Fabrication of a Ni nano-imprint stamp for an anti-reflective layer using an anodic aluminum oxide template.
Aluminum anodizing can alter pore diameter, density distribution, periodicity and layer thickness in a controlled way. Because of this property, porous type anodic aluminum oxide (AAO) was used as a template for nano-structure fabrication. The alumina layer generated at a constant voltage increased the pore size from 120 nm to 205 nm according to an increasing process time from 60 min to 150 min. The resulting fabricated AAO templates had pore diameters at or less than 200 nm. Ni was sputtered as a conductive layer onto this AAO template and electroplated using DC and pulse power. Comparing these Ni stamps, those generated from electroplating using on/reverse/off pulsing had an ordered pillar array and maintained the AAO template morphology. This stamp was used for nano-imprinting on UV curable resin coated glass wafer. Surface observations via electron microscopy showed that the nano-imprinted patterned had the same shape as the AAO template. A soft mold was subsequently fabricated and nano-imprinted to form a moth-eye structure on the glass wafer. An analysis of the substrate transmittance using UV-VIS/NIR spectroscopy showed that the transmittance of the substrate with the moth-eye structure was 5% greater that the non-patterned substrate.
School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746, Republic of Korea.
Eun-Mi
EM
Park
Seung-Kyu
SK
Lim
Senug-Hyun
SH
Ra
Su-Jung
SJ
Suh
D000537:Aluminum Oxide / Q000737:chemistry*; D003460:Crystallization / Q000379:methods*; D004566:Electrodes; D004595:Electroplating / Q000379:methods*; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D053768:Metal Nanoparticles / Q000737:chemistry* / Q000648:ultrastructure*; D008968:Molecular Conformation; D054802:Molecular Imprinting / Q000379:methods*; D009532:Nickel / Q000737:chemistry*; D010316:Particle Size; D013499:Surface Properties
D046911:Macromolecular Substances; D009532:Nickel; D000537:Aluminum Oxide