Preparation and characterization of novel anion phase change heat storage materials.
In this paper, polyurethane phase change material was successfully prepared with TDI with BDO for hard segments and PEG for soft segments. Moreover, based on this the solid-solid phase change material, A-PCM1030 which can release anions was prepared with the successful addition of anion additives A1030 for the first time. Then the test of the above material was conducted utilizing FT-IR, DSC, TEM, WAXD and Air Ion Detector. The Results indicated that the polyurethane phase change material possesses excellent thermal stability since there was no appearance of liquid leakage and phase separation after 50 times warming-cooling thermal cycles. It also presented reversibility on absorbing and releasing heat. In addition, adding a little A1030 can increase the thermal stability and reduce phase transition temperatures, as well as reduce the undercooling of the polyurethane phase change material. In addition, the anion test results suggested that the supreme amount of anion released by A-PCM1030 could reach 2510 anions/cm3 under dynamic conditions, which is beneficial for human health.
State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, PR China.
Wei
W
Hong
Qingshan
Q
Lil
Jing
J
Sun
Youbo
Y
Di
Zhou
Z
Zhao
Wei'an
W
Yu
Yuan
Y
Qu
TiFeng
T
Jiao
Guowei
G
Wang
Guangzhong
G
Xing
D000838:Anions; D002152:Calorimetry, Differential Scanning; D006358:Hot Temperature; D046529:Microscopy, Electron, Transmission; D017550:Spectroscopy, Fourier Transform Infrared; D013818:Thermogravimetry
D000838:Anions