Bond strength of repaired amalgam restorations.
This in vitro study investigated the interfacial flexural strength (FS) of amalgam repairs and the optimal combination of repair materials and mechanical retention required for a consistent and durable repair bond. Amalgam bricks were created, each with 1 end roughened to expose a fresh surface before repair. Four groups followed separate repair protocols: group 1, bonding agent with amalgam; group 2, bonding agent with composite resin; group 3, mechanical retention (slot) with amalgam; and group 4, slot with bonding agent and amalgam. Repaired specimens were stored in artificial saliva for 1, 10, 30, 120, or 360 days before being loaded to failure in a 3-point bending test. Statistical analysis showed significant changes in median FS over time in groups 2 and 4. The effect of the repair method on the FS values after each storage period was significant for most groups except the 30-day storage groups. Amalgam-amalgam repair with adequate condensation yielded the most consistent and durable bond. An amalgam bonding agent could be beneficial when firm condensation on the repair surface cannot be achieved or when tooth structure is involved. Composite resin can be a viable option for amalgam repair in an esthetically demanding region, but proper mechanical modification of the amalgam surface and selection of the proper bonding system are essential.
Rosalia
R
Rey
Eduardo
E
Mondragon
Chiayi
C
Shen
D003188:Composite Resins / Q000627:therapeutic use; D003723:Dental Amalgam / Q000592:standards / Q000627:therapeutic use*; D001840:Dental Bonding / Q000379:methods / Q000592:standards*; D058250:Dental Restoration Repair / Q000379:methods* / Q000592:standards; D006801:Humans; D066298:In Vitro Techniques
D003188:Composite Resins; D003723:Dental Amalgam
amalgam repair; bonding agent; interfacial strength