminum / Q000737:chemistry*; D003460:Crystallization / Q000379:methods*; D011211:Electric Power Supplies; D004566:Electrodes; D004867:Equipment Design; D019544:Equipment Failure Analysis; D008422:Materials Testing; D053768:Metal Nanoparticles / Q000737:chemistry* / Q000648:ultrastructure; D010316:Particle Size; D012825:Silicon / Q000737:chemistry*; D012993:Solar Energy
D000535:Aluminum; D012825:Silicon