Property-based design: optimization and characterization of polyvinyl alcohol (PVA) hydrogel and PVA-matrix composite for artificial cornea.
Each approach for artificial cornea design is toward the same goal: to develop a material that best mimics the important properties of natural cornea. Accordingly, the selection and optimization of corneal substitute should be based on their physicochemical properties. In this study, three types of polyvinyl alcohol (PVA) hydrogels with different polymerization degree (PVA1799, PVA2499 and PVA2699) were prepared by freeze-thawing techniques. After characterization in terms of transparency, water content, water contact angle, mechanical property, root-mean-square roughness and protein adsorption behavior, the optimized PVA2499 hydrogel with similar properties of natural cornea was selected as a matrix material for artificial cornea. Based on this, a biomimetic artificial cornea was fabricated with core-and-skirt structure: a transparent PVA hydrogel core, surrounding by a ringed PVA-matrix composite skirt that composed of graphite, Fe-doped nano hydroxyapatite (n-Fe-HA) and PVA hydrogel. Different ratio of graphite/n-Fe-HA can tune the skirt color from dark brown to light brown, which well simulates the iris color of Oriental eyes. Moreover, morphologic and mechanical examination showed that an integrated core-and-skirt artificial cornea was formed from an interpenetrating polymer network, no phase separation appeared on the interface between the core and the skirt.
Department of Biomedical Materials Science, School of Biomedical Engineering, Third Military Medical University, Chongqing, 400038, People's Republic of China.
Hong
H
Jiang
Yi
Y
Zuo
Li
L
Zhang
Jidong
J
Li
Aiming
A
Zhang
Yubao
Y
Li
Xiaochao
X
Yang
D001187:Artificial Organs; D040761:Biomimetic Materials / Q000138:chemical synthesis*; D019245:Compressive Strength; D003315:Cornea; D016039:Corneal Transplantation / Q000295:instrumentation*; D019544:Equipment Failure Analysis; D006244:Hardness; D006801:Humans; D020100:Hydrogels / Q000737:chemistry*; D008422:Materials Testing; D008968:Molecular Conformation; D011142:Polyvinyl Alcohol / Q000737:chemistry*; D011474:Prosthesis Design; D012031:Refractometry; D013499:Surface Properties
D020100:Hydrogels; D011142:Polyvinyl Alcohol