Assembling strategy to synthesize palladium modified kaolin nanocomposites with different morphologies.
Nanocomposites of aluminosilicate minerals, kaolins (kaolinite and halloysite) with natural different morphologies assembling with palladium (Pd) nanoparticles have been successfully synthesized through strong electrostatic adsorption and chemical bonding after surface modification with 3-aminopropyl triethoxysilane (APTES). Meanwhile, the influence of different morphologies supports on catalytic hydrogenation properties was explored. The surface concentration of amino groups on the kaolins was related to the morphology and surface nature. Electronmicroscopy revealed that the monodisperse Pd nanoparticles were uniformly deposited onto the surface of kaolins, ranging in diameter from 0.5 nm to 5.5 nm. The functional groups could not only improve the dispersion of kaolins with different morphologies in solution, but also enhance the interaction between Pd precursors and kaolins, thus preventing small Pd nanoparticles from agglomerating and leading to high activity for the catalytic hydrogenation of styrene. Pd-FK@APTES was more active compared to other samples. Selecting the kaolin morphology with a different surface nature allows the selective surface modification of a larger fraction of the reactive facets on which the active sites can be enriched and tuned. This desirable surface coordination of catalytically active atoms could substantially improve catalytic activity.
Centre for Mineral Materials, School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, China.
Xiaoyu
X
Li
Centre for Mineral Materials, School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, China.
Jing
J
Ouyang
School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China.
Yonghua
Y
Zhou
Centre for Mineral Materials, School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, China.
Huaming
H
Yang