Thermal activation of serpentine for adsorption of cadmium.
Thermal activated serpentine with high adsorption capacity for heavy metals was prepared. The batch experiment studies were conducted to evaluate the adsorption performance of Cd2+in aqueous solution using thermal activated serpentine as adsorbent. These samples before and after adsorption were characterized by XRD, FT-IR, SEM, XPS, and N2adsorption-desorption at low temperature. It was found that serpentine with layered structure transformed to forsterite with amorphous structure after thermal treatment at over 700°C, while the surface area of the samples was increased with activated temperature and the serpentine activated at 700°C (S-700) presented the largest surface area. The pH of solution after adsorption was increased in different degrees due to hydrolysis of MgO in serpentine, resulting in enhancing adsorption of Cd2+. The S-700 exhibited the maximum equilibrium adsorption capacity (15.21mg/g), which was 2 times more than pristine serpentine. Langmuir isotherm was proved to describe the equilibrium adsorption data better than Freundlich isotherm and pseudo second order kinetics model could fit the adsorption kinetics processes well. Based on the results of characterization with XPS and XRD, the adsorption mechanisms could be explained as primarily formation of CdCO3and Cd(OH)2precipitation on the surface of serpentine.
College of Land and Environment, Shenyang Agricultural University, Shenyang, China; College of Chemistry, Chemical Engineering and Food Safety, Bohai University, Jinzhou, China.
Chun-Yan
CY
Cao
College of Land and Environment, Shenyang Agricultural University, Shenyang, China. Electronic address: liang110161@163.com.
Cheng-Hua
CH
Liang
Institute of Applied Ecology, Chinese Academy of Sciences, Shenyang, China.
Yan
Y
Yin
College of Land and Environment, Shenyang Agricultural University, Shenyang, China.
Li-Yu
LY
Du
Adsorption; Cadmium; Serpentine; Thermal activation