Electro-osmotic drag effect on the methanol permeation for sulfonated poly(ether ether ketone) and nafion 117 membranes.
Electro-osmotic drag effect on the methanol permeation was investigated for sulfonated poly(ether ether ketone) (sPEEK) membrane, and its result was compared with that of Nafion 117 membrane. The electro-osmotic drag coefficient was determined from the limiting current density measured at different temperature. The methanol permeability of sPEEK membrane increased with temperature but its temperature dependence was not as strong as that of Nafion 117 membrane. The methanol permeability or the total methanol flux of Nafion 117 membrane was at least twice higher than that of sPEEK70 membrane (sPEEK membrane with 70% sulfonation degree), as the methanol permeation was highly contributed by the electro-osmotic drag effect. This higher electro-osmotic drag of Nafion 117 membrane is attributed to the bigger ion cluster and waster channel in nanophase and thus more free water absorption than sPEEK membrane.
School of Chemical Engineering, Sungkyunkwan University, Suwon 440-746, Korea.
Nguyen Thi Que
NT
Chi
Byungchan
B
Bae
Dukjoon
D
Kim
D000476:Alkanesulfonates / Q000737:chemistry*; D001577:Benzophenones; D005465:Fluorocarbon Polymers / Q000737:chemistry*; D007659:Ketones / Q000737:chemistry*; D008422:Materials Testing; D008567:Membranes, Artificial; D000432:Methanol / Q000737:chemistry* / Q000302:isolation & purification*; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure*; D009997:Osmotic Pressure; D010316:Particle Size; D010539:Permeability / Q000528:radiation effects; D011092:Polyethylene Glycols / Q000737:chemistry*; D011108:Polymers; D055672:Static Electricity
D000476:Alkanesulfonates; D001577:Benzophenones; D005465:Fluorocarbon Polymers; D007659:Ketones; D008567:Membranes, Artificial; D011108:Polymers; C063834:polyetheretherketone; C040402:perfluorosulfonic acid; D011092:Polyethylene Glycols; D000432:Methanol