Fabrication of uniform nanoscale cavities via silicon direct wafer bonding.
Measurements of the heat capacity and superfluid fraction of confined (4)He have been performed near the lambda transition using lithographically patterned and bonded silicon wafers. Unlike confinements in porous materials often used for these types of experiments(3), bonded wafers provide predesigned uniform spaces for confinement. The geometry of each cell is well known, which removes a large source of ambiguity in the interpretation of data. Exceptionally flat, 5 cm diameter, 375 µm thick Si wafers with about 1 µm variation over the entire wafer can be obtained commercially (from Semiconductor Processing Company, for example). Thermal oxide is grown on the wafers to define the confinement dimension in the z-direction. A pattern is then etched in the oxide using lithographic techniques so as to create a desired enclosure upon bonding. A hole is drilled in one of the wafers (the top) to allow for the introduction of the liquid to be measured. The wafers are cleaned(2) in RCA solutions and then put in a microclean chamber where they are rinsed with deionized water(4). The wafers are bonded at RT and then annealed at ~1,100 °C. This forms a strong and permanent bond. This process can be used to make uniform enclosures for measuring thermal and hydrodynamic properties of confined liquids from the nanometer to the micrometer scale.
Department of Physics, The State University of New York at Buffalo.
Stephen R D
SR
Thomson
Justin K
JK
Perron
Mark O
MO
Kimball
Sarabjit
S
Mehta
Francis M
FM
Gasparini
D049329:Nanostructures / Q000737:chemistry*; D036103:Nanotechnology / Q000295:instrumentation* / Q000379:methods*; D012825:Silicon / Q000737:chemistry*
D012825:Silicon