title: Accessing photo-based morphological control in phase-separated, cross-linked networks through delayed gelation.
abstract: This work presents an approach to extend the period for phase separation, independent of temperature, in ambient phase-separating photopolymerizations based on the copolymerization of structurally similar mono- and di-vinyl monomers. Copolymer resins composed of triethylene glycol dimethacrylate (TEGDMA) and ethylene glycol methyl ether methacrylate (EGMEMA) were modified with a thermoplastic prepolymer, poly(butyl methacrylate). With increasing EGMEMA modification into the bulk TEGDMA resin, there is a decrease in the initial reaction rate, which increases the time for development of compositionally different phases prior to network gelation. The period between phase separation and gelation was probed through optical and rheological measurements, and it was extended from 22 s in a TEGDMA resin to 69 s in a TEGDMA:EGMEMA copolymer, allowing these materials to be processed under a wide range of UV-irradiation intensities (300 µW cm-2- 100 mW cm-2), which provided an additional degree of control over the resulting phase separated domain size and morphology.
authors.affiliation: Department of Chemical and Biological Engineering, University of Colorado, Boulder, CO, 80309, USA.
authors.forename: Caroline R
authors.initials: CR
authors.lastname: Szczepanski
authors.affiliation: Department of Craniofacial Biology, School of Dental Medicine, University of Colorado, Aurora, CO 80045, USA.
authors.forename: Jeffrey W
authors.initials: JW
authors.lastname: Stansbury
keywords: heterogeneous polymers; phase separation; photopolymerization