title: Composition-ratio influence on resistive switching behavior of solution-processed InGaZnO-based thin-film.
abstract: The influence of composition ratio on the bipolar resistive switching behavior of resistive switching memory devices based on amorphous indium-gallium-zinc-oxide (a-IGZO) using the spin-coating process was investigated. To study the stoichiometric effects of the a-IGZO films on device characteristics, four devices with In/Ga/Zn stoichiometries of 1:1:1, 3:1:1, 1:3:1, and 1:1:3 were fabricated and characterized. The 3:1:1 film showed an ohmic behavior and the 1:1:3 film showed a rectifying switching behavior. The current-voltage characteristics of the a-IGZO films with stoichiometries of 1:1:1 and 1:3:1, however, showed a bipolar resistive memory switching behavior. We found that the three-fold increase in the gallium content ratio reduces the reset voltage from -0.9 to - 0.4 V and enhances the current ratio of high to low resistive states from 0.7 x 10(1) to 3 x 10(1). Our results show that the increase in the Ga composition ratio in the a-IGZO-based ReRAM cells effectively improves the device performance and reliability by increasing the initial defect density in the a-IGZO films.
authors.forename: Yeong-Hyeon
authors.initials: YH
authors.lastname: Hwang
authors.forename: Inchan
authors.initials: I
authors.lastname: Hwang
authors.forename: Won-Ju
authors.initials: WJ
authors.lastname: Cho