title: Determination of sulfuric acid concentration for anti-cavitation characteristics of Al alloy by two step anodizing process to forming nano porous.
abstract: Al alloy is a highly active metal but forms a protective oxide film having high corrosion resistance in atmosphere environment. However, the oxide film is not suitable for practical use, since the thickness of the film is not uniform and it is severly altered with formation conditions. This study focused on developing an aluminum anodizing layer having hardness, corrosion resistance and abrasion resistance equivalent to a commercial grade protective layer. Aluminum anodizing layer was produced by two-step aluminum anodizing oxide (AAO) process with different sulfuric acid concentrations, and the cavitation characteristics of the anodized coating layer was investigated. In hardness measurement, the anodized coating layer produced with 15 vol.% of sulfuric acid condition had the highest value of hardness but exhibited poor cavitation resistance due to being more brittle than those with other conditions. The 10 vol.% of sulfuric acid condition was thus considered to be the optimum condition as it had the lowest weight loss and damage depth.
authors.forename: Seung-Jun
authors.initials: SJ
authors.lastname: Lee
authors.forename: Seong-Kweon
authors.initials: SK
authors.lastname: Kim
authors.forename: Jae-Yong
authors.initials: JY
authors.lastname: Jeong
authors.forename: Seong-Jong
authors.initials: SJ
authors.lastname: Kim
mesh_terms: D000497:Alloys; D000535:Aluminum / Q000737:chemistry*; D058608:Nanopores; D013464:Sulfuric Acids / Q000032:analysis*; D013499:Surface Properties
chemical_list: D000497:Alloys; D013464:Sulfuric Acids; D000535:Aluminum; C033158:sulfuric acid