Microscale investigation of arsenic distribution and species in cement product from cement kiln coprocessing wastes.
To improve the understanding of the immobilization mechanism and the leaching risk of Arsenic (As) in the cement product from coprocessing wastes using cement kiln, distribution and species of As in cement product were determined by microscale investigation methods, including electron probe microanalysis (EPMA) and X-ray absorption spectroscopy. In this study, sodium arsenate crystals (Na3AsO412H2O) were mixed with cement production raw materials and calcined to produce cement clinker. Then, clinker was mixed water to prepare cement paste. EPMA results showed that As was generally distributed throughout the cement paste. As content in calcium silicate hydrates gel (C-S-H) was in low level, but higher than that in other cement mineral phases. This means that most of As is expected to form some compounds that disperse on the surfaces of cement mineral phases. Linear combination fitting (LCF) of the X-ray absorption near edge structure spectra revealed that As in the cement paste was predominantly As(V) and mainly existed as Mg3(AsO4)2, Ca3(AsO4)2, and Na2HAsO4.
State Key Laboratory of Environmental Criteria and Risk Assessment, Chinese Research Academy of Environmental Science, Beijing 100012, China.
Yufei
Y
Yang
Jingchuan
J
Xue
Qifei
Q
Huang
D001151:Arsenic / Q000032:analysis* / Q000737:chemistry; D001152:Arsenicals / Q000032:analysis* / Q000737:chemistry; D002119:Calcium Carbonate / Q000737:chemistry; D003252:Construction Materials; D007220:Industrial Waste
D001152:Arsenicals; D007220:Industrial Waste; D002119:Calcium Carbonate; D001151:Arsenic