Anisotropic local physical properties of human dental enamel in comparison to properties of some common dental filling materials.
OBJECTIVE
A major aspect in evaluating the quality of dental materials is their physical properties. Their properties should be a best fit of the ones of dental hard tissues. Manufacturers give data sheets for each material. The properties listed are characterized by a specific value. This assumes (but does not prove) that there is no direction dependence of the properties. However, dental enamel has direction-dependent properties which additionally vary with location in the tooth. The aim of this paper is to show the local direction dependence of physical properties like the elastic modulus or the thermal expansion in dental hard tissues. With this knowledge the 'perfect filling/dental material' could be characterized.


METHODS
Enamel sections of ∼400-500 μm thickness have been cut with a diamond saw from labial/buccal to palatal/lingual (canine, premolar and molar) and parallel to labial (incisor). Crystallite arrangements have been measured in over 400 data points on all types of teeth with x-ray scattering techniques, known from materials science.


RESULTS
X-ray scattering measurements show impressively that dental enamel has a strong direction dependence of its physical properties which also varies with location within the tooth. Dental materials possess only little or no property direction dependence. Therefore, a mismatch was found between enamel and dental materials properties.


CONCLUSIONS
Since dental materials should possess equal (direction depending) properties, worthwhile properties could be characterized by transferring the directional properties of enamel into a property 'wish list' which future dental materials should fulfil. Hereby the 'perfect dental material' can be characterized.
Department of Prosthodontics, Center for Dentistry, Oral Medicine and Craniomaxillofacial Surgery, University Clinical Center, Georg-August-University , Goettingen , Germany.
Lars
L
Raue
Christiane D
CD
Hartmann
Matthias
M
Rödiger
Ralf
R
Bürgers
Nikolaus
N
Gersdorff
D016880:Anisotropy; D001641:Bicuspid / Q000737:chemistry; D001696:Biomechanical Phenomena; D003461:Crystallography; D003481:Cuspid / Q000737:chemistry; D003743:Dental Enamel / Q000737:chemistry*; D003764:Dental Materials / Q000737:chemistry*; D055119:Elastic Modulus; D006244:Hardness; D006801:Humans; D007180:Incisor / Q000737:chemistry; D008422:Materials Testing; D008963:Molar / Q000737:chemistry; D012542:Scattering, Radiation; D013816:Thermodynamics; D014965:X-Rays
D003764:Dental Materials
dental enamel; dental material; direction dependence; elastic modulus; thermal expansion