title: Effect of CNT as a Nucleating Agent on Cell Morphology and Thermal Insulation Property of the Rigid Polyurethane Foams.
abstract: The effects of MWCNT on the cell sizes, cell uniformities, thermal conductivities, bulk densities, foaming kinetics, and compressive mechanical properties of the rigid PUFs were investigated. To obtain the better uniform dispersed state of MWCNT, grease-type master batch of MWCNT/surfactant was prepared by three-roll mill. Average cell size of the PUF samples decreased from 185.1 for the neat PUF to 162.9 μm for the sample of 0.01 phr of MWCNT concentration. Cell uniformity was also enhanced showing the standard cell-size deviation of 61.7 and 35.2, respectively. While the thermal conductivity of the neat PUF was 0.0222 W/m(o)K, that of the sample with 0.01 phr of MWCNT showed 0.0204 W/m(o)K, resulting 8.2% reduction of the thermal conductivity. Bulk density of the PUF samples was observed as nearly the same values as 30.0 ± 1.0 g/cm3 regardless of MWCNT. Temperature profiles during foaming process showed that an indirect indication of the nucleation effect of MWCNT for the PUF foaming system, showing faster and higher temperature rising with time. The compressive yield stress is nearly the same as 0.030 x 10(5) Pa regardless of MWCNT.
authors.forename: WonSool
authors.initials: W
authors.lastname: Ahn
authors.forename: Joon-Man
authors.initials: JM
authors.lastname: Lee
mesh_terms: D003460:Crystallization / Q000379:methods*; D055119:Elastic Modulus; D005740:Gases / Q000737:chemistry*; D006244:Hardness; D006358:Hot Temperature; D008422:Materials Testing; D037742:Nanotubes, Carbon / Q000737:chemistry* / Q000648:ultrastructure; D011140:Polyurethanes / Q000737:chemistry*; D013814:Thermal Conductivity
chemical_list: D005740:Gases; D037742:Nanotubes, Carbon; D011140:Polyurethanes