Bioactivity studies on TiO₂-bearing Na₂O-CaO-SiO₂-B₂O₃ glasses.
Soda lime silica borate glasses mixed with different concentrations of TiO2 are synthesized by the melt-quenching technique. As a part of study on bioactivity of these glasses, the samples were immersed in simulated body fluid (SBF) solution for prolonged times (~21 days) during which weight loss along with pH measurements is carried out at specific intervals of time. The XRD and SEM analyses of post-immersed samples confirm the formation of crystalline hydroxyapatite layer (HA) on the surface of the samples. To assess the role of TiO2 on the formation of HA layer and degradability of the samples the spectroscopic studies viz. optical absorption and IR spectral studies on post- and pre-immersed samples have been carried out. The analysis of the results of degradability together with spectroscopic studies as a function of TiO2 concentration indicated that about 6.0 mol% of TiO2 is the optimal concentration for achieving better bioactivity of these glasses. The presence of the maximal concentration octahedral titanium ions in this glass that facilitates the formation of HA layer is found to be the reason for such a higher bioactivity.
Department of Physics, Andhra Loyola College, Vijayawada 520 008, Andhra Pradesh, India; Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P., India.
G
G
Jagan Mohini
Department of Physics, Andhra Loyola College, Vijayawada 520 008, Andhra Pradesh, India.
G
G
Sahaya Baskaran
Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P., India.
V
V
Ravi Kumar
Institute of Physics, J. Dlugosz University, Al. Armii Krajowej 13/15, Czestochowa, Poland.
M
M
Piasecki
Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P., India. Electronic address: nvr8@rediffmail.com.
N
N
Veeraiah
D001826:Body Fluids / Q000737:chemistry*; D018786:Bone Substitutes / Q000737:chemistry*; D001896:Boron Compounds / Q000737:chemistry*; D017886:Durapatite / Q000138:chemical synthesis*; D005898:Glass / Q000737:chemistry*; D008422:Materials Testing; D014025:Titanium / Q000737:chemistry*
D018786:Bone Substitutes; D001896:Boron Compounds; C009495:titanium dioxide; D017886:Durapatite; D014025:Titanium
Bioactivity; HAP layer; Soda lime silicate glasses