Fractal and multifractal characteristics of swift heavy ion induced self-affine nanostructured BaF2 thin film surfaces.
Fractal and multifractal characteristics of self-affine surfaces of BaF2 thin films, deposited on crystalline Si ⟨1 1 1⟩ substrate at room temperature, were studied. Self-affine surfaces were prepared by irradiation of 120 MeV Ag(9+) ions which modified the surface morphology at nanometer scale. The surface morphology of virgin thin film and those irradiated with different ion fluences are characterized by atomic force microscopy technique. The surface roughness (interface width) shows monotonic decrease with ion fluences, while the other parameters, such as lateral correlation length, roughness exponent, and fractal dimension, did not show either monotonic decrease or increase in nature. The self-affine nature of the films is further confirmed by autocorrelation function. The power spectral density of thin films surfaces exhibits inverse power law variation with spatial frequency, suggesting the existence of fractal component in surface morphology. The multifractal detrended fluctuation analysis based on the partition function approach is also performed on virgin and irradiated thin films. It is found that the partition function exhibits the power law behavior with the segment size. Moreover, it is also seen that the scaling exponents vary nonlinearly with the moment, thereby exhibiting the multifractal nature.
Department of Physics, University of Allahabad, Allahabad 211002, India.
R P
RP
Yadav
Nanotechnology Application Centre, University of Allahabad, Allahabad 211002, India.
Manvendra
M
Kumar
Department of Physics, University of Allahabad, Allahabad 211002, India.
A K
AK
Mittal
Nanotechnology Application Centre, University of Allahabad, Allahabad 211002, India.
A C
AC
Pandey