NO2 Gas Sensing Properties of Multiple Networked ZnGa2O4 Nanorods Coated with TiO2.
The NO2 gas sensing properties of ZnGa2O4-TiO2 heterostructure nanorods was examined. ZnGa2O4-core/TiO2-shell nanorods were fabricated by the thermal evaporation of a mixture of Zn and GaN powders and the sputter deposition of TiO2. Multiple networked ZnGa2O4-core/TiO2-shell nanorod sensors showed the response of 876% at 10 ppm NO2 at 300 degrees C. This response value at 10 ppm NO2 is approximately 4 times larger than that of bare ZnGa2O4 nanorod sensors. The response values obtained by the ZnGa2O4-core/TiO2-shell nanorods in this study are more than 13 times higher than those obtained previously by the SnO2-core/ZnO-shell nanofibers at 5% NO2. The significant enhancement in the response of ZnGa2O4 nanorods to NO2 gas by coating them with TiO2 can be explained based on the space-charge model.