Spark plasma sintering of Mn-Al-C hard magnets.
Structural and magnetic characterization of isotropic Mn-Al-C bulk samples obtained by spark plasma sintering (SPS) is reported. This technique, to the best of our knowledge, has not been used for preparation of Mn-Al-based permanent magnets previously. Transformation from the parent -phase to the ferromagnetic τ-phase occurred on heating in the process of sintering. The phase constitution of the melt-spun precursors and consolidated samples was determined by x-ray diffraction. Magnetic hysteresis loops were recorded using a vibrating sample magnetometer. The compositional dependence of the coercivity, magnetization and density of the sintered materials is analysed. To combine good magnetic properties with proper densification, further optimization of the production parameters is necessary.
A
A
Pasko
M
M
LoBue
E
E
Fazakas
L K
LK
Varga
F
F
Mazaleyrat
D000497:Alloys / Q000737:chemistry*; D000535:Aluminum / Q000737:chemistry*; D002244:Carbon / Q000737:chemistry*; D006244:Hardness; D060328:Magnetic Phenomena; D059346:Magnets / Q000737:chemistry*; D008345:Manganese / Q000737:chemistry*; D058626:Plasma Gases / Q000737:chemistry*; D013696:Temperature
D000497:Alloys; D058626:Plasma Gases; D008345:Manganese; D002244:Carbon; D000535:Aluminum