Large stokes shift of Ag doped CdSe quantum dots via aqueous route.
Monodispersed and luminescent Ag-doped CdSe semiconductor quantum dots (d-dots) were synthesized by an aqueous route assisted with electrochemical preparation of Se source with 3-mercaptopropionic acid as stabilizer. The silver dopants were incorporated into the host crystals via cation-exchange mechanism. X-ray diffraction patterns revealed that the as-synthesized CdSe:Ag d-dots were well retained in the zinc blende structure. The CdSe:Ag d-dots that exhibited uniform size distribution and good crystallnity could be observed by High-resolution transmission electron microscopy (HRTEM), with average diameter of 2.7 nm. Successful doping was confirmed by X-ray photoelectron spectroscopy survey spectra. The peculiar Ag-related photoluminescence showed strong intensity, and at the same time, intrinsic band-edge exciton emission of CdSe QDs was suppressed. The dopant emission exhibited larger Stockes shift of - 0.51 eV than that of the band-gap emission, and varied from 546 to 583 nm by changing electrolytic time. Possible radiative recombination mechanism of the aqueous Ag-doped CdSe d-dots was discussed. The results demonstrated that doping can be an effective way to manipulate the optical properties of semiconductor nanocrystals.
School of Material Science and Engineering, Hefei University of Technology, Hefei, Anhui 230009, PR China.
Jian
J
Huang
Yang
Y
Jiang
Hongyan
H
Duan
Chao
C
Liu
Longfei
L
Mi
Xinzheng
X
Lan
Hongyang
H
Zhou
Honghai
H
Zhong