Sulfur-doped graphene as a potential alternative metal-free electrocatalyst and Pt-catalyst supporting material for oxygen reduction reaction.
In this study, sulfur-doped graphene (S-graphene) was synthesized by thermal treatment of exfoliated graphene under CS2 gas flow. Its electrocatalytic activity as a metal-free catalyst was evaluated and compared with other doped-graphenes and commercial platinum nanoparticles loaded on carbon black (Pt/C) catalysts for oxygen reduction reaction (ORR) in fuel cell cathodes. The resultant S-graphene was shown to act as a viable catalyst for ORR and its limiting current density and durability were improved compared to those of the commercial Pt/C catalyst. The current density at -1.0 V for the commercial Pt/C catalyst, pristine graphene, nitrogen-doped graphene (N-graphene) and S-graphene was 4.7, 0.15, 6.26 and 6.99 mA cm(-2), respectively. The durability of S-graphene (70.3%) was much better compared to commercial Pt/C (37.2%) and N-graphene (67.9%). When S-graphene was used as a supporting material for Pt nanoparticles, its catalytic performance was significantly higher than other Pt catalysts supported on different doped graphenes. Here, we demonstrate that S-graphene can be used as a novel graphene-based efficient metal-free ORR catalyst in fuel cells.
Department of Chemistry and Nano Science, Global Top 5 Program, Division of Molecular and Life Sciences, College of Natural Sciences, Ewha Womans University, 52, Ewhayeondae-gil, Seodaemun-gu, Seoul 120-750, Korea. dhkim@ewha.ac.kr sjkim@ewha.ac.kr.
Ji-eun
JE
Park
Yu Jin
YJ
Jang
Yeo Jin
YJ
Kim
Mi-sun
MS
Song
Seokhyun
S
Yoon
Dong Ha
DH
Kim
Sung-Jin
SJ
Kim