title: Development of dental composites with reactive fillers that promote precipitation of antibacterial-hydroxyapatite layers.
abstract: The study aim was to develop light-curable, high strength dental composites that would release calcium phosphate and chlorhexidine (CHX) but additionally promote surface hydroxyapatite/CHX co-precipitation in simulated body fluid (SBF). 80 wt.% urethane dimethacrylate based liquid was mixed with glass fillers containing 10 wt.% CHX and 0, 10, 20 or 40 wt.% reactive mono- and tricalcium phosphate (CaP). Surface hydroxyapatite layer thickness/coverage from SEM images, Ca/Si ratio from EDX and hydroxyapatite Raman peak intensities were all proportional to both time in SBF and CaP wt.% in the filler. Hydroxyapatite was, however, difficult to detect by XRD until 4 weeks. XRD peak width and SEM images suggested this was due to the very small size (~10 nm) of the hydroxyapatite crystallites. Precipitate mass at 12 weeks was 22 wt.% of the sample CaP total mass irrespective of CaP wt.% and up to 7 wt.% of the specimen. Early diffusion controlled CHX release, assessed by UV spectrometry, was proportional to CaP and twice as fast in water compared with SBF. After 1 week, CHX continued to diffuse into water but in SBF, became entrapped within the precipitating hydroxyapatite layer. At 12 weeks CHX formed 5 to 15% of the HA layer with 10 to 40 wt.% CaP respectively. Despite linear decline of strength and modulus in 4 weeks from 160 to 101 MPa and 4 to 2.4 GPa, respectively, upon raising CaP content, all values were still within the range expected for commercial composites. The high strength, hydroxyapatite precipitation and surface antibacterial accumulation should reduce tooth restoration failure due to fracture, aid demineralised dentine repair and prevent subsurface carious disease respectively.
authors.affiliation: UCL Eastman Dental Institute, Biomaterials & Tissue Engineering Division, 256 Gray's Inn Road, London WC1X 8LD, United Kingdom.
authors.forename: Anas
authors.initials: A
authors.lastname: Aljabo
authors.affiliation: UCL Eastman Dental Institute, Biomaterials & Tissue Engineering Division, 256 Gray's Inn Road, London WC1X 8LD, United Kingdom; Division of Biomaterials, Operative Dentistry Department, Faculty of Dentistry, King Abdulaziz University, Jeddah, Saudi Arabia; Biomaterials Department, Faculty of Dentistry, Tanta University, Tanta, Egypt.
authors.forename: Ensanya A
authors.initials: EA
authors.lastname: Abou Neel
authors.affiliation: UCL Eastman Dental Institute, Biomaterials & Tissue Engineering Division, 256 Gray's Inn Road, London WC1X 8LD, United Kingdom.
authors.forename: Jonathan C
authors.initials: JC
authors.lastname: Knowles
authors.affiliation: UCL Eastman Dental Institute, Biomaterials & Tissue Engineering Division, 256 Gray's Inn Road, London WC1X 8LD, United Kingdom.
authors.forename: Anne M
authors.initials: AM
authors.lastname: Young
mesh_terms: D000900:Anti-Bacterial Agents / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry*; D013499:Surface Properties
chemical_list: D000900:Anti-Bacterial Agents; D002130:Calcium Phosphates; D003188:Composite Resins; D017886:Durapatite; C020243:calcium phosphate
keywords: Antibacterial; Dental composite; Hydroxyapatite precipitation; Mono- and tricalcium phosphate