[Mechanical properties of polylactic acid/beta-tricalcium phosphate composite scaffold with double channels based on three-dimensional printing technique].
OBJECTIVE
To improve the poor mechanical strength of porous ceramic scaffold, an integrated method based on three-dimensional (3-D) printing technique is developed to incorporate the controlled double-channel porous structure into the polylactic acid/beta-tricalcium phosphate (PLA/beta-TCP) reinforced composite scaffolds (double-channel composite scaffold) to improve their tissue regeneration capability and the mechanical properties.


METHODS
The designed double-channel structure inside the ceramic scaffold consisted of both primary and secondary micropipes, which parallel but un-connected. The set of primary channels was used for cell ingrowth, while the set of secondary channels was used for the PLA perfusion. Integration technology of 3-D printing technique and gel-casting was firstly used to fabricate the double-channel ceramic scaffolds. PLA/beta-TCP composite scaffolds were obtained by the polymer gravity perfusion process to pour PLA solution into the double-channel ceramic scaffolds through the secondary channel set. Microscope, porosity, and mechanical experiments for the standard samples were used to evaluate the composite properties. The ceramic scaffold with only the primary channel (single-channel scaffold) was also prepared as a control.


RESULTS
Morphology observation results showed that there was no PLA inside the primary channels of the double-channel composite scaffolds but a dense interface layer between PLA and beta-TCP obviously formed on the inner wall of the secondary channels by the PLA penetration during the perfusion process. Finite element simulation found that the compressive strength of the double-channel composite scaffold was less than that of the single-channel scaffold; however, mechanical tests found that the maximum compressive strength of the double-channel composite scaffold [(21.25 +/- 1.15) MPa] was higher than that of the single-channel scaffold[ (9.76 +/- 0.64) MPa].


CONCLUSIONS
The double-channel composite scaffolds fabricated by 3-D printing technique have controlled complex micropipes and can significantly enhance mechanical properties, which is a promising strategy to solve the contradiction of strength and high-porosity of the ceramic scaffolds for the bone tissue engineering application.
Qin
Q
Lian
Pei
P
Zhuang
Changhai
C
Li
Zhongmin
Z
Jin
Dichen
D
Li
D001672:Biocompatible Materials / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D002516:Ceramics / Q000737:chemistry; D019245:Compressive Strength; D021621:Imaging, Three-Dimensional; D019344:Lactic Acid / Q000737:chemistry*; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D016062:Porosity; D011327:Printing / Q000379:methods*; D013314:Stress, Mechanical; D013499:Surface Properties; D023822:Tissue Engineering / Q000295:instrumentation / Q000379:methods*; D054457:Tissue Scaffolds / Q000737:chemistry*
D001672:Biocompatible Materials; D002130:Calcium Phosphates; D011091:Polyesters; D011108:Polymers; C485817:beta-tricalcium phosphate; D019344:Lactic Acid; C033616:poly(lactide)