Novel biodegradable calcium phosphate/polymer composite coating with adjustable mechanical properties formed by hydrothermal process for corrosion protection of magnesium substrate.
Ceramic type coatings on metallic implants, such as calcium phosphate (Ca-P), are generally stiff and brittle, potentially leading to the early failure of the bone-implant interface. To reduce material brittleness, polyacrylic acid and carboxymethyl cellulose were used in this study to deposit two types of novel Ca-P/polymer composite coatings on AZ31 magnesium alloy using a one-step hydrothermal process. X-ray diffraction and scanning electron microscopy showed that the deposited Ca-P crystal phase and morphology could be controlled by the type and concentration of polymer used. Incorporation of polymer in the Ca-P coatings reduced the coating elastic modulus bringing it close to that of magnesium and that of human bone. Nanoindentation test results revealed significantly decreased cracking tendency with the incorporation of polymer in the Ca-P coating. Apart from mechanical improvements, the protective composite layers had also enhanced the corrosion resistance of the substrate by a factor of 1000 which is sufficient for implant application. Cell proliferation studies indicated that the composite coatings induced better cell attachment compared with the purely inorganic Ca-P coating, confirming that the obtained composite materials could be promising candidates for surface protection of magnesium for implant application with the multiple functions of corrosion protection, interfacial stress reduction, and cell attachment/cell growth promotion. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1643-1657, 2016.
School of Mechanical & Aerospace Engineering, Nanyang Technological University, 639708, Singapore. sara002@e.ntu.edu.sg.|Singapore Institute Of Manufacturing Technology, 638075, Singapore. sara002@e.ntu.edu.sg.
Sara
S
Kaabi Falahieh Asl
Singapore Institute Of Manufacturing Technology, 638075, Singapore.
Sandor
S
Nemeth
School of Mechanical & Aerospace Engineering, Nanyang Technological University, 639708, Singapore.
Ming Jen
MJ
Tan
D000497:Alloys / Q000737:chemistry / Q000494:pharmacology; D063566:Biodegradable Plastics / Q000737:chemistry / Q000494:pharmacology; D002130:Calcium Phosphates / Q000737:chemistry / Q000494:pharmacology; D045744:Cell Line, Tumor; D020099:Coated Materials, Biocompatible / Q000737:chemistry / Q000494:pharmacology; D003343:Corrosion; D006801:Humans; D008274:Magnesium / Q000737:chemistry / Q000494:pharmacology; D008422:Materials Testing
D000497:Alloys; D063566:Biodegradable Plastics; D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; C586533:Mg-Al-Zn-Mn-Si-Cu alloy; C020243:calcium phosphate; D008274:Magnesium
calcium phosphate coating; composite coating; corrosion performance; magnesium implant