Observation of magnetoelectric coupling and local piezoresponse in modified (Na0.5Bi0.5)TiO3-BaTiO3-CoFe2O4 lead-free composites.
Lead-free particulate multiferroic composites of [0.94(Na0.5Bi0.5)TiO3-0.06 BaTiO3]:(Co0.6Zn0.4)(Fe1.7Mn0.3)O4 were synthesized and magnetoelectric (ME) properties were studied. X-ray diffraction and microstructural studies indicated the formation of a two-phase composite system without any impurities. The shift of Raman modes corresponding to ferroelectric and ferrite phases was assigned to the induced strain amid the formation of a two-phase system, in relation to the fraction of each phase in the samples. A strong local piezoresponse and hysteresis loops observed for composites established the ferroelectric properties at a nanoscale. Magnetostriction measurements revealed values of λ11 = -10.4 and λ12 = 5.3 ppm and piezomagnetic coefficient dλ11/dH = -0.0087 ppm Oe(-1) at 0.45 kOe for a composite with a ferrite concentration of 35 mol%. A maximum change of 18.5% in magnetization after electrical poling indicates a strong magnetoelectric response of the present composites followed by a direct ME coefficient of 8.2 mV cm(-1) Oe(-1). Our studies point to the fact that the present multiferroic composites having strong ME coupling are useful for lead-free electronic applications.
I3N-Aveiro, Department of Physics, University of Aveiro, Aveiro-3810 193, Portugal. venkataramanaesk@rediffmail.com.
E Venkata
EV
Ramana
F
F
Figueiras
M P F
MP
Graça
M A
MA
Valente