In vitro comparison of flexural strength and elastic modulus of three provisional crown materials used in fixed prosthodontics.
OBJECTIVE
To evaluate and compare the flexural strength and the elastic moduli of three provisional crown materials (methyl methacrylate based autopolymerized resin, bis acryl composite based autopolymerized resin and urethane dimethacrylate based light polymerized resin) after storing in artificial saliva and testing at intervals of 24 hours and 7 days.


METHODS
A metal master mould with four slots of dimensions 25x2x2 mm was fabricated to obtain samples of standard dimensions. A total of 135 specimens were thus obtained with 45 each of three provisional materials. Further 15 samples of each group were tested after storing for one hour at room temperature and again at intervals of 24 hours and 7 days after storing in artificial saliva. Three point flexural tests were carried out in the universal testing machine to calculate the flexural strength and the elastic modulus. The changes were calculated and data was analyzed with Fisher's test and ANOVA.


RESULTS
The flexural strength of the methyl methacrylate resin reduced significantly while bis-acrylic composite resin showed a significant increase in its flexural strength after storing in artificial saliva for 24 hours and the values of both remained constant thereafter. Contrary to these findings, light polymerized resin showed a significant decrease in flexural strength after storing in artificial saliva for 24 hours and then significantly increased in flexural strength after 7 days. However the changes in the values for elastic modulus of respective materials were statistically insignificant.


CONCLUSIONS
Methacrylate based autopolymerizing resin showed the highest flexural strength and elastic moduli after fabrication and after storing in artificial saliva and for 24 hours and 7 days. Bis-acrylic composite resin showed the least flexural strength and elastic moduli. Key words:Provisional restorations, interim restorations, Methyl Methacrylate, composite restoration, flexural strength, elastic moduli.
MDS, Senior Lecturer. Dept. of Prosthodontics, Coorg Institute of Dental Sciences, Virajpet, S-Coorg, Karnataka India.
Vachan
V
Poonacha
MDS, Senior Lecturer. Dept. of Conservative Dentistry And Endodontics, Coorg Institute of Dental Sciences, Virajpet, S-Coorg, Karnataka India.
Seema
S
Poonacha
MDS, Professor- Dept. of Prosthodontics, Coorg Institute of Dental Sciences, Virajpet, S-Coorg, Karnataka, India.
Basavaraj
B
Salagundi
MDS, Professor and Head. Dept. of Prosthodontics, Coorg Institute of Dental Sciences, Virajpet, S-Coorg, Karnataka, India.
P L
PL
Rupesh
MDS, Professor- Dept. of Prosthodontics, Coorg Institute of Dental Sciences, Virajpet, S-Coorg, Karnataka, India.
Rohit
R
Raghavan